AA Standards Grade 3003 H16

Want to keep this datasheet? Save it now in your required format

Description

Related Standards

Equivalent Materials

Ashby charts

See where AA Standards Grade 3003 H16 falls on the material property chart for Density against Elastic modulus in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

Density

ρ

2.73 - 2.8 g/cm³ at 20 °C

Dimension

Dimensions

Wanddicke

Mechanical

Elastic modulus

E

69 GPa at 20 °C

Elongation

A

5.8 - 9.5 % at 20 °C

Elongation A100

A100

12 % at 20 °C

Elongation A50

A50

1 - 5 % at 20 °C

Fatigue strength

SNf

69 MPa at 20 °C

for 5x10⁸ cycles

Hardness, Brinell

HB

47 [-] at 20 °C

500 kg load, 10 mm ball

Plane-Strain Fracture Toughnes

KIC

22 - 35 MPa·√m at 20 °C

Typical for Wrought 3000 Series Aluminium

Poisson's ratio

ν

0.33 [-] at 20 °C

Typical for Wrought 3000 Series Aluminium

Shear modulus

G

25 GPa at 20 °C

Shear strength

τ

105 MPa at 20 °C

Tensile strength

Rm

165 - 205 MPa at 20 °C

Yield strength

YS

170 MPa at 20 °C

Yield strength Rp0.2

Rp0.2

145 - 170 MPa at 20 °C

Thermal

Coefficient of thermal expansion

α

2.3E-5 - 2.32E-5 1/K at 20 °C

Hide chart

Melting point

Tm

640 - 655 °C

Specific heat capacity

cp

890 J/(kg·K) at 20 °C

Thermal conductivity

λ

159 - 193 W/(m·K) at 20 °C

Electrical

Electrical conductivity

σel

2.40E+7 - 2.55E+8 S/m at 20 °C

Electrical resistivity

ρel

3.45E-8 - 4.17E-8 Ω·m at 20 °C

Chemical properties

Element

Weight %

Comment

Al

96.8 - 99 %

Mn

1 - 1.5 %

Cu

0.05 - 0.2 %

Fe

0 - 0.7 %

Other

0 - 0.15 %

each 0.05, total 0.15, Rest Al

More

Technological properties

Brazing

general: possible with commercial processes and methods

Corrosion properties

Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere

General machinability

General: not suitable (O, H12), poor (H14, H16, H25)

Workability

general (condition): good (O, H12), acceptable (H14, H25), poor(H16, H18)

This material data has been provided by MakeItFrom.com,ASM Handbook Volume 2 Properties and Selection: Nonferrous Alloys and Special-Purpose Materials,AluKey.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.