VYPET™ VNT-2330 BK

Alternative and trade names
PBT+PET-GF30

Want to keep this datasheet? Save it now in your required format

Description

Polybutylene Terephthalate (PBT) and Polyethylene Terephthalate (PET) alloy with 30% Glass Fiber Reinforced and Flame Retardant. Contains a minimum of 30% Post-consumer resin

This material data has been provided by Lavergne.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.5 g/cm³ Show Supplier Material materials with Density of 1.5 g/cm³	ISO 1183
Recycled Content		30 % Show Supplier Material materials with Recycled Content of 30 %
Water absorption	23.0 °C	0.06 % Show Supplier Material materials with Water absorption of 0.06 %	ASTM D570, 23°C/24hr

Mechanical

Property	Temperature	Value	Comment
Flexural modulus	23.0 °C	8 GPa Show Supplier Material materials with Flexural modulus of 8 GPa	ISO 178, 2 mm/min
Flexural strength	23.0 °C	190 MPa Show Supplier Material materials with Flexural strength of 190 MPa	ISO 178, 2 mm/min
Impact strength, Charpy notched	23.0 °C	14 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 14 kJ/m²	ISO 179eA
Impact strength, Charpy unnotched	23.0 °C	70 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 70 kJ/m²	ISO 179eA
Tensile strength	23.0 °C	120 MPa Show Supplier Material materials with Tensile strength of 120 MPa	ISO 527, 5 mm/min

Thermal

Property	Temperature	Value	Comment
Ash content	23.0 °C	30 % Show Supplier Material materials with Ash content of 30 %	ASTM D5630
Heat deflection temperature, 1.80 MPa		202 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 202 °C	ISO-75
Melting point		240 °C Show Supplier Material materials with Melting point of 240 °C	ISO 3146
Flammability	HB for 3.2 mm sample UL94

Electrical

Property	Temperature	Value	Comment
Dielectric strength	23.0 °C	33 kV/mm Show Supplier Material materials with Dielectric strength of 33 kV/mm	ASTM D149, 1.6 mm, 500V/s in oil
Dissipation factor, 1kHz	23.0 °C	2E-3 [-] Show Supplier Material materials with Dissipation factor, 1kHz of 2E-3 [-]	ASTM D150
Surface resistivity	23.0 °C	1.00E+17 Ω/sq Show Supplier Material materials with Surface resistivity of 1.00E+17 Ω/sq	ASTM D257
Volume resistivity	23.0 °C	2.00E+16 Ω·cm Show Supplier Material materials with Volume resistivity of 2.00E+16 Ω·cm	ASTM D257

Rheological Properties

Property	Temperature	Value	Comment
Shrinkage	23.0 °C	0.4 - 0.6 % Show Supplier Material materials with Shrinkage of 0.4 - 0.6 %	ASTM D955
Shrinkage, transverse	23.0 °C	0.6 - 0.9 % Show Supplier Material materials with Shrinkage, transverse of 0.6 - 0.9 %	ASTM D955

Technological properties

Property
Application areas	Eelcrtical components (e.g. connectros) and structural components.
Certifications	RoHS,RECH,ULE Environmental Claims Validation
Fillers	30% Glass Fiber
Processing methods	Drying to Dew Point:-18°C or lower Feed zone: 250-260°C Middle zone: 260-270°C Front zone: 270-280°C Nozzle: 270-290°C Melt temperature: 275-290°C Mold temperature (thick wall parts): 75-95°C Mold temperature (thin wall parts): 80-100°C Injection Pressure: 55-85 MPa (8-12 kpsi) Injection Speed: Fast Back Pressure: 25-50 PSI Screw Speed: 50-75 rpm