Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.72 g/cm³ Show Material materials with Density of 2.72 g/cm³ | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
2.72 g/cm³ Show Material materials with Density of 2.72 g/cm³ | O | ||
2.8 g/cm³ Show Material materials with Density of 2.8 g/cm³ | O |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Bending Fatigue Strength | 95.0 MPa Show Material materials with Bending Fatigue Strength of 95.0 MPa | O | AA Standards | ||
Elastic modulus | 69.0 GPa Show Material materials with Elastic modulus of 69.0 GPa | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 | ||
69 GPa Show Material materials with Elastic modulus of 69 GPa | O | ||||
Elongation | -195 °C | 38 % Show Material materials with Elongation of 38 % | O | Elongation in 50 mm | |
-80 °C | 30 % Show Material materials with Elongation of 30 % | O | Elongation in 50 mm | ||
9.0 % Show Material materials with Elongation of 9.0 % | O | AA Standards, ASTM B209 | A50 | ||
12.0 % Show Material materials with Elongation of 12.0 % | O | AA Standards, ASTM B209 | A50 | ||
14.0 % Show Material materials with Elongation of 14.0 % | O | AA Standards, ASTM B209 | A100 | ||
15.0 % Show Material materials with Elongation of 15.0 % | O | AA Standards, ASTM B209, ASTM B313 | A50 | ||
16.0 % Show Material materials with Elongation of 16.0 % | O | AA Standards, ASTM B209, ASTM B547 | A50 | ||
18.0 % Show Material materials with Elongation of 18.0 % | O | AA Standards, ASTM B209, ASTM B313, ASTM B547 | A50 | ||
18.0 % Show Material materials with Elongation of 18.0 % | O | ||||
20.0 % Show Material materials with Elongation of 20.0 % | O | AA Standards | A50 | ||
22.0 % Show Material materials with Elongation of 22.0 % | O | AA Standards | A100 | ||
0 °C | 26 % Show Material materials with Elongation of 26 % | O | Elongation in 50 mm | ||
24 °C | 25 % Show Material materials with Elongation of 25 % | O | Elongation in 50 mm | ||
100 °C | 25 % Show Material materials with Elongation of 25 % | O | Elongation in 50 mm | ||
150 °C | 35 % Show Material materials with Elongation of 35 % | O | Elongation in 50 mm | ||
205 °C | 55 % Show Material materials with Elongation of 55 % | O | Elongation in 50 mm | ||
260 °C | 70 % Show Material materials with Elongation of 70 % | O | Elongation in 50 mm | ||
315 °C | 80 % Show Material materials with Elongation of 80 % | O | Elongation in 50 mm | ||
370 °C | 90 % Show Material materials with Elongation of 90 % | O | Elongation in 50 mm | ||
Fatigue strength | 14 MPa Show Material materials with Fatigue strength of 14 MPa | O | for 5x10⁸ cycles | ||
Hardness, Brinell | 45.0 [-] Show Material materials with Hardness, Brinell of 45.0 [-] | O | AA Standards | ||
45.0 [-] Show Material materials with Hardness, Brinell of 45.0 [-] | O | 500 kg load, 10 mm ball | |||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 3000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 3000 Series Aluminium | |||
Shear modulus | 25.0 GPa Show Material materials with Shear modulus of 25.0 GPa | O | |||
Shear strength | 110.0 MPa Show Material materials with Shear strength of 110.0 MPa | O | |||
Tensile strength | -195 °C | 290 MPa Show Material materials with Tensile strength of 290 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
-80 °C | 193 MPa Show Material materials with Tensile strength of 193 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
150.0 - 200.0 MPa Show Material materials with Tensile strength of 150.0 - 200.0 MPa | O | AA Standards, ASTM B209, ASTM B313, ASTM B547 | |||
160.0 - 200.0 MPa Show Material materials with Tensile strength of 160.0 - 200.0 MPa | O | AA Standards, ASTM B221 | |||
170.0 MPa Show Material materials with Tensile strength of 170.0 MPa | O | ||||
180.0 MPa Show Material materials with Tensile strength of 180.0 MPa | O | AA Standards | |||
0 °C | 180 MPa Show Material materials with Tensile strength of 180 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
24 °C | 180 MPa Show Material materials with Tensile strength of 180 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
100 °C | 180 MPa Show Material materials with Tensile strength of 180 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
150 °C | 152 MPa Show Material materials with Tensile strength of 152 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
205 °C | 97 MPa Show Material materials with Tensile strength of 97 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
