ASTM B241 Grade 1100 H112

.XLSX
.PDF
Save

Description

Related Standards

Equivalent Materials

Properties

General

Density ρ

2.7 g/cm³ at 20 °C

Typical for Wrought 1000 Series Aluminium

Mechanical

Elastic modulus E

68 - 70 GPa at 20 °C

Typical for Wrought 1000 Series Aluminium

Elongation A

22 % at 20 °C

Elongation A50 A50

25 % at 20 °C

Fracture toughness KIC

22 - 35 MPa·√m at 20 °C

Typical for Wrought 1000 Series Aluminium

Poisson's ratio ν

0.33 [-] at 20 °C

Typical for Wrought 1000 Series Aluminium

Shear modulus G

25.9 GPa at 20 °C

Typical for Wrought 1000 Series Aluminium

Tensile strength Rm

75 MPa at 20 °C

Yield Strength Rp0.2, short transverse Rp0.2,shorttrans_

20 MPa at 20 °C

Thermal

Coefficient of thermal expansion α

2.2E-5 - 2.5E-5 1/K at 20 °C

Typical for Wrought 1000 Series Aluminium

Melting point Tm

646 - 658 °C

Typical for Wrought 1000 Series Aluminium

Specific heat capacity cp

900 - 963 J/(kg·K) at 20 °C

Typical for Wrought 1000 Series Aluminium

Thermal conductivity λ

167 - 244 W/(m·K) at 20 °C

Typical for Wrought 1000 Series Aluminium

Electrical

Electrical conductivity σel

3.30E+7 - 3.80E+7 S/m at 20 °C

Typical for Wrought 1000 Series Aluminium

Electrical resistivity ρel

2.7E-8 - 3E-8 Ω·m at 20 °C

Typical for Wrought 1000 Series Aluminium

Chemical properties

Element

Weight %

Comment

Al

99 %

Si

0.95 %

Zn

0.1 %

Cu

0.05 - 0.2 %

Mn

0.05 %

Technological properties

Brazing

Excellent

Workability

Excellent workability.

This material data has been provided by ASTM.