AA Standards Grade 3004 H34

View suppliers (23)
Want to keep this datasheet? Save it now in your required format

Related Standards

Equivalent Materials

This material data has been provided by AluKey,MakeItFrom.com,ASM Handbook Volume 2 Properties and Selection: Nonferrous Alloys and Special-Purpose Materials.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionRelated Standards

Density

2.72 g/cm³

Show Material materials with Density of 2.72 g/cm³

H34

AA Standards, ASTM B209, ASTM B313, ASTM B547

2.72 g/cm³

Show Material materials with Density of 2.72 g/cm³

H34

2.8 g/cm³

Show Material materials with Density of 2.8 g/cm³

H34

Mechanical

PropertyTemperatureValueConditionRelated StandardsComment

Bending Fatigue Strength

105.0 MPa

Show Material materials with Bending Fatigue Strength of 105.0 MPa

H34

AA Standards

Elastic modulus

69.0 GPa

Show Material materials with Elastic modulus of 69.0 GPa

H34

AA Standards, ASTM B209, ASTM B313, ASTM B547

69 GPa

Show Material materials with Elastic modulus of 69 GPa

H34

Elongation

-195 °C

26 %

Show Material materials with Elongation of 26 %

H34

Elongation in 50 mm

-80 °C

16 %

Show Material materials with Elongation of 16 %

H34

Elongation in 50 mm

1.0 %

Show Material materials with Elongation of 1.0 %

H34

AA Standards, ASTM B209

A50

2.0 %

Show Material materials with Elongation of 2.0 %

H34

AA Standards, ASTM B209

A50

3.0 %

Show Material materials with Elongation of 3.0 %

H34

AA Standards, ASTM B209, ASTM B313

A50

4.0 %

Show Material materials with Elongation of 4.0 %

H34

AA Standards, ASTM B209, ASTM B313, ASTM B547

A50

4.0 %

Show Material materials with Elongation of 4.0 %

H34

AA Standards, ASTM B209

A100

5.0 %

Show Material materials with Elongation of 5.0 %

H34

AA Standards, ASTM B209, ASTM B547

A50

7.1 %

Show Material materials with Elongation of 7.1 %

H34

9.0 %

Show Material materials with Elongation of 9.0 %

H34

AA Standards

A50

10.0 %

Show Material materials with Elongation of 10.0 %

H34

AA Standards

A100

0 °C

13 %

Show Material materials with Elongation of 13 %

H34

Elongation in 50 mm

24 °C

12 %

Show Material materials with Elongation of 12 %

H34

Elongation in 50 mm

100 °C

13 %

Show Material materials with Elongation of 13 %

H34

Elongation in 50 mm

150 °C

22 %

Show Material materials with Elongation of 22 %

H34

Elongation in 50 mm

205 °C

35 %

Show Material materials with Elongation of 35 %

H34

Elongation in 50 mm

260 °C

55 %

Show Material materials with Elongation of 55 %

H34

Elongation in 50 mm

315 °C

80 %

Show Material materials with Elongation of 80 %

H34

Elongation in 50 mm

370 °C

90 %

Show Material materials with Elongation of 90 %

H34

Elongation in 50 mm

Fatigue strength

15 MPa

Show Material materials with Fatigue strength of 15 MPa

H34

for 5x10⁸ cycles

Hardness, Brinell

63.0 [-]

Show Material materials with Hardness, Brinell of 63.0 [-]

H34

AA Standards

63.0 [-]

Show Material materials with Hardness, Brinell of 63.0 [-]

H34

500 kg load, 10 mm ball

Plane-Strain Fracture Toughnes

22.0 - 35.0 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m

Typical for Wrought 3000 Series Aluminium

Poisson's ratio

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-]

Typical for Wrought 3000 Series Aluminium

Shear modulus

25.0 GPa

Show Material materials with Shear modulus of 25.0 GPa

H34

Shear strength

125.0 MPa

Show Material materials with Shear strength of 125.0 MPa

H34

Tensile strength

-195 °C

360 MPa

Show Material materials with Tensile strength of 360 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

-80 °C

262 MPa

Show Material materials with Tensile strength of 262 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

220.0 - 265.0 MPa

Show Material materials with Tensile strength of 220.0 - 265.0 MPa

H34

AA Standards, ASTM B209, ASTM B313, ASTM B547

240.0 MPa

Show Material materials with Tensile strength of 240.0 MPa

H34

AA Standards

0 °C

248 MPa

Show Material materials with Tensile strength of 248 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

24 °C

240 MPa

Show Material materials with Tensile strength of 240 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

