Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Density | 1.41 g/cm³ Show Supplier Material materials with Density of 1.41 g/cm³ | dry | ISO 1183 | |
Limiting oxygen index | 22 % Show Supplier Material materials with Limiting oxygen index of 22 % | dry | ISO 4589-1/-2 | |
Moisture absorption | 2.6 % Show Supplier Material materials with Moisture absorption of 2.6 % | dry | Sim. to ISO 62 | |
Water absorption | 2.65 % Show Supplier Material materials with Water absorption of 2.65 % | dry | ISO 62 | at 23°C after 24h |
9.5 % Show Supplier Material materials with Water absorption of 9.5 % | dry | Sim. to ISO 62 |
Mechanical
Property | Temperature | Value | Condition | Testing Standard | Thickness | Comment |
---|---|---|---|---|---|---|
Elastic modulus | 6 GPa Show Supplier Material materials with Elastic modulus of 6 GPa | conditioned | ISO 527-1/-2 | |||
6 GPa Show Supplier Material materials with Elastic modulus of 6 GPa | conditioned | ISO 527-1/-2 | ||||
10 GPa Show Supplier Material materials with Elastic modulus of 10 GPa | dry | ISO 527-1/-2 | ||||
10 GPa Show Supplier Material materials with Elastic modulus of 10 GPa | dry | ISO 527-1/-2 | 1 mm | |||
120 °C | 5.3 GPa Show Supplier Material materials with Elastic modulus of 5.3 GPa | dry | ISO 527-1/-2 | |||
160 °C | 4.8 GPa Show Supplier Material materials with Elastic modulus of 4.8 GPa | dry | ISO 527-1/-2 | |||
180 °C | 4.5 GPa Show Supplier Material materials with Elastic modulus of 4.5 GPa | dry | ISO 527-1/-2 | |||
200 °C | 4.3 GPa Show Supplier Material materials with Elastic modulus of 4.3 GPa | dry | ISO 527-1/-2 | |||
Elongation | 2.5 % Show Supplier Material materials with Elongation of 2.5 % | dry | ISO 527-1/-2 | |||
2.6 % Show Supplier Material materials with Elongation of 2.6 % | dry | ISO 527-1/-2 | 1 mm | |||
5 % Show Supplier Material materials with Elongation of 5 % | conditioned | ISO 527-1/-2 | ||||
5 % Show Supplier Material materials with Elongation of 5 % | conditioned | ISO 527-1/-2 | ||||
120 °C | 5.5 % Show Supplier Material materials with Elongation of 5.5 % | dry | ISO 527-1/-2 | |||
160 °C | 5.5 % Show Supplier Material materials with Elongation of 5.5 % | dry | ISO 527-1/-2 | |||
180 °C | 5.5 % Show Supplier Material materials with Elongation of 5.5 % | dry | ISO 527-1/-2 | |||
200 °C | 5.5 % Show Supplier Material materials with Elongation of 5.5 % | dry | ISO 527-1/-2 | |||
Flexural modulus | 5.5 GPa Show Supplier Material materials with Flexural modulus of 5.5 GPa | conditioned | ISO 178 | |||
9.5 GPa Show Supplier Material materials with Flexural modulus of 9.5 GPa | dry | ISO 178 | ||||
120 °C | 5.1 GPa Show Supplier Material materials with Flexural modulus of 5.1 GPa | dry | ISO 178 | |||
160 °C | 4.9 GPa Show Supplier Material materials with Flexural modulus of 4.9 GPa | dry | ISO 178 | |||
Flexural yield strength | 160 MPa Show Supplier Material materials with Flexural yield strength of 160 MPa | conditioned | ISO 178 | |||
270 MPa Show Supplier Material materials with Flexural yield strength of 270 MPa | dry | ISO 178 | ||||
120 °C | 140 MPa Show Supplier Material materials with Flexural yield strength of 140 MPa | dry | ISO 178 | |||
160 °C | 125 MPa Show Supplier Material materials with Flexural yield strength of 125 MPa | dry | ISO 178 | |||
Impact strength, Charpy notched | -30 °C | 10 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 10 kJ/m² | dry, conditioned | ISO 179/1eA | ||
23 °C | 10 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 10 kJ/m² | dry | ISO 179/1eA | |||
23 °C | 15 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 15 kJ/m² | conditioned | ISO 179/1eA | |||
Impact strength, Charpy unnotched | -30 °C | 60 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 60 kJ/m² | dry, conditioned | ISO 179/1eU | ||
23 °C | 60 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 60 kJ/m² | dry | ISO 179/1eU | |||
23 °C | 90 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 90 kJ/m² | conditioned | ISO 179/1eU | |||
Tensile strength | 110 MPa Show Supplier Material materials with Tensile strength of 110 MPa | conditioned | ISO 527-1/-2 | |||
