Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.84 g/cm³ Show Material materials with Density of 2.84 g/cm³ | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
2.84 g/cm³ Show Material materials with Density of 2.84 g/cm³ | T62 | ||
3.1 g/cm³ Show Material materials with Density of 3.1 g/cm³ | T62 |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Bending Fatigue Strength | 105.0 MPa Show Material materials with Bending Fatigue Strength of 105.0 MPa | T62 | AA Standards | ||
Elastic modulus | 73.0 GPa Show Material materials with Elastic modulus of 73.0 GPa | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | ||
73 GPa Show Material materials with Elastic modulus of 73 GPa | T62 | ||||
74.0 GPa Show Material materials with Elastic modulus of 74.0 GPa | T62 | ||||
Elongation | -195 °C | 16 % Show Material materials with Elongation of 16 % | T62 | Elongation in 50 mm | |
-80 °C | 13 % Show Material materials with Elongation of 13 % | T62 | Elongation in 50 mm | ||
5.0 % Show Material materials with Elongation of 5.0 % | T62 | AA Standards, ASTM B221, ASTM B241 | A100 | ||
6.0 % Show Material materials with Elongation of 6.0 % | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | A50 | ||
6.0 % Show Material materials with Elongation of 6.0 % | T62 | AA Standards, ASTM B209 | A100 | ||
7.0 % Show Material materials with Elongation of 7.0 % | T62 | AA Standards, ASTM B209 | A50 | ||
7.0 % Show Material materials with Elongation of 7.0 % | T62 | AA Standards, ASTM B209 | A100 | ||
8.0 % Show Material materials with Elongation of 8.0 % | T62 | AA Standards, ASTM B209 | A50 | ||
8.2 % Show Material materials with Elongation of 8.2 % | T62 | ||||
10.0 % Show Material materials with Elongation of 10.0 % | T62 | AA Standards | A50 | ||
0 °C | 12 % Show Material materials with Elongation of 12 % | T62 | Elongation in 50 mm | ||
24 °C | 12 % Show Material materials with Elongation of 12 % | T62 | Elongation in 50 mm | ||
100 °C | 14 % Show Material materials with Elongation of 14 % | T62 | Elongation in 50 mm | ||
150 °C | 17 % Show Material materials with Elongation of 17 % | T62 | Elongation in 50 mm | ||
205 °C | 20 % Show Material materials with Elongation of 20 % | T62 | Elongation in 50 mm | ||
260 °C | 21 % Show Material materials with Elongation of 21 % | T62 | Elongation in 50 mm | ||
315 °C | 40 % Show Material materials with Elongation of 40 % | T62 | Elongation in 50 mm | ||
370 °C | 75 % Show Material materials with Elongation of 75 % | T62 | Elongation in 50 mm | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 2000 Series Aluminium | |||
Shear modulus | 26.0 GPa Show Material materials with Shear modulus of 26.0 GPa | T62 | |||
Tensile strength | -195 °C | 503 MPa Show Material materials with Tensile strength of 503 MPa | T62 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
-80 °C | 435 MPa Show Material materials with Tensile strength of 435 MPa | T62 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
370.0 MPa Show Material materials with Tensile strength of 370.0 MPa | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | |||
415.0 MPa Show Material materials with Tensile strength of 415.0 MPa | T62 | AA Standards | |||
0 °C | 415 MPa Show Material materials with Tensile strength of 415 MPa | T62 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
420.0 MPa Show Material materials with Tensile strength of 420.0 MPa | T62 | ||||
24 °C | 400 MPa Show Material materials with Tensile strength of 400 MPa | T62 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
100 °C | 372 MPa Show Material materials with Tensile strength of 372 MPa | T62 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
150 °C | 310 MPa Show Material materials with Tensile strength of 310 MPa | T62 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
205 °C | 235 MPa Show Material materials with Tensile strength of 235 MPa | T62 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
260 °C | 185 MPa Show Material materials with Tensile strength of 185 MPa | T62 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
315 °C | 70 MPa Show Material materials with Tensile strength of 70 MPa | T62 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