260 °C | 70 MPa Show Material materials with Tensile strength of 70 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
315 °C | 52 MPa Show Material materials with Tensile strength of 52 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
370 °C | 35 MPa Show Material materials with Tensile strength of 35 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
Yield strength | -200 °C | 90 MPa Show Material materials with Yield strength of 90 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
-100 °C | 80 MPa Show Material materials with Yield strength of 80 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
-30 °C | 69 MPa Show Material materials with Yield strength of 69 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
60.0 MPa Show Material materials with Yield strength of 60.0 MPa | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 | RP02 | ||
69.0 MPa Show Material materials with Yield strength of 69.0 MPa | O | ||||
70.0 MPa Show Material materials with Yield strength of 70.0 MPa | O | AA Standards | RP02 | ||
25 °C | 69 MPa Show Material materials with Yield strength of 69 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
100 °C | 69 MPa Show Material materials with Yield strength of 69 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
200 °C | 65 MPa Show Material materials with Yield strength of 65 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
300 °C | 34 MPa Show Material materials with Yield strength of 34 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
400 °C | 9 MPa Show Material materials with Yield strength of 9 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 |
Thermal
| Property | Temperature | Value | Condition | Related Standards |
|---|---|---|---|---|
Coefficient of thermal expansion | 2.4e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.4e-05 1/K | O | ||
20 °C | 2.3899999999999998e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3899999999999998e-05 1/K | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 | |
100 °C | 2.3899999999999998e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3899999999999998e-05 1/K | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 | |
Melting point | 630.0 - 655.0 °C Show Material materials with Melting point of 630.0 - 655.0 °C | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 | |
630.0 °C Show Material materials with Melting point of 630.0 °C | O | |||
Specific heat capacity | 890.0 J/(kg·K) Show Material materials with Specific heat capacity of 890.0 J/(kg·K) | O | ||
Thermal conductivity | 160.0 W/(m·K) Show Material materials with Thermal conductivity of 160.0 W/(m·K) | O | ||
163 W/(m·K) Show Material materials with Thermal conductivity of 163 W/(m·K) | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
Electrical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Electrical conductivity | 24000000.0 S/m Show Material materials with Electrical conductivity of 24000000.0 S/m | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 | |
24000000 S/m Show Material materials with Electrical conductivity of 24000000 S/m | O | Typical/derived value | ||
Electrical resistivity | 4.17e-08 Ω·m Show Material materials with Electrical resistivity of 4.17e-08 Ω·m | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 | |
Specific Electrical conductivity | 42.0 % IACS Show Material materials with Specific Electrical conductivity of 42.0 % IACS | O | Typical value |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 95.6 - 98.2 % Show Material materials with Aluminium of 95.6 - 98.2 % | O | |
Copper | 0.25 % Show Material materials with Copper of 0.25 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
Iron | 0.70 % Show Material materials with Iron of 0.70 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
0.7 % Show Material materials with Iron of 0.7 % | O | ||
Magnesium | 0.8 - 1.3 % Show Material materials with Magnesium of 0.8 - 1.3 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
Manganese | 1.0 - 1.5 % Show Material materials with Manganese of 1.0 - 1.5 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
Other | 0.15 % Show Material materials with Other of 0.15 % | O | |
Silicon | 0.3 % Show Material materials with Silicon of 0.3 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: Lötbar mit speziellen Techniken oder bei bestimmten Anwendungen | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (O, H32), sufficient (H34, H36, H38) | |
| Workability | general (condition): good (O), acceptable (H32, H34), poor(H36, H38) | |