DIN 1725-1 Grade 3.3207 T5

Want to keep this datasheet? Save it now in your required format

Description

E-AlMgSi0,5 is ensured by the German electrotechnical commission as alloy for electro-technology according to DIN 40 501 part of 1 to part of 4. This cold and hothardenable material reaches mechanical strength in range of 200 to 250 MPa with A5-elongation at break of approx. 10 %. In hot and/or cold hardend state is this alloy only limited formable, in the soft material condition however well. Weldability, corrosion resistance and anodising ability of this material are good. Heat treatment for hardening: solution annealing: 525 to 540 °C, quenching on air or in water cold ageing: 5 to 8 d at ambient temperatures warm ageing: 4 to 16 h at 155 to 190 °C. Application: The alloy E-AlMgSi0,5 is used with priority for bus bars. Because of the good extruding bar of this material as flat -, profile or tubing bus bars. Electro-technology (bus bars)

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueConditionRelated StandardsShape

Density

20.0 °C

2.7 g/cm³

Show Material materials with Density of 2.7 g/cm³

T5

DIN 1725-1, EN 573-3, EN 573-4

Profile, Rod, Tube

Mechanical

PropertyTemperatureValueConditionRelated StandardsShapeComment

Elastic modulus

70.0 GPa

Show Material materials with Elastic modulus of 70.0 GPa

Typical for Wrought 6000 Series Aluminium

Elongation

20.0 °C

10.0 %

Show Material materials with Elongation of 10.0 %

T5

DIN 1725-1, EN 573-3, EN 573-4

Profile, Rod, Tube

A10

20.0 °C

12.0 %

Show Material materials with Elongation of 12.0 %

T5

DIN 1725-1, EN 573-3, EN 573-4

Profile, Rod, Tube

20.0 °C

8.0 %

Show Material materials with Elongation of 8.0 %

T5

DIN 1725-1, EN 573-3, EN 573-4

Tube

Hardness, Brinell

20.0 °C

45.0 - 65.0 [-]

Show Material materials with Hardness, Brinell of 45.0 - 65.0 [-]

T5

DIN 1725-1, EN 573-3, EN 573-4

Profile, Rod

20.0 °C

65.0 - 90.0 [-]

Show Material materials with Hardness, Brinell of 65.0 - 90.0 [-]

T5

DIN 1725-1, EN 573-3, EN 573-4

Rod

20.0 °C

65.0 - 80.0 [-]

Show Material materials with Hardness, Brinell of 65.0 - 80.0 [-]

T5

DIN 1725-1, EN 573-3, EN 573-4

Tube

Unlock all property charts

Plane-Strain Fracture Toughnes

22.0 - 35.0 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m

Typical for Wrought 6000 Series Aluminium

Poisson's ratio

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-]

Typical for Wrought 6000 Series Aluminium

Shear modulus

20.0 °C

25.5 GPa

Show Material materials with Shear modulus of 25.5 GPa

T5

DIN 1725-1, EN 573-3, EN 573-4

Profile, Rod, Tube

Tensile strength

20.0 °C

170.0 - 220.0 MPa

Show Material materials with Tensile strength of 170.0 - 220.0 MPa

T5

DIN 1725-1, EN 573-3, EN 573-4

Profile, Rod

20.0 °C

215.0 - 280.0 MPa

Show Material materials with Tensile strength of 215.0 - 280.0 MPa

T5

DIN 1725-1, EN 573-3, EN 573-4

Rod, Tube

Unlock all property charts

Thermal

PropertyTemperatureValueConditionRelated StandardsShapeComment

Coefficient of thermal expansion

1.6e-05 - 2.4e-05 1/K

Show Material materials with Coefficient of thermal expansion of 1.6e-05 - 2.4e-05 1/K

Typical for Wrought 6000 Series Aluminium

Melting point

555.0 - 655.0 °C

Show Material materials with Melting point of 555.0 - 655.0 °C

Typical for Wrought 6000 Series Aluminium

Specific heat capacity

20.0 °C

898.0 J/(kg·K)

Show Material materials with Specific heat capacity of 898.0 J/(kg·K)

T5

DIN 1725-1, EN 573-3, EN 573-4

Profile, Rod, Tube

Thermal conductivity

20.0 °C

220.0 W/(m·K)

Show Material materials with Thermal conductivity of 220.0 W/(m·K)

T5

DIN 1725-1, EN 573-3, EN 573-4

Profile, Rod, Tube

Electrical

PropertyValueComment

Electrical conductivity

21000000.0 - 34000000.0 S/m

Show Material materials with Electrical conductivity of 21000000.0 - 34000000.0 S/m

Typical for Wrought 6000 Series Aluminium

Electrical resistivity

2.9e-08 - 5e-08 Ω·m

Show Material materials with Electrical resistivity of 2.9e-08 - 5e-08 Ω·m

Typical for Wrought 6000 Series Aluminium

Chemical properties

PropertyValueConditionRelated StandardsShape

Copper

0.05

Show Material materials with Copper of 0.05

T5

DIN 1725-1, EN 573-3, EN 573-4

Profile, Rod, Tube

Iron

0.1 - 0.3 %

Show Material materials with Iron of 0.1 - 0.3 %

T5

DIN 1725-1, EN 573-3, EN 573-4

Profile, Rod, Tube

Magnesium

0.35 - 0.6 %

Show Material materials with Magnesium of 0.35 - 0.6 %

T5

DIN 1725-1, EN 573-3, EN 573-4

Profile, Rod, Tube

Manganese

0.05

Show Material materials with Manganese of 0.05

T5

DIN 1725-1, EN 573-3, EN 573-4

Profile, Rod, Tube

Silicon

0.3 - 0.6 %

Show Material materials with Silicon of 0.3 - 0.6 %

T5

DIN 1725-1, EN 573-3, EN 573-4

Profile, Rod, Tube

Zinc

0.1

Show Material materials with Zinc of 0.1

T5

DIN 1725-1, EN 573-3, EN 573-4

Profile, Rod, Tube

Technological properties

Property
Workability

Excellent workability.