Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.72 g/cm³ Show Material materials with Density of 2.72 g/cm³ | H38 | AA Standards, ASTM B209, ASTM B313 |
2.72 g/cm³ Show Material materials with Density of 2.72 g/cm³ | H38 | ||
2.8 g/cm³ Show Material materials with Density of 2.8 g/cm³ | H38 |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Bending Fatigue Strength | 110.0 MPa Show Material materials with Bending Fatigue Strength of 110.0 MPa | H38 | AA Standards | ||
Elastic modulus | 69.0 GPa Show Material materials with Elastic modulus of 69.0 GPa | H38 | AA Standards, ASTM B209, ASTM B313 | ||
69 GPa Show Material materials with Elastic modulus of 69 GPa | H38 | ||||
Elongation | -195 °C | 20 % Show Material materials with Elongation of 20 % | H38 | Elongation in 50 mm | |
-80 °C | 10 % Show Material materials with Elongation of 10 % | H38 | Elongation in 50 mm | ||
1.0 % Show Material materials with Elongation of 1.0 % | H38 | AA Standards, ASTM B209 | A50 | ||
2.0 % Show Material materials with Elongation of 2.0 % | H38 | AA Standards, ASTM B209, ASTM B313 | A50 | ||
3.8 % Show Material materials with Elongation of 3.8 % | H38 | ||||
4.0 % Show Material materials with Elongation of 4.0 % | H38 | AA Standards, ASTM B209, ASTM B313 | A50 | ||
5.0 % Show Material materials with Elongation of 5.0 % | H38 | AA Standards | A50 | ||
5.0 % Show Material materials with Elongation of 5.0 % | H38 | AA Standards | A100 | ||
0 °C | 7 % Show Material materials with Elongation of 7 % | H38 | Elongation in 50 mm | ||
24 °C | 6 % Show Material materials with Elongation of 6 % | H38 | Elongation in 50 mm | ||
100 °C | 7 % Show Material materials with Elongation of 7 % | H38 | Elongation in 50 mm | ||
150 °C | 15 % Show Material materials with Elongation of 15 % | H38 | Elongation in 50 mm | ||
205 °C | 30 % Show Material materials with Elongation of 30 % | H38 | Elongation in 50 mm | ||
260 °C | 50 % Show Material materials with Elongation of 50 % | H38 | Elongation in 50 mm | ||
315 °C | 80 % Show Material materials with Elongation of 80 % | H38 | Elongation in 50 mm | ||
370 °C | 90 % Show Material materials with Elongation of 90 % | H38 | Elongation in 50 mm | ||
Fatigue strength | 16 MPa Show Material materials with Fatigue strength of 16 MPa | H38 | for 5x10⁸ cycles | ||
Hardness, Brinell | 77.0 [-] Show Material materials with Hardness, Brinell of 77.0 [-] | H38 | AA Standards | ||
77.0 [-] Show Material materials with Hardness, Brinell of 77.0 [-] | H38 | 500 kg load, 10 mm ball | |||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 3000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 3000 Series Aluminium | |||
Shear modulus | 25.0 GPa Show Material materials with Shear modulus of 25.0 GPa | H38 | |||
Shear strength | 145.0 MPa Show Material materials with Shear strength of 145.0 MPa | H38 | |||
Tensile strength | -195 °C | 400 MPa Show Material materials with Tensile strength of 400 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
-80 °C | 303 MPa Show Material materials with Tensile strength of 303 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
260.0 MPa Show Material materials with Tensile strength of 260.0 MPa | H38 | AA Standards, ASTM B209, ASTM B313 | |||
285.0 MPa Show Material materials with Tensile strength of 285.0 MPa | H38 | AA Standards | |||
290.0 MPa Show Material materials with Tensile strength of 290.0 MPa | H38 | ||||
0 °C | 290 MPa Show Material materials with Tensile strength of 290 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
24 °C | 283 MPa Show Material materials with Tensile strength of 283 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
100 °C | 275 MPa Show Material materials with Tensile strength of 275 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
150 °C | 215 MPa Show Material materials with Tensile strength of 215 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
205 °C | 152 MPa Show Material materials with Tensile strength of 152 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
260 °C | 83 MPa Show Material materials with Tensile strength of 83 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
