Property | Value | Comment |
---|---|---|
Density | 2.75 - 2.84 g/cm³ Show Material materials with Density of 2.75 - 2.84 g/cm³ | Typical for Wrought 2000 Series Aluminium |
Mechanical
Property | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|
Elastic modulus | 70.0 - 73.0 GPa Show Material materials with Elastic modulus of 70.0 - 73.0 GPa | Typical for Wrought 2000 Series Aluminium | |||
Elongation | 16.0 % Show Material materials with Elongation of 16.0 % | T4 | ASTM B316 | Wire, Rod | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 2000 Series Aluminium | |||
Shear modulus | 26.0 - 27.5 GPa Show Material materials with Shear modulus of 26.0 - 27.5 GPa | Typical for Wrought 2000 Series Aluminium | |||
Shear strength | 180.0 MPa Show Material materials with Shear strength of 180.0 MPa | T4 | ASTM B316 | Wire, Rod | |
Tensile strength | 260.0 MPa Show Material materials with Tensile strength of 260.0 MPa | T4 | ASTM B316 | Wire, Rod |
Thermal
Property | Value | Comment |
---|---|---|
Coefficient of thermal expansion | 1.6e-05 - 2.4e-05 1/K Show Material materials with Coefficient of thermal expansion of 1.6e-05 - 2.4e-05 1/K | Typical for Wrought 2000 Series Aluminium |
Melting point | 500.0 - 650.0 °C Show Material materials with Melting point of 500.0 - 650.0 °C | Typical for Wrought 2000 Series Aluminium |
Specific heat capacity | 816.0 - 963.0 J/(kg·K) Show Material materials with Specific heat capacity of 816.0 - 963.0 J/(kg·K) | Typical for Wrought 2000 Series Aluminium |
Thermal conductivity | 112.0 - 251.0 W/(m·K) Show Material materials with Thermal conductivity of 112.0 - 251.0 W/(m·K) | Typical for Wrought 2000 Series Aluminium |
Electrical
Property | Value | Comment |
---|---|---|
Electrical conductivity | 18000000.0 - 30000000.0 S/m Show Material materials with Electrical conductivity of 18000000.0 - 30000000.0 S/m | Typical for Wrought 2000 Series Aluminium |
Electrical resistivity | 3.4e-08 - 6e-08 Ω·m Show Material materials with Electrical resistivity of 3.4e-08 - 6e-08 Ω·m | Typical for Wrought 2000 Series Aluminium |
Chemical properties
Property | Value | Condition | Related Standards | Shape |
---|---|---|---|---|
Chromium | 0.1 Show Material materials with Chromium of 0.1 | T4 | ASTM B316 | Wire, Rod |
Copper | 2.2 - 3.0 % Show Material materials with Copper of 2.2 - 3.0 % | T4 | ASTM B316 | Wire, Rod |
Iron | 0.7 Show Material materials with Iron of 0.7 | T4 | ASTM B316 | Wire, Rod |
Magnesium | 0.2 - 0.5 % Show Material materials with Magnesium of 0.2 - 0.5 % | T4 | ASTM B316 | Wire, Rod |
Manganese | 0.2 Show Material materials with Manganese of 0.2 | T4 | ASTM B316 | Wire, Rod |
Silicon | 0.8 Show Material materials with Silicon of 0.8 | T4 | ASTM B316 | Wire, Rod |
Zinc | 0.25 Show Material materials with Zinc of 0.25 | T4 | ASTM B316 | Wire, Rod |
Technological properties
Property | ||
---|---|---|
Workability | Moderate Workability |