Epoxy NU 6110 T/V

Alternative and trade names
Epoxy NU 6110 T/V
Want to keep this datasheet? Save it now in your required format

Description

Glass fibre reinforced epoxy moulding compound with very good mechanical properties for high temperature applications. Shelf life: 18 months at temperatures ≤ 8°C or 6 months at temperatures ≤18°C

This material data has been provided by Duresco GmbH.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

2 g/cm³

Show Supplier Material materials with Density of 2 g/cm³

DIN 53479

Water absorption

23.0 °C

0.03 %

Show Supplier Material materials with Water absorption of 0.03 %

ISO 62, 100°C/30 min

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

18 GPa

Show Supplier Material materials with Elastic modulus of 18 GPa

ISO 178 (Flexural Test)

Elongation

23.0 °C

1.2 %

Show Supplier Material materials with Elongation of 1.2 %

ISO 178

Flexural strength

23.0 °C

165 MPa

Show Supplier Material materials with Flexural strength of 165 MPa

ISO 178

Impact strength, Charpy notched

23.0 °C

3.8 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 3.8 kJ/m²

ISO 179-1

Impact strength, Charpy unnotched

23.0 °C

16 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 16 kJ/m²

ISO 179-1

Tensile strength

23.0 °C

80 MPa

Show Supplier Material materials with Tensile strength of 80 MPa

ISO 527

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.8E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 1.8E-5 1/K

ISO 11359-2, Mean value for 20-105°C

Glass transition temperature

160 °C

Show Supplier Material materials with Glass transition temperature of 160 °C

ISO 6721-7

Relative temperature index, mechanical strength

150 °C

Show Supplier Material materials with Relative temperature index, mechanical strength of 150 °C

UL 746 (Flexural Test)

Thermal conductivity

23.0 °C

0.85 W/(m·K)

Show Supplier Material materials with Thermal conductivity of 0.85 W/(m·K)

ISO 8894

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

275 V

Show Supplier Material materials with Comparative tracking index of 275 V

IEC 60112

Dielectric constant, 50Hz

23.0 °C

5.2 [-]

Show Supplier Material materials with Dielectric constant, 50Hz of 5.2 [-]

IEC 60250

Dielectric strength

23.0 °C

23 kV/mm

Show Supplier Material materials with Dielectric strength of 23 kV/mm

IEC 60243-1, 3mm Plate

Loss tangent, 50Hz

23.0 °C

1.1 [-]

Show Supplier Material materials with Loss tangent, 50Hz of 1.1 [-]

IEC 60250

Volume resistivity

23.0 °C

1.00E+14 Ω·cm

Show Supplier Material materials with Volume resistivity of 1.00E+14 Ω·cm

IEC 60093

Technological properties

Property
Application areas

Encapsulation of electrical devices e.g. Protection of PCB, Solenoids, Sensors

Fillers

Glass Fiber