AA Standards Grade 3003 H14

View suppliers (179)
Want to keep this datasheet? Save it now in your required format

Description

Aluminum AA 3003 is a popular alloy that offers customers very good atmospheric corrosion resistance and moderate strength. Aluminum 3003 offers good machinability for aluminum alloys, though it is not heat treatable. Unlike other aluminum alloys, AA 3003 is weldable by conventional welding methods. It also takes cold and hot working well and has generally better mechanical properties when compared to 1000 series aluminum alloys.

Related Standards

Equivalent Materials

This material data has been provided by AluKey,MakeItFrom.com,ASM Handbook Volume 2 Properties and Selection: Nonferrous Alloys and Special-Purpose Materials,WroughtAl_ElectricalResistivity.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionRelated Standards

Density

2.73 g/cm³

Show Material materials with Density of 2.73 g/cm³

H14

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547

2.73 g/cm³

Show Material materials with Density of 2.73 g/cm³

H14

2.8 g/cm³

Show Material materials with Density of 2.8 g/cm³

H14

Mechanical

PropertyTemperatureValueConditionRelated StandardsComment

Bending Fatigue Strength

60.0 MPa

Show Material materials with Bending Fatigue Strength of 60.0 MPa

H14

AA Standards

Elastic modulus

69.0 GPa

Show Material materials with Elastic modulus of 69.0 GPa

H14

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547

69 GPa

Show Material materials with Elastic modulus of 69 GPa

H14

Elongation

-195 °C

30 %

Show Material materials with Elongation of 30 %

H14

Elongation in 50 mm

-80 °C

18 %

Show Material materials with Elongation of 18 %

H14

Elongation in 50 mm

1.0 %

Show Material materials with Elongation of 1.0 %

H14

AA Standards, ASTM B209

A50

2.0 %

Show Material materials with Elongation of 2.0 %

H14

AA Standards, ASTM B209

A50

3.0 %

Show Material materials with Elongation of 3.0 %

H14

AA Standards, ASTM B209, ASTM B210, ASTM B234, ASTM B313

A50

3.0 %

Show Material materials with Elongation of 3.0 %

H14

AA Standards, ASTM B234

A100

4.0 %

Show Material materials with Elongation of 4.0 %

H14

AA Standards, ASTM B210

A50

4.0 %

Show Material materials with Elongation of 4.0 %

H14

AA Standards, ASTM B234

A100

5.0 %

Show Material materials with Elongation of 5.0 %

H14

AA Standards, ASTM B209, ASTM B234, ASTM B313, ASTM B547

A50

7.0 %

Show Material materials with Elongation of 7.0 %

H14

AA Standards, ASTM B209

A100

7.5 %

Show Material materials with Elongation of 7.5 %

H14

8.0 %

Show Material materials with Elongation of 8.0 %

H14

AA Standards, ASTM B209, ASTM B234, ASTM B547

A50

14.0 %

Show Material materials with Elongation of 14.0 %

H14

AA Standards

A100

0 °C

16 %

Show Material materials with Elongation of 16 %

H14

Elongation in 50 mm

24 °C

16 %

Show Material materials with Elongation of 16 %

H14

Elongation in 50 mm

100 °C

16 %

Show Material materials with Elongation of 16 %

H14

Elongation in 50 mm

150 °C

16 %

Show Material materials with Elongation of 16 %

H14

Elongation in 50 mm

205 °C

20 %

Show Material materials with Elongation of 20 %

H14

Elongation in 50 mm

260 °C

60 %

Show Material materials with Elongation of 60 %

H14

Elongation in 50 mm

315 °C

70 %

Show Material materials with Elongation of 70 %

H14

Elongation in 50 mm

370 °C

70 %

Show Material materials with Elongation of 70 %

H14

Elongation in 50 mm

Fatigue strength

62 MPa

Show Material materials with Fatigue strength of 62 MPa

H14

for 5x10⁸ cycles

Hardness, Brinell

40.0 [-]

Show Material materials with Hardness, Brinell of 40.0 [-]

H14

AA Standards

40.0 [-]

Show Material materials with Hardness, Brinell of 40.0 [-]

H14

500 kg load, 10 mm ball

Plane-Strain Fracture Toughnes

22.0 - 35.0 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m

Typical for Wrought 3000 Series Aluminium

Poisson's ratio

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-]