100 °C

235 MPa

Show Material materials with Tensile strength of 235 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

150 °C

193 MPa

Show Material materials with Tensile strength of 193 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

205 °C

145 MPa

Show Material materials with Tensile strength of 145 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

260 °C

97 MPa

Show Material materials with Tensile strength of 97 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

315 °C

52 MPa

Show Material materials with Tensile strength of 52 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

370 °C

35 MPa

Show Material materials with Tensile strength of 35 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

Yield strength

-200 °C

235 MPa

Show Material materials with Yield strength of 235 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

-100 °C

212 MPa

Show Material materials with Yield strength of 212 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

-30 °C

200 MPa

Show Material materials with Yield strength of 200 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

170.0 MPa

Show Material materials with Yield strength of 170.0 MPa

H34

AA Standards, ASTM B209, ASTM B313, ASTM B547

RP02

200.0 MPa

Show Material materials with Yield strength of 200.0 MPa

H34

AA Standards

RP02

200.0 MPa

Show Material materials with Yield strength of 200.0 MPa

H34

25 °C

200 MPa

Show Material materials with Yield strength of 200 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

100 °C

200 MPa

Show Material materials with Yield strength of 200 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

200 °C

105 MPa

Show Material materials with Yield strength of 105 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

300 °C

34 MPa

Show Material materials with Yield strength of 34 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

400 °C

19 MPa

Show Material materials with Yield strength of 19 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

Thermal

PropertyTemperatureValueConditionRelated Standards

Coefficient of thermal expansion

2.4e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.4e-05 1/K

H34

20 °C

2.3899999999999998e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.3899999999999998e-05 1/K

H34

AA Standards, ASTM B209, ASTM B313, ASTM B547

100 °C

2.3899999999999998e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.3899999999999998e-05 1/K

H34

AA Standards, ASTM B209, ASTM B313, ASTM B547

Melting point

630.0 - 655.0 °C

Show Material materials with Melting point of 630.0 - 655.0 °C

H34

AA Standards, ASTM B209, ASTM B313, ASTM B547

630.0 °C

Show Material materials with Melting point of 630.0 °C

H34

Specific heat capacity

890.0 J/(kg·K)

Show Material materials with Specific heat capacity of 890.0 J/(kg·K)

H34

Thermal conductivity

160.0 W/(m·K)

Show Material materials with Thermal conductivity of 160.0 W/(m·K)

H34

163 W/(m·K)

Show Material materials with Thermal conductivity of 163 W/(m·K)

H34

AA Standards, ASTM B209, ASTM B313, ASTM B547

Electrical

PropertyValueConditionRelated Standards

Electrical conductivity

24000000.0 S/m

Show Material materials with Electrical conductivity of 24000000.0 S/m

H34

AA Standards, ASTM B209, ASTM B313, ASTM B547

Electrical resistivity

4.17e-08 Ω·m

Show Material materials with Electrical resistivity of 4.17e-08 Ω·m

H34

AA Standards, ASTM B209, ASTM B313, ASTM B547

Chemical properties

PropertyValueConditionRelated Standards

Aluminium

95.6 - 98.2 %

Show Material materials with Aluminium of 95.6 - 98.2 %

H34

Copper

0.25 %

Show Material materials with Copper of 0.25 %

H34

AA Standards, ASTM B209, ASTM B313, ASTM B547

Iron

0.70 %

Show Material materials with Iron of 0.70 %

H34

AA Standards, ASTM B209, ASTM B313, ASTM B547

0.7 %

Show Material materials with Iron of 0.7 %

H34

Magnesium

0.8 - 1.3 %

Show Material materials with Magnesium of 0.8 - 1.3 %

H34

AA Standards, ASTM B209, ASTM B313, ASTM B547

Manganese

1.0 - 1.5 %

Show Material materials with Manganese of 1.0 - 1.5 %

H34

AA Standards, ASTM B209, ASTM B313, ASTM B547

Other

0.15 %

Show Material materials with Other of 0.15 %

H34

Silicon

0.3 %

Show Material materials with Silicon of 0.3 %

H34

AA Standards, ASTM B209, ASTM B313, ASTM B547

Zinc

0.25 %

Show Material materials with Zinc of 0.25 %

H34

AA Standards, ASTM B209, ASTM B313, ASTM B547

Technological properties

Property
Brazing

general: Lötbar mit speziellen Techniken oder bei bestimmten Anwendungen

Corrosion properties

Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere

General machinability

General: poor (O, H32), sufficient (H34, H36, H38)

Workability

general (condition): good (O), acceptable (H32, H34), poor(H36, H38)