370 °C | 30 MPa Show Material materials with Tensile strength of 30 MPa | T62 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
Yield strength | 250.0 MPa Show Material materials with Yield strength of 250.0 MPa | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | RP02 | |
290.0 MPa Show Material materials with Yield strength of 290.0 MPa | T62 | AA Standards | RP02 | ||
290.0 MPa Show Material materials with Yield strength of 290.0 MPa | T62 |
Thermal
| Property | Temperature | Value | Condition | Related Standards |
|---|---|---|---|---|
Coefficient of thermal expansion | 2.2e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.2e-05 1/K | T62 | ||
20 °C | 2.23e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.23e-05 1/K | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | |
100 °C | 2.23e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.23e-05 1/K | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | |
Melting point | 540.0 °C Show Material materials with Melting point of 540.0 °C | T62 | ||
545.0 - 645.0 °C Show Material materials with Melting point of 545.0 - 645.0 °C | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | ||
Specific heat capacity | 860.0 J/(kg·K) Show Material materials with Specific heat capacity of 860.0 J/(kg·K) | T62 | ||
Thermal conductivity | 113.0 - 172.0 W/(m·K) Show Material materials with Thermal conductivity of 113.0 - 172.0 W/(m·K) | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | |
140.0 W/(m·K) Show Material materials with Thermal conductivity of 140.0 W/(m·K) | T62 |
Electrical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Electrical conductivity | 16000000.0 - 26000000.0 S/m Show Material materials with Electrical conductivity of 16000000.0 - 26000000.0 S/m | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | |
17000000 S/m Show Material materials with Electrical conductivity of 17000000 S/m | T62 | Typical/derived value | ||
Electrical resistivity | 3.85e-08 - 6.25e-08 Ω·m Show Material materials with Electrical resistivity of 3.85e-08 - 6.25e-08 Ω·m | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | |
6.2e-08 Ω·m Show Material materials with Electrical resistivity of 6.2e-08 Ω·m | T62 | Typical value | ||
Specific Electrical conductivity | 30.0 % IACS Show Material materials with Specific Electrical conductivity of 30.0 % IACS | T62 | Typical value |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 91.5 - 93.8 % Show Material materials with Aluminium of 91.5 - 93.8 % | T62 | |
Copper | 5.8 - 6.8 % Show Material materials with Copper of 5.8 - 6.8 % | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
Iron | 0.30 % Show Material materials with Iron of 0.30 % | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
0.3 % Show Material materials with Iron of 0.3 % | T62 | ||
Magnesium | 0.02 % Show Material materials with Magnesium of 0.02 % | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
Manganese | 0.2 - 0.4 % Show Material materials with Manganese of 0.2 - 0.4 % | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
Other | 0.15 % Show Material materials with Other of 0.15 % | T62 | |
Silicon | 0.2 % Show Material materials with Silicon of 0.2 % | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
Titanium | 0.02 - 0.1 % Show Material materials with Titanium of 0.02 - 0.1 % | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
Vanadium | 0.05 - 0.15 % Show Material materials with Vanadium of 0.05 - 0.15 % | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
Zinc | 0.1 % Show Material materials with Zinc of 0.1 % | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
Zirconium | 0.1 - 0.25 % Show Material materials with Zirconium of 0.1 - 0.25 % | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: Betriebsschäden in Gebieten mit Zugspannungen quer zur Kornstruktur, Eingeschränkte Schäden an Laborproben (T31, T351, T3510, T3511, T37), kein Schadensfall im Betrieb, eingeschränkte Schäden bei den Labortests (T81, T851, T8510, T8511), general: sufficient, in principle it should be protected | |
| General machinability | General: good to acceptable | |
| Workability | general (condition): poor(T31, T351, T3510, T3511), not suitable (T37, T81, T851, T8510, T8511, T87) | |