General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.95 g/cm³ Show Supplier Material materials with Density of 1.95 g/cm³ | DIN 53479 |
Water absorption | 23.0 °C | 0.06 % Show Supplier Material materials with Water absorption of 0.06 % | ISO 62, 100°C/30 min |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 17 GPa Show Supplier Material materials with Elastic modulus of 17 GPa | ISO 178 (Flexural Test) |
Elongation | 23.0 °C | 1.4 % Show Supplier Material materials with Elongation of 1.4 % | ISO 178 |
Flexural strength | 23.0 °C | 190 MPa Show Supplier Material materials with Flexural strength of 190 MPa | ISO 178 |
Impact strength, Charpy unnotched | 23.0 °C | 22 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 22 kJ/m² | ISO 179-1 |
Tensile strength | 23.0 °C | 100 MPa Show Supplier Material materials with Tensile strength of 100 MPa | ISO 527 |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 2E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2E-5 1/K | ISO 11359-2, Mean value for 20-105°C |
Glass transition temperature | 120 °C Show Supplier Material materials with Glass transition temperature of 120 °C | ISO 6721-7 | |
Thermal conductivity | 23.0 °C | 0.85 W/(m·K) Show Supplier Material materials with Thermal conductivity of 0.85 W/(m·K) | ISO 8894 |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 300 V Show Supplier Material materials with Comparative tracking index of 300 V | IEC 60112 |
Dielectric constant, 50Hz | 23.0 °C | 5 [-] Show Supplier Material materials with Dielectric constant, 50Hz of 5 [-] | IEC 60250 |
Loss tangent, 50Hz | 23.0 °C | 1.6 [-] Show Supplier Material materials with Loss tangent, 50Hz of 1.6 [-] | IEC 60250 |
Volume resistivity | 23.0 °C | 1.00E+14 Ω·cm Show Supplier Material materials with Volume resistivity of 1.00E+14 Ω·cm | IEC 60093 |
Technological properties
Property | ||
---|---|---|
Application areas | Encapsulation of electrical devices, e.g. Electronic, Sensors, Solenoids, Stators | |
Fillers | Glass Fiber |