DIN 1712-3 Grade 3.0305 H14

Want to keep this datasheet? Save it now in your required format

Description

Pure aluminium This material is well anodically oxidisable, has a good electrical and thermal conductivity. The splinter-giving workability is bad because of danger of smearing. Its mechanical strength is low, the plasticity is high. The forming capacity and the chemical as well as weather proofness are excellent. For welding and braze welding the material is well suitable. Application: Apparatus engineering, roll bond, z-bond, household devices, camp and transportation containers for the chemical, pharmaceutical and food industry, roofing, linings, arts and crafts, packing, flow pressed parts (tubes, tube, doses, bottles).

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Properties

General

Property	Temperature	Value	Condition	Related Standards	Shape
Density	20.0 °C	2.7 g/cm³ Show Material materials with Density of 2.7 g/cm³	H14	DIN 1712-3, EN 573-3, EN 573-4	Wire

Mechanical

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Elastic modulus	20.0 °C	70.0 Show Material materials with Elastic modulus of 70.0	H14	DIN 1712-3, EN 573-3, EN 573-4	Wire
Hardness, Brinell	20.0 °C	20.0 [-] Show Material materials with Hardness, Brinell of 20.0 [-]	H14	DIN 1712-3, EN 573-3, EN 573-4	Wire
Plane-Strain Fracture Toughnes		22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m				Typical for Wrought 1000 Series Aluminium
Poisson's ratio		0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-]				Typical for Wrought 1000 Series Aluminium
Shear modulus	20.0 °C	25.0 GPa Show Material materials with Shear modulus of 25.0 GPa	H14	DIN 1712-3, EN 573-3, EN 573-4	Wire
Tensile strength	20.0 °C	70.0 MPa Show Material materials with Tensile strength of 70.0 MPa	H14	DIN 1712-3, EN 573-3, EN 573-4	Wire

Thermal

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Coefficient of thermal expansion		2.2e-05 - 2.5e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.2e-05 - 2.5e-05 1/K				Typical for Wrought 1000 Series Aluminium
Melting point		645.0 - 660.0 °C Show Material materials with Melting point of 645.0 - 660.0 °C				Typical for Wrought 1000 Series Aluminium
Specific heat capacity	20.0 °C	921.0 J/(kg·K) Show Material materials with Specific heat capacity of 921.0 J/(kg·K)	H14	DIN 1712-3, EN 573-3, EN 573-4	Wire
Thermal conductivity	20.0 °C	215.0 W/(m·K) Show Material materials with Thermal conductivity of 215.0 W/(m·K)	H14	DIN 1712-3, EN 573-3, EN 573-4	Wire

Electrical

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Electrical conductivity	20.0 °C	37000000.0 Show Material materials with Electrical conductivity of 37000000.0	H14	DIN 1712-3, EN 573-3, EN 573-4	Wire
Electrical resistivity		2.7e-08 - 3e-08 Ω·m Show Material materials with Electrical resistivity of 2.7e-08 - 3e-08 Ω·m				Typical for Wrought 1000 Series Aluminium

Chemical properties

Property	Value	Condition	Related Standards	Shape
Copper	0.01 Show Material materials with Copper of 0.01	H14	DIN 1712-3, EN 573-3, EN 573-4	Wire
Gallium	0.03 Show Material materials with Gallium of 0.03	H14	DIN 1712-3, EN 573-3, EN 573-4	Wire
Iron	0.05 Show Material materials with Iron of 0.05	H14	DIN 1712-3, EN 573-3, EN 573-4	Wire
Magnesium	0.01 Show Material materials with Magnesium of 0.01	H14	DIN 1712-3, EN 573-3, EN 573-4	Wire
Manganese	0.01 Show Material materials with Manganese of 0.01	H14	DIN 1712-3, EN 573-3, EN 573-4	Wire
Silicon	0.06 Show Material materials with Silicon of 0.06	H14	DIN 1712-3, EN 573-3, EN 573-4	Wire
Titanium	0.006 Show Material materials with Titanium of 0.006	H14	DIN 1712-3, EN 573-3, EN 573-4	Wire
Zinc	0.04 Show Material materials with Zinc of 0.04	H14	DIN 1712-3, EN 573-3, EN 573-4	Wire

Technological properties

Property

Brazing

Excellent

Workability

Excellent workability.