General
Property | Value | Condition |
---|---|---|
Density | 2.78 g/cm³ Show Material materials with Density of 2.78 g/cm³ | T651 |
3.0 g/cm³ Show Material materials with Density of 3.0 g/cm³ | T651 |
Mechanical
Property | Temperature | Value | Condition | Comment |
---|---|---|---|---|
Elastic modulus | 73.0 GPa Show Material materials with Elastic modulus of 73.0 GPa | T651 | ||
Elongation | -195 °C | 11 % Show Material materials with Elongation of 11 % | T651 | Elongation in 50 mm |
-80 °C | 10 % Show Material materials with Elongation of 10 % | T651 | Elongation in 50 mm | |
4.6 % Show Material materials with Elongation of 4.6 % | T651 | |||
0 °C | 10 % Show Material materials with Elongation of 10 % | T651 | Elongation in 50 mm | |
24 °C | 10 % Show Material materials with Elongation of 10 % | T651 | Elongation in 50 mm | |
100 °C | 10 % Show Material materials with Elongation of 10 % | T651 | Elongation in 50 mm | |
150 °C | 17 % Show Material materials with Elongation of 17 % | T651 | Elongation in 50 mm | |
205 °C | 27 % Show Material materials with Elongation of 27 % | T651 | Elongation in 50 mm | |
260 °C | 55 % Show Material materials with Elongation of 55 % | T651 | Elongation in 50 mm | |
315 °C | 75 % Show Material materials with Elongation of 75 % | T651 | Elongation in 50 mm | |
370 °C | 100 % Show Material materials with Elongation of 100 % | T651 | Elongation in 50 mm | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 2000 Series Aluminium | ||
Shear modulus | 28.0 GPa Show Material materials with Shear modulus of 28.0 GPa | T651 | ||
Tensile strength | -195 °C | 580 MPa Show Material materials with Tensile strength of 580 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture |
-80 °C | 495 MPa Show Material materials with Tensile strength of 495 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
0 °C | 483 MPa Show Material materials with Tensile strength of 483 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
490.0 MPa Show Material materials with Tensile strength of 490.0 MPa | T651 | |||
24 °C | 475 MPa Show Material materials with Tensile strength of 475 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
100 °C | 448 MPa Show Material materials with Tensile strength of 448 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
150 °C | 310 MPa Show Material materials with Tensile strength of 310 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
205 °C | 180 MPa Show Material materials with Tensile strength of 180 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
260 °C | 75 MPa Show Material materials with Tensile strength of 75 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
315 °C | 52 MPa Show Material materials with Tensile strength of 52 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
370 °C | 35 MPa Show Material materials with Tensile strength of 35 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
Yield strength | -195 °C | 469 MPa Show Material materials with Yield strength of 469 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 |
-80 °C | 407 MPa Show Material materials with Yield strength of 407 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
360.0 MPa Show Material materials with Yield strength of 360.0 MPa | T651 | |||
0 °C | 400 MPa Show Material materials with Yield strength of 400 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
24 °C | 393 MPa Show Material materials with Yield strength of 393 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
100 °C | 372 MPa Show Material materials with Yield strength of 372 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
150 °C | 248 MPa Show Material materials with Yield strength of 248 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
205 °C | 131 MPa Show Material materials with Yield strength of 131 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
260 °C | 62 MPa Show Material materials with Yield strength of 62 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
315 °C | 41 MPa Show Material materials with Yield strength of 41 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
370 °C | 28 MPa Show Material materials with Yield strength of 28 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 |
Thermal
Property | Value | Condition |
---|---|---|
Coefficient of thermal expansion | 2.3e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3e-05 1/K | T651 |
Melting point | 500.0 °C Show Material materials with Melting point of 500.0 °C | T651 |
Specific heat capacity | 870.0 J/(kg·K) Show Material materials with Specific heat capacity of 870.0 J/(kg·K) | T651 |
Thermal conductivity | 120.0 W/(m·K) Show Material materials with Thermal conductivity of 120.0 W/(m·K) | T651 |
Electrical
Property | Value | Comment |
---|---|---|
Electrical conductivity | 18000000.0 - 30000000.0 S/m Show Material materials with Electrical conductivity of 18000000.0 - 30000000.0 S/m | Typical for Wrought 2000 Series Aluminium |
Electrical resistivity | 3.4e-08 - 6e-08 Ω·m Show Material materials with Electrical resistivity of 3.4e-08 - 6e-08 Ω·m | Typical for Wrought 2000 Series Aluminium |
Chemical properties
Property | Value | Condition |
---|---|---|
Aluminium | 90.7 - 94.7 % Show Material materials with Aluminium of 90.7 - 94.7 % | T651 |
Chromium | 0.1 % Show Material materials with Chromium of 0.1 % | T651 |
Copper | 3.8 - 4.9 % Show Material materials with Copper of 3.8 - 4.9 % | T651 |
Iron | 0.5 % Show Material materials with Iron of 0.5 % | T651 |
Magnesium | 1.2 - 1.8 % Show Material materials with Magnesium of 1.2 - 1.8 % | T651 |
Manganese | 0.3 - 0.9 % Show Material materials with Manganese of 0.3 - 0.9 % | T651 |
Other | 0.15 % Show Material materials with Other of 0.15 % | T651 |
Silicon | 0.5 % Show Material materials with Silicon of 0.5 % | T651 |
Titanium | 0.15 % Show Material materials with Titanium of 0.15 % | T651 |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | T651 |
Zirconium | 0.2 % Show Material materials with Zirconium of 0.2 % | T651 |
Technological properties
Property | ||
---|---|---|
Workability | Moderate Workability |