315 °C | 52 MPa Show Material materials with Tensile strength of 52 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
370 °C | 35 MPa Show Material materials with Tensile strength of 35 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
Yield strength | -200 °C | 295 MPa Show Material materials with Yield strength of 295 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
-100 °C | 267 MPa Show Material materials with Yield strength of 267 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
-30 °C | 245 MPa Show Material materials with Yield strength of 245 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
215.0 MPa Show Material materials with Yield strength of 215.0 MPa | H38 | AA Standards, ASTM B209, ASTM B313 | RP02 | ||
250.0 MPa Show Material materials with Yield strength of 250.0 MPa | H38 | AA Standards | RP02 | ||
250.0 MPa Show Material materials with Yield strength of 250.0 MPa | H38 | ||||
25 °C | 245 MPa Show Material materials with Yield strength of 245 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
100 °C | 245 MPa Show Material materials with Yield strength of 245 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
200 °C | 105 MPa Show Material materials with Yield strength of 105 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
300 °C | 34 MPa Show Material materials with Yield strength of 34 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
400 °C | 19 MPa Show Material materials with Yield strength of 19 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
Thermal
| Property | Temperature | Value | Condition | Related Standards |
|---|---|---|---|---|
Coefficient of thermal expansion | 2.4e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.4e-05 1/K | H38 | ||
20 °C | 2.3899999999999998e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3899999999999998e-05 1/K | H38 | AA Standards, ASTM B209, ASTM B313 | |
100 °C | 2.3899999999999998e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3899999999999998e-05 1/K | H38 | AA Standards, ASTM B209, ASTM B313 | |
Melting point | 630.0 - 655.0 °C Show Material materials with Melting point of 630.0 - 655.0 °C | H38 | AA Standards, ASTM B209, ASTM B313 | |
630.0 °C Show Material materials with Melting point of 630.0 °C | H38 | |||
Specific heat capacity | 890.0 J/(kg·K) Show Material materials with Specific heat capacity of 890.0 J/(kg·K) | H38 | ||
Thermal conductivity | 160.0 W/(m·K) Show Material materials with Thermal conductivity of 160.0 W/(m·K) | H38 | ||
163 W/(m·K) Show Material materials with Thermal conductivity of 163 W/(m·K) | H38 | AA Standards, ASTM B209, ASTM B313 | ||
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 24000000.0 S/m Show Material materials with Electrical conductivity of 24000000.0 S/m | H38 | AA Standards, ASTM B209, ASTM B313 |
Electrical resistivity | 4.17e-08 Ω·m Show Material materials with Electrical resistivity of 4.17e-08 Ω·m | H38 | AA Standards, ASTM B209, ASTM B313 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 95.6 - 98.2 % Show Material materials with Aluminium of 95.6 - 98.2 % | H38 | |
Copper | 0.25 % Show Material materials with Copper of 0.25 % | H38 | AA Standards, ASTM B209, ASTM B313 |
Iron | 0.70 % Show Material materials with Iron of 0.70 % | H38 | AA Standards, ASTM B209, ASTM B313 |
0.7 % Show Material materials with Iron of 0.7 % | H38 | ||
Magnesium | 0.8 - 1.3 % Show Material materials with Magnesium of 0.8 - 1.3 % | H38 | AA Standards, ASTM B209, ASTM B313 |
Manganese | 1.0 - 1.5 % Show Material materials with Manganese of 1.0 - 1.5 % | H38 | AA Standards, ASTM B209, ASTM B313 |
Other | 0.15 % Show Material materials with Other of 0.15 % | H38 | |
Silicon | 0.3 % Show Material materials with Silicon of 0.3 % | H38 | AA Standards, ASTM B209, ASTM B313 |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | H38 | AA Standards, ASTM B209, ASTM B313 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: Lötbar mit speziellen Techniken oder bei bestimmten Anwendungen | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (O, H32), sufficient (H34, H36, H38) | |
| Workability | general (condition): good (O), acceptable (H32, H34), poor(H36, H38) | |