General
Property | Temperature | Value |
---|---|---|
Density | 23.0 °C | 18.7 g/cm³ Show Supplier Material materials with Density of 18.7 g/cm³ |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Creep strength | 1200.0 °C | 13.6 MPa Show Supplier Material materials with Creep strength of 13.6 MPa | 10,000 h (extrapolated data) |
1400.0 °C | 7.1 MPa Show Supplier Material materials with Creep strength of 7.1 MPa | 10,000 h (extrapolated data) | |
1600.0 °C | 6.1 MPa Show Supplier Material materials with Creep strength of 6.1 MPa | 10,000 h (extrapolated data) | |
Elastic modulus | 20.0 °C | 247.8 GPa Show Supplier Material materials with Elastic modulus of 247.8 GPa | |
1200.0 °C | 180 GPa Show Supplier Material materials with Elastic modulus of 180 GPa | ||
1400.0 °C | 170 GPa Show Supplier Material materials with Elastic modulus of 170 GPa | ||
1600.0 °C | 150 GPa Show Supplier Material materials with Elastic modulus of 150 GPa | ||
Elongation | 20.0 °C | 35.8 % Show Supplier Material materials with Elongation of 35.8 % | |
Hardness, Vickers | 23.0 °C | 130 [-] Show Supplier Material materials with Hardness, Vickers of 130 [-] | |
Norton Exponent | 1200.0 °C | 6.3 [-] Show Supplier Material materials with Norton Exponent of 6.3 [-] | |
1400.0 °C | 10 [-] Show Supplier Material materials with Norton Exponent of 10 [-] | ||
1600.0 °C | 9.3 [-] Show Supplier Material materials with Norton Exponent of 9.3 [-] | ||
Tensile strength | 23.0 °C | 464.7 MPa Show Supplier Material materials with Tensile strength of 464.7 MPa | |
Yield strength Rp0.2 | 20.0 °C | 147.4 MPa Show Supplier Material materials with Yield strength Rp0.2 of 147.4 MPa |
Thermal
Property | Value |
---|---|
Melting point | 1830 - 1855 °C Show Supplier Material materials with Melting point of 1830 - 1855 °C |