Typical for Wrought 3000 Series Aluminium

Shear modulus

25.0 GPa

Show Material materials with Shear modulus of 25.0 GPa

H14

Shear strength

97.0 MPa

Show Material materials with Shear strength of 97.0 MPa

H14

Tensile strength

-195 °C

240 MPa

Show Material materials with Tensile strength of 240 MPa

H14

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

-80 °C

165 MPa

Show Material materials with Tensile strength of 165 MPa

H14

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

140.0 - 180.0 MPa

Show Material materials with Tensile strength of 140.0 - 180.0 MPa

H14

AA Standards, ASTM B209, ASTM B313, ASTM B316, ASTM B547

140.0 MPa

Show Material materials with Tensile strength of 140.0 MPa

H14

AA Standards, ASTM B210, ASTM B211, ASTM B234, ASTM B483

150.0 MPa

Show Material materials with Tensile strength of 150.0 MPa

H14

AA Standards

0 °C

152 MPa

Show Material materials with Tensile strength of 152 MPa

H14

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

160.0 MPa

Show Material materials with Tensile strength of 160.0 MPa

H14

24 °C

152 MPa

Show Material materials with Tensile strength of 152 MPa

H14

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

100 °C

145 MPa

Show Material materials with Tensile strength of 145 MPa

H14

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

150 °C

125 MPa

Show Material materials with Tensile strength of 125 MPa

H14

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

205 °C

97 MPa

Show Material materials with Tensile strength of 97 MPa

H14

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

260 °C

52 MPa

Show Material materials with Tensile strength of 52 MPa

H14

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

315 °C

28 MPa

Show Material materials with Tensile strength of 28 MPa

H14

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

370 °C

19 MPa

Show Material materials with Tensile strength of 19 MPa

H14

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

Yield strength

-200 °C

170 MPa

Show Material materials with Yield strength of 170 MPa

H14

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

-100 °C

155 MPa

Show Material materials with Yield strength of 155 MPa

H14

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

-30 °C

145 MPa

Show Material materials with Yield strength of 145 MPa

H14

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

115.0 MPa

Show Material materials with Yield strength of 115.0 MPa

H14

AA Standards, ASTM B209, ASTM B210, ASTM B234, ASTM B313, ASTM B483, ASTM B547

RP02

130.0 MPa

Show Material materials with Yield strength of 130.0 MPa

H14

145.0 MPa

Show Material materials with Yield strength of 145.0 MPa

H14

AA Standards

RP02

25 °C

145 MPa

Show Material materials with Yield strength of 145 MPa

H14

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

100 °C

130 MPa

Show Material materials with Yield strength of 130 MPa

H14

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

200 °C

62 MPa

Show Material materials with Yield strength of 62 MPa

H14

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

300 °C

17 MPa

Show Material materials with Yield strength of 17 MPa

H14

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

400 °C

12 MPa

Show Material materials with Yield strength of 12 MPa

H14

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

Thermal

PropertyTemperatureValueConditionRelated Standards

Coefficient of thermal expansion

2.3e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.3e-05 1/K

H14

20 °C

2.3199999999999998e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.3199999999999998e-05 1/K

H14

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547

100 °C

2.3199999999999998e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.3199999999999998e-05 1/K

H14

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547

Melting point

640.0 - 655.0 °C

Show Material materials with Melting point of 640.0 - 655.0 °C

H14

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547

640.0 °C

Show Material materials with Melting point of 640.0 °C

H14

Specific heat capacity

890.0 J/(kg·K)

Show Material materials with Specific heat capacity of 890.0 J/(kg·K)

H14

Thermal conductivity

159.0 - 193.0 W/(m·K)

Show Material materials with Thermal conductivity of 159.0 - 193.0 W/(m·K)

H14

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547

180.0 W/(m·K)

Show Material materials with Thermal conductivity of 180.0 W/(m·K)

H14

Electrical

PropertyValueConditionRelated StandardsComment

Electrical conductivity

24000000.0 - 29000000.0 S/m

Show Material materials with Electrical conductivity of 24000000.0 - 29000000.0 S/m

H14

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547

24000000 S/m

Show Material materials with Electrical conductivity of 24000000 S/m

H14

Typical value

Electrical resistivity

3.45e-08 - 4.17e-08 Ω·m

Show Material materials with Electrical resistivity of 3.45e-08 - 4.17e-08 Ω·m

H14

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547

4.2e-08 Ω·m

Show Material materials with Electrical resistivity of 4.2e-08 Ω·m

H14

Typical value

Specific Electrical conductivity

41.0 % IACS

Show Material materials with Specific Electrical conductivity of 41.0 % IACS

H14

Typical/Derived value

Chemical properties

PropertyValueConditionRelated Standards

Aluminium

96.8 - 99.0 %

Show Material materials with Aluminium of 96.8 - 99.0 %

H14

Copper

0.05 - 0.2 %

Show Material materials with Copper of 0.05 - 0.2 %

H14

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547

Iron

0.70 %

Show Material materials with Iron of 0.70 %

H14

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547

0.7 %

Show Material materials with Iron of 0.7 %

H14

Manganese

1.0 - 1.5 %

Show Material materials with Manganese of 1.0 - 1.5 %

H14

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547

Other

0.15 %

Show Material materials with Other of 0.15 %

H14

Silicon

0.6 %

Show Material materials with Silicon of 0.6 %

H14

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547

Zinc

0.1 %

Show Material materials with Zinc of 0.1 %

H14

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547

Technological properties

Property
Brazing

general: possible with commercial processes and methods

Corrosion properties

Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere

General machinability

General: not suitable (O, H12), poor (H14, H16, H25)

Workability

general (condition): good (O, H12), acceptable (H14, H25), poor(H16, H18)