General
Property | Value | Condition | Related Standards | Shape |
---|---|---|---|---|
Density | 2.73 g/cm³ Show Material materials with Density of 2.73 g/cm³ | H14 | BS EN 573-3, BS EN 485-2 | Sheet |
2.8 g/cm³ Show Material materials with Density of 2.8 g/cm³ | H14 |
Mechanical
Property | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|
Elastic modulus | 69.5 GPa Show Material materials with Elastic modulus of 69.5 GPa | H14 | BS EN 573-3, BS EN 485-2 | Sheet | |
72.0 GPa Show Material materials with Elastic modulus of 72.0 GPa | H14 | ||||
Elongation | 4.6 % Show Material materials with Elongation of 4.6 % | H14 | |||
Hardness, Brinell | 45.0 [-] Show Material materials with Hardness, Brinell of 45.0 [-] | H14 | BS EN 573-3, BS EN 485-2 | Sheet | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 3000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 3000 Series Aluminium | |||
Shear modulus | 25.0 - 26.0 GPa Show Material materials with Shear modulus of 25.0 - 26.0 GPa | Typical for Wrought 3000 Series Aluminium | |||
Tensile strength | 140.0 - 180.0 MPa Show Material materials with Tensile strength of 140.0 - 180.0 MPa | H14 | BS EN 573-3, BS EN 485-2 | Sheet | |
150.0 MPa Show Material materials with Tensile strength of 150.0 MPa | H14 | ||||
Yield strength | 130.0 MPa Show Material materials with Yield strength of 130.0 MPa | H14 |
Thermal
Property | Value | Condition | Related Standards | Shape |
---|---|---|---|---|
Coefficient of thermal expansion | 2.3e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3e-05 1/K | H14 | ||
2.31e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.31e-05 1/K | H14 | BS EN 573-3, BS EN 485-2 | Sheet | |
Melting point | 640.0 °C Show Material materials with Melting point of 640.0 °C | H14 | ||
655.0 °C Show Material materials with Melting point of 655.0 °C | H14 | BS EN 573-3, BS EN 485-2 | Sheet | |
Specific heat capacity | 890.0 J/(kg·K) Show Material materials with Specific heat capacity of 890.0 J/(kg·K) | H14 | ||
Thermal conductivity | 160.0 W/(m·K) Show Material materials with Thermal conductivity of 160.0 W/(m·K) | H14 | BS EN 573-3, BS EN 485-2 | Sheet |
Electrical
Property | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|
Electrical conductivity | 23000000.0 - 29000000.0 S/m Show Material materials with Electrical conductivity of 23000000.0 - 29000000.0 S/m | Typical for Wrought 3000 Series Aluminium | |||
Electrical resistivity | 4.11e-08 Ω·m Show Material materials with Electrical resistivity of 4.11e-08 Ω·m | H14 | BS EN 573-3, BS EN 485-2 | Sheet |
Chemical properties
Property | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|
Aluminium | 96.3 - 99.1 % Show Material materials with Aluminium of 96.3 - 99.1 % | H14 | |||
Chromium | 0.1 % Show Material materials with Chromium of 0.1 % | H14 | BS EN 573-3, BS EN 485-2 | Sheet | |
Copper | 0.1 % Show Material materials with Copper of 0.1 % | H14 | BS EN 573-3, BS EN 485-2 | Sheet | |
Iron | 0.7 % Show Material materials with Iron of 0.7 % | H14 | |||
Magnesium | 0.3 % Show Material materials with Magnesium of 0.3 % | H14 | BS EN 573-3, BS EN 485-2 | Sheet | |
Manganese | 0.9 - 1.5 % Show Material materials with Manganese of 0.9 - 1.5 % | H14 | BS EN 573-3, BS EN 485-2 | Sheet | |
Other | 0.15 % Show Material materials with Other of 0.15 % | H14 | BS EN 573-3, BS EN 485-2 | Sheet | Total |
Silicon | 0.5 % Show Material materials with Silicon of 0.5 % | H14 | BS EN 573-3, BS EN 485-2 | Sheet | |
Titanium | 0.1 % Show Material materials with Titanium of 0.1 % | H14 | BS EN 573-3, BS EN 485-2 | Sheet | Ti + Zr |
Zinc | 0.2 % Show Material materials with Zinc of 0.2 % | H14 | BS EN 573-3, BS EN 485-2 | Sheet | |
Zirconium | 0.1 % Show Material materials with Zirconium of 0.1 % | H14 |
Technological properties
Property | ||
---|---|---|
Brazing | Very Good | |
General machinability | Acceptable | |
Soldering general | Very Good | |
Welding | Gas: Very Good; Arc: Very Good; Resistance: Good | |
Workability | Cold: Good |