VYPET™ VNT-102 HS

Want to keep this datasheet? Save it now in your required format

Description

Polyethylene Terephthalate (PET) - unfilled

This material data has been provided by Lavergne.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.33 g/cm³ Show Supplier Material materials with Density of 1.33 g/cm³	ISO 1183

Mechanical

Property	Temperature	Value	Comment
Flexural modulus	23.0 °C	2.8 GPa Show Supplier Material materials with Flexural modulus of 2.8 GPa	ASTM D790
Flexural strength	23.0 °C	90 MPa Show Supplier Material materials with Flexural strength of 90 MPa	ASTM D790, 1.3 mm/min
Impact strength, Izod notched	23.0 °C	33 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 33 kJ/m²	ISO 180
Yield strength	23.0 °C	58 MPa Show Supplier Material materials with Yield strength of 58 MPa	ASTM D638, 50 mm/min

Thermal

Property	Value	Comment
Heat deflection temperature, 1.80 MPa	72 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 72 °C	ASTM D648
Melting point	246 °C Show Supplier Material materials with Melting point of 246 °C	ASTM D3418
Flammability	HB for 3.2 mm sample UL94

Technological properties

Property

Certifications

RoHS,RECH,ULE Environmental Claims Validation

Processing methods

Drying to Dew Point:-18°C or lower

Feed zone: 270-285°C

Middle zone: 270-280°C

Front zone: 260-275°C

Nozzle: 275-285°C

Melt temperature: 265-285°C

Mold temperature (thick wall parts): 15-40°C

Mold temperature (thin wall parts): 15-40°C

Injection Speed: Medium-Fast

Back Pressure: Low

Screw Speed: Medium