115 MPa Show Supplier Material materials with Tensile strength of 115 MPa | conditioned | ISO 527-1/-2 | at low thickness | |||
180 MPa Show Supplier Material materials with Tensile strength of 180 MPa | dry | ISO 527-1/-2 | ||||
180 MPa Show Supplier Material materials with Tensile strength of 180 MPa | dry | ISO 527-1/-2 | 1 mm | at low thickness | ||
120 °C | 105 MPa Show Supplier Material materials with Tensile strength of 105 MPa | dry | ISO 527-1/-2 | |||
160 °C | 90 MPa Show Supplier Material materials with Tensile strength of 90 MPa | dry | ISO 527-1/-2 | |||
180 °C | 85 MPa Show Supplier Material materials with Tensile strength of 85 MPa | dry | ISO 527-1/-2 | |||
200 °C | 80 MPa Show Supplier Material materials with Tensile strength of 80 MPa | dry | ISO 527-1/-2 |
Thermal
Property | Value | Condition | Testing Standard | Thickness | Pressure | Comment |
---|---|---|---|---|---|---|
Coefficient of thermal expansion | 2.5e-07 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2.5e-07 1/K | dry | ISO 11359-1/-2 | Parallel | ||
6e-07 1/K Show Supplier Material materials with Coefficient of thermal expansion of 6e-07 1/K | dry | ISO 11359-1/-2 | Normal | |||
Flammability | HB | dry | IEC 60695-11-10 | 1.5 mm | UL recognition :Yes | |
Glass transition temperature | 75 °C Show Supplier Material materials with Glass transition temperature of 75 °C | dry | ISO 11357-1/-2 | 10°C/min | ||
Glow Wire Flammability Index | 675 °C Show Supplier Material materials with Glow Wire Flammability Index of 675 °C | dry | IEC 60695-2-12 | 0.75 mm | ||
960 °C Show Supplier Material materials with Glow Wire Flammability Index of 960 °C | dry | IEC 60695-2-12 | 3 mm | |||
Glow Wire Ignition Temperature | 700 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 700 °C | dry | IEC 60695-2-13 | 0.75 mm | ||
725 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 725 °C | dry | IEC 60695-2-13 | 3 mm | |||
Heat deflection temperature | 290 °C Show Supplier Material materials with Heat deflection temperature of 290 °C | dry | ISO 75-1/-2 | 2 MPa | ||
290 °C Show Supplier Material materials with Heat deflection temperature of 290 °C | dry | ISO 75-1/-2 | 0.45 MPa | |||
Melting point | 295 °C Show Supplier Material materials with Melting point of 295 °C | dry | ISO 11357-1/-3 | 10°C/min | ||
Relative temperature index, electrical | 65 °C Show Supplier Material materials with Relative temperature index, electrical of 65 °C | dry | UL746B | 0.75 mm | ||
Relative temperature index, mechanical impact | 65 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 65 °C | dry | UL746B | 0.75 mm | ||
Relative temperature index, mechanical strength | 65 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 65 °C | dry | UL746B | 0.75 mm | ||
Thermal diffusivity | 1.31e-07 mm²/s Show Supplier Material materials with Thermal diffusivity of 1.31e-07 mm²/s | dry | - | |||
Vicat softening temperature | 290 °C Show Supplier Material materials with Vicat softening temperature of 290 °C | dry | ISO 306 | 50°C/h 50N |
Rheological Properties
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Density of melt | 1190 g/cm³ Show Supplier Material materials with Density of melt of 1190 g/cm³ | dry | - | |
Shrinkage | 0.5 % Show Supplier Material materials with Shrinkage of 0.5 % | dry | Sim. to ISO 294-4 | Parallel |
1.3 % Show Supplier Material materials with Shrinkage of 1.3 % | dry | Sim. to ISO 294-4 | Normal | |
Specific heat capacity melt | 2290 J/(kg·K) Show Supplier Material materials with Specific heat capacity melt of 2290 J/(kg·K) | dry | - | |
Spiral flow length | 145 | dry | - | 1.0 mm 800 bar |
170 | dry | - | 1.0 mm 900 bar | |
195 | dry | - | 1.0 mm 1000 bar | |
86 | dry | - | 0.5mm 1200 bar | |
110 | dry | - | 0.5mm 1600 bar | |
132 | dry | - | 0.5mm 2000 bar | |
Thermal conductivity of melt | 0.367 W/(m·K) Show Supplier Material materials with Thermal conductivity of melt of 0.367 W/(m·K) | dry | - | |
Viscosity number | 85 cm³/gr Show Supplier Material materials with Viscosity number of 85 cm³/gr | dry | ISO 307, 1157, 1628 |
Technological properties
Property | ||
---|---|---|
Certifications | Yellow Card Available | |
Fillers | 30% Glass Fiber |