JIS H4080 Grade 6063 T6

Want to keep this datasheet? Save it now in your required format

Description

Aluminum JIS 6063 is an architectural alloy that offers users a high resistance to corrosion and excellent finishing characteristics. Easy to extrude with fair machinability, JIS 6063 can be both hot and cold formed and is commonly available as T6 temper as well as T4 temper.

Related Standards

Equivalent Materials

This material data has been provided by Japanese Industrial Standards.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueComment

Density

2.7 g/cm³

Show Material materials with Density of 2.7 g/cm³

Typical for Wrought 6000 Series Aluminium

Mechanical

PropertyValueConditionRelated StandardsComment

Elastic modulus

70.0 GPa

Show Material materials with Elastic modulus of 70.0 GPa

Typical for Wrought 6000 Series Aluminium

Elongation

8.0 %

Show Material materials with Elongation of 8.0 %

T6

JIS H4080

Plane-Strain Fracture Toughnes

22.0 - 35.0 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m

Typical for Wrought 6000 Series Aluminium

Poisson's ratio

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-]

Typical for Wrought 6000 Series Aluminium

Shear modulus

26.0 - 26.5 GPa

Show Material materials with Shear modulus of 26.0 - 26.5 GPa

Typical for Wrought 6000 Series Aluminium

Tensile strength

206.0 MPa

Show Material materials with Tensile strength of 206.0 MPa

T6

JIS H4080

Yield strength

167.0 MPa

Show Material materials with Yield strength of 167.0 MPa

T6

JIS H4080

Thermal

PropertyValueComment

Coefficient of thermal expansion

1.6e-05 - 2.4e-05 1/K

Show Material materials with Coefficient of thermal expansion of 1.6e-05 - 2.4e-05 1/K

Typical for Wrought 6000 Series Aluminium

Melting point

555.0 - 655.0 °C

Show Material materials with Melting point of 555.0 - 655.0 °C

Typical for Wrought 6000 Series Aluminium

Specific heat capacity

887.0 - 963.0 J/(kg·K)

Show Material materials with Specific heat capacity of 887.0 - 963.0 J/(kg·K)

Typical for Wrought 6000 Series Aluminium

Thermal conductivity

170.0 - 220.0 W/(m·K)

Show Material materials with Thermal conductivity of 170.0 - 220.0 W/(m·K)

Typical for Wrought 6000 Series Aluminium

Electrical

PropertyValueComment

Electrical conductivity

21000000.0 - 34000000.0 S/m

Show Material materials with Electrical conductivity of 21000000.0 - 34000000.0 S/m

Typical for Wrought 6000 Series Aluminium

Electrical resistivity

2.9e-08 - 5e-08 Ω·m

Show Material materials with Electrical resistivity of 2.9e-08 - 5e-08 Ω·m

Typical for Wrought 6000 Series Aluminium

Technological properties

Property
Processing history

T6

Workability

Excellent workability.