General
Property | Value | Condition | Testing Standard |
---|---|---|---|
Density | 0.65 g/cm³ Show Supplier Material materials with Density of 0.65 g/cm³ | dry | ISO 60 |
1.08 g/cm³ Show Supplier Material materials with Density of 1.08 g/cm³ | dry | ISO 1183 | |
Water absorption | 0.8 % Show Supplier Material materials with Water absorption of 0.8 % | dry | Sim. to ISO 62 |
Mechanical
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Elastic modulus | 0.03 GPa Show Supplier Material materials with Elastic modulus of 0.03 GPa | dry | ISO 527-1/-2 | |
Elongation | 300 % Show Supplier Material materials with Elongation of 300 % | dry | ISO 527-1/-2 | |
900 % Show Supplier Material materials with Elongation of 900 % | dry | ISO 527-1/-2 | ||
Flexural modulus | 0.02 GPa Show Supplier Material materials with Flexural modulus of 0.02 GPa | dry | ISO 178 | |
Hardness, Shore A | 85 [-] Show Supplier Material materials with Hardness, Shore A of 85 [-] | dry | ISO 868 | 3s |
Hardness, Shore D | 25 [-] Show Supplier Material materials with Hardness, Shore D of 25 [-] | dry | ISO 868 | 3s |
Tensile strength | 15 MPa Show Supplier Material materials with Tensile strength of 15 MPa | dry | ISO 527-1/-2 |
Thermal
Property | Value | Condition | Testing Standard | Thickness | Comment |
---|---|---|---|---|---|
Coefficient of thermal expansion | 2.2e-06 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2.2e-06 1/K | dry | ISO 11359-1/-2 | Parallel | |
2.2e-06 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2.2e-06 1/K | dry | ISO 11359-1/-2 | Normal | ||
Flammability | HB | dry | IEC 60695-11-10 | 1.5 mm | UL recognition :Yes |
Glass transition temperature | -80 °C Show Supplier Material materials with Glass transition temperature of -80 °C | dry | ISO 11357-1/-2 | 10°C/min | |
-74 °C Show Supplier Material materials with Glass transition temperature of -74 °C | dry | ASTM D5026/D7028 | DMTA (tan d) | ||
Melting point | 180 °C Show Supplier Material materials with Melting point of 180 °C | dry | ISO 11357-1/-3 | 10°C/min | |
Relative temperature index, electrical | 50 °C Show Supplier Material materials with Relative temperature index, electrical of 50 °C | dry | UL746B | 2 mm | |
Relative temperature index, mechanical impact | 50 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 50 °C | dry | UL746B | 2 mm | |
Relative temperature index, mechanical strength | 50 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 50 °C | dry | UL746B | 2 mm |
Electrical
Property | Value | Condition | Testing Standard |
---|---|---|---|
Volume resistivity | 5e+12 Ω·cm Show Supplier Material materials with Volume resistivity of 5e+12 Ω·cm | dry | IEC 62631-3-1 |
Rheological Properties
Property | Temperature | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|---|
Density of melt | 905 g/cm³ Show Supplier Material materials with Density of melt of 905 g/cm³ | dry | - | ||
Melt volume-flow rate | 230 °C | 48 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 48 cm³/10min | dry | ISO 1133 | |
Shrinkage | 1 % Show Supplier Material materials with Shrinkage of 1 % | dry | Sim. to ISO 294-4 | Parallel | |
1 % Show Supplier Material materials with Shrinkage of 1 % | dry | Sim. to ISO 294-4 | Normal |
Technological properties
Property | ||
---|---|---|
Application areas | Medical gowns, Wound dressings, Medical Tubes, Respiratory Tubes |