AA Standards Grade 2219 O

Want to keep this datasheet? Save it now in your required format

Description

Related Standards

Equivalent Materials

Ashby charts

See where AA Standards Grade 2219 O falls on the material property chart for Density against Elastic modulus in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

Density

ρ

2.84 - 3.1 g/cm³ at 20 °C

Dimension

Dimensions

Dicke

Mechanical

Elastic modulus

E

73 - 74 GPa at 20 °C

Elongation

A

15 % at 20 °C

Elongation A100

A100

10 % at 20 °C

Elongation A50

A50

12 - 18 % at 20 °C

Plane-Strain Fracture Toughnes

KIC

22 - 35 MPa·√m at 20 °C

Typical for Wrought 2000 Series Aluminium

Poisson's ratio

ν

0.33 [-] at 20 °C

Typical for Wrought 2000 Series Aluminium

Shear modulus

G

26 - 27.5 GPa at 20 °C

Typical for Wrought 2000 Series Aluminium

Tensile strength

Rm

170 - 220 MPa at 20 °C

Yield strength

YS

88 MPa at 20 °C

Yield strength Rp0.2

Rp0.2

75 - 125 MPa at 20 °C

Thermal

Coefficient of thermal expansion

α

2.2E-5 - 2.23E-5 1/K at 20 °C

Hide chart

Melting point

Tm

540 - 645 °C

Specific heat capacity

cp

860 J/(kg·K) at 20 °C

Thermal conductivity

λ

113 - 172 W/(m·K) at 20 °C

Electrical

Electrical conductivity

σel

1.60E+7 - 2.55E+8 S/m at 20 °C

Typical value

Electrical resistivity

ρel

3.8E-8 - 6.25E-8 Ω·m at 20 °C

Typical value

Specific Electrical conductivity

45 % IACS

Typical/Derived value

Chemical properties

Element

Weight %

Comment

Al

91.5 - 93.8 %

Cu

5.8 - 6.8 %

Mn

0.2 - 0.4 %

Zr

0.1 - 0.25 %

V

0.05 - 0.15 %

More

Technological properties

Brazing

general: no brazing is known or developed

Corrosion properties

Stress corrosion cracking: Betriebsschäden in Gebieten mit Zugspannungen quer zur Kornstruktur, Eingeschränkte Schäden an Laborproben (T31, T351, T3510, T3511, T37), kein Schadensfall im Betrieb, eingeschränkte Schäden bei den Labortests (T81, T851, T8510, T8511), general: sufficient, in principle it should be protected

General machinability

General: good to acceptable

Workability

general (condition): poor(T31, T351, T3510, T3511), not suitable (T37, T81, T851, T8510, T8511, T87)

This material data has been provided by MakeItFrom.com,WroughtAl_ElectricalResistivity,AluKey.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.