General
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Density | 1.51 g/cm³ Show Supplier Material materials with Density of 1.51 g/cm³ | dry | ISO 1183 | |
Moisture absorption | 1.4 % Show Supplier Material materials with Moisture absorption of 1.4 % | dry | Sim. to ISO 62 | |
Water absorption | 0.28 % Show Supplier Material materials with Water absorption of 0.28 % | dry | ISO 62 | at 23°C after 24h |
3.5 % Show Supplier Material materials with Water absorption of 3.5 % | dry | Sim. to ISO 62 |
Mechanical
Property | Temperature | Value | Condition | Testing Standard | Thickness | Comment |
---|---|---|---|---|---|---|
Elastic modulus | 10 GPa Show Supplier Material materials with Elastic modulus of 10 GPa | dry, conditioned | ISO 527-1/-2 | |||
10 GPa Show Supplier Material materials with Elastic modulus of 10 GPa | dry, conditioned | ISO 527-1/-2 | 1 mm | |||
120 °C | 5.6 GPa Show Supplier Material materials with Elastic modulus of 5.6 GPa | dry | ISO 527-1/-2 | |||
160 °C | 3 GPa Show Supplier Material materials with Elastic modulus of 3 GPa | dry | ISO 527-1/-2 | |||
Elongation | 2.1 % Show Supplier Material materials with Elongation of 2.1 % | dry, conditioned | ISO 527-1/-2 | |||
2.1 % Show Supplier Material materials with Elongation of 2.1 % | conditioned | ISO 527-1/-2 | ||||
2.2 % Show Supplier Material materials with Elongation of 2.2 % | dry | ISO 527-1/-2 | 1 mm | |||
120 °C | 4 % Show Supplier Material materials with Elongation of 4 % | dry | ISO 527-1/-2 | |||
160 °C | 6 % Show Supplier Material materials with Elongation of 6 % | dry | ISO 527-1/-2 | |||
Flexural modulus | 9.4 GPa Show Supplier Material materials with Flexural modulus of 9.4 GPa | dry | ISO 178 | |||
9.6 GPa Show Supplier Material materials with Flexural modulus of 9.6 GPa | conditioned | ISO 178 | ||||
120 °C | 5.4 GPa Show Supplier Material materials with Flexural modulus of 5.4 GPa | dry | ISO 178 | |||
160 °C | 3.1 GPa Show Supplier Material materials with Flexural modulus of 3.1 GPa | dry | ISO 178 | |||
Flexural yield strength | 165 MPa Show Supplier Material materials with Flexural yield strength of 165 MPa | conditioned | ISO 178 | |||
185 MPa Show Supplier Material materials with Flexural yield strength of 185 MPa | dry | ISO 178 | ||||
120 °C | 100 MPa Show Supplier Material materials with Flexural yield strength of 100 MPa | dry | ISO 178 | |||
160 °C | 70 MPa Show Supplier Material materials with Flexural yield strength of 70 MPa | dry | ISO 178 | |||
Impact strength, Charpy notched | 23 °C | 3.6 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 3.6 kJ/m² | conditioned | ISO 179/1eA | ||
23 °C | 4 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 4 kJ/m² | dry | ISO 179/1eA | |||
Impact strength, Charpy unnotched | 23 °C | 35 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 35 kJ/m² | dry, conditioned | ISO 179/1eU | ||
Tensile strength | 105 MPa Show Supplier Material materials with Tensile strength of 105 MPa | conditioned | ISO 527-1/-2 | |||
110 MPa Show Supplier Material materials with Tensile strength of 110 MPa | conditioned | ISO 527-1/-2 | at low thickness | |||
125 MPa Show Supplier Material materials with Tensile strength of 125 MPa | dry | ISO 527-1/-2 | ||||
130 MPa Show Supplier Material materials with Tensile strength of 130 MPa | dry | ISO 527-1/-2 | 1 mm | at low thickness | ||
120 °C | 64 MPa Show Supplier Material materials with Tensile strength of 64 MPa | dry | ISO 527-1/-2 | |||
160 °C | 45 MPa Show Supplier Material materials with Tensile strength of 45 MPa | dry | ISO 527-1/-2 |
Thermal
Property | Value | Condition | Testing Standard | Pressure | Comment |
---|---|---|---|---|---|
Coefficient of thermal expansion | 1.8e-07 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.8e-07 1/K | dry | ISO 11359-1/-2 | Parallel | |
6e-07 1/K Show Supplier Material materials with Coefficient of thermal expansion of 6e-07 1/K | dry | ISO 11359-1/-2 | Normal | ||
Glass transition temperature | 125 °C Show Supplier Material materials with Glass transition temperature of 125 °C | dry | ISO 11357-1/-2 | 10°C/min | |
Heat deflection temperature | 285 °C Show Supplier Material materials with Heat deflection temperature of 285 °C | dry | ISO 75-1/-2 | 2 MPa | |
315 °C Show Supplier Material materials with Heat deflection temperature of 315 °C | dry | ISO 75-1/-2 | 0.45 MPa | ||
Melting point | 325 °C Show Supplier Material materials with Melting point of 325 °C | dry | ISO 11357-1/-3 | 10°C/min |
Electrical
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Dielectric constant | 3.73 [-] Show Supplier Material materials with Dielectric constant of 3.73 [-] | dry | IEC 60250 | 5GHz |
3.78 [-] Show Supplier Material materials with Dielectric constant of 3.78 [-] | dry | IEC 60250 | 1GHz | |
3.8 [-] Show Supplier Material materials with Dielectric constant of 3.8 [-] | conditioned | IEC 60250 | 5GHz | |
3.85 [-] Show Supplier Material materials with Dielectric constant of 3.85 [-] | conditioned | IEC 60250 | 1GHz | |
Dissipation factor | 140 [-] Show Supplier Material materials with Dissipation factor of 140 [-] | dry | IEC 60250 | 5GHz |
160 [-] Show Supplier Material materials with Dissipation factor of 160 [-] | dry | IEC 60250 | 1GHz | |
170 [-] Show Supplier Material materials with Dissipation factor of 170 [-] | conditioned | IEC 60250 | 5GHz | |
190 [-] Show Supplier Material materials with Dissipation factor of 190 [-] | conditioned | IEC 60250 | 1GHz |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | T10 LDS sockets | |
Certifications | Yellow Card Available | |
Fillers | 30% Glass Fiber |