General
Property | Temperature | Value |
---|---|---|
Density | 23.0 °C | 10.4 g/cm³ Show Supplier Material materials with Density of 10.4 g/cm³ |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 76 GPa Show Supplier Material materials with Elastic modulus of 76 GPa | |
Elongation | 23.0 °C | 30 % Show Supplier Material materials with Elongation of 30 % | min. |
Hardness, Vickers | 23.0 °C | 30 - 80 [-] Show Supplier Material materials with Hardness, Vickers of 30 - 80 [-] | |
Shear modulus | 23.0 °C | 24 GPa Show Supplier Material materials with Shear modulus of 24 GPa | |
Tensile strength | 23.0 °C | 170 - 260 MPa Show Supplier Material materials with Tensile strength of 170 - 260 MPa | |
Yield strength Rp0.2 | 23.0 °C | 50 - 190 MPa Show Supplier Material materials with Yield strength Rp0.2 of 50 - 190 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.85E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.85E-5 1/K | RT-100 °C |
Melting point | 900 - 938 °C Show Supplier Material materials with Melting point of 900 - 938 °C | ||
Thermal conductivity | 23.0 °C | 372 W/(m·K) Show Supplier Material materials with Thermal conductivity of 372 W/(m·K) |
Electrical
Property | Temperature | Value |
---|---|---|
Electrical resistivity | 23.0 °C | 1.8E-8 - 1.9E-8 Ω·m Show Supplier Material materials with Electrical resistivity of 1.8E-8 - 1.9E-8 Ω·m |
Specific Electrical conductivity | 90.5 - 95.6 % IACS Show Supplier Material materials with Specific Electrical conductivity of 90.5 - 95.6 % IACS | |
Temperature coefficient of resistance | 23.0 °C | 2.5E-3 1/K Show Supplier Material materials with Temperature coefficient of resistance of 2.5E-3 1/K |
Technological properties
Property | ||
---|---|---|
Application areas | Collectors, communicators | |
Corrosion properties | Corrosion resistant | |
Other | Ductile, can be roll clad, formable, machinable, sensitive to sulphur |