AA Standards Grade 5005 H16

Want to keep this datasheet? Save it now in your required format

Description

Aluminum AA 5005 is a lean aluminum magnesium alloy with low density and excellent thermal conductivity. This medium strength non-heat-treatable alloy is known for its corrosion resistance in alkaline marine situations. Aluminum AA 5005 is readily machinable, and can be welded using TIG and MIG methods. It is important to note that anodizing is a critical part to how Aluminum AA 5005 is used.

Related Standards

Equivalent Materials

This material data has been provided by AluKey,MakeItFrom.com,ASM Handbook Volume 2 Properties and Selection: Nonferrous Alloys and Special-Purpose Materials.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Applications

Fluid Systems

Fluid Storage

Fluid Storage General

Consumer Goods

Domestic Electrical Appliances

Furniture

Properties

General

Property	Value	Condition	Related Standards
Density	2.7 g/cm³ Show Material materials with Density of 2.7 g/cm³	H16	AA Standards, ASTM B209
	2.7 g/cm³ Show Material materials with Density of 2.7 g/cm³	H16

Mechanical

Property	Value	Condition	Related Standards	Comment
Elastic modulus	69.0 GPa Show Material materials with Elastic modulus of 69.0 GPa	H16	AA Standards, ASTM B209
	69 GPa Show Material materials with Elastic modulus of 69 GPa	H16
Elongation	1.0 % Show Material materials with Elongation of 1.0 %	H16	AA Standards, ASTM B209	A50
	2.0 % Show Material materials with Elongation of 2.0 %	H16	AA Standards, ASTM B209	A50
	3.0 % Show Material materials with Elongation of 3.0 %	H16	AA Standards, ASTM B209	A50
	3.4 % Show Material materials with Elongation of 3.4 %	H16
	5.0 % Show Material materials with Elongation of 5.0 %	H16	AA Standards	A50
	5 % Show Material materials with Elongation of 5 %	H16
Plane-Strain Fracture Toughnes	22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m			Typical for Wrought 5000 Series Aluminium
Poisson's ratio	0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-]			Typical for Wrought 5000 Series Aluminium
Shear modulus	25.9 GPa Show Material materials with Shear modulus of 25.9 GPa	H16
Shear strength	103.0 MPa Show Material materials with Shear strength of 103.0 MPa	H16
Tensile strength	165.0 - 205.0 MPa Show Material materials with Tensile strength of 165.0 - 205.0 MPa	H16	AA Standards, ASTM B209
	180.0 MPa Show Material materials with Tensile strength of 180.0 MPa	H16	AA Standards
	180 MPa Show Material materials with Tensile strength of 180 MPa	H16
Yield strength	135.0 MPa Show Material materials with Yield strength of 135.0 MPa	H16	AA Standards, ASTM B209	RP02
	170.0 MPa Show Material materials with Yield strength of 170.0 MPa	H16	AA Standards	RP02
	170 MPa Show Material materials with Yield strength of 170 MPa	H16		RP02
	170.0 MPa Show Material materials with Yield strength of 170.0 MPa	H16

Thermal

Property	Temperature	Value	Condition	Related Standards	Comment
Coefficient of thermal expansion		2.4e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.4e-05 1/K	H16
	20 °C	2.38e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.38e-05 1/K	H16	AA Standards, ASTM B209
	100 °C	2.38e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.38e-05 1/K	H16	AA Standards, ASTM B209

Max service temperature		150.0 °C Show Material materials with Max service temperature of 150.0 °C			Typical for Wrought 5000 Series Aluminium
Melting point		630.0 - 655.0 °C Show Material materials with Melting point of 630.0 - 655.0 °C	H16	AA Standards, ASTM B209
		630.0 °C Show Material materials with Melting point of 630.0 °C	H16
Specific heat capacity		900.0 J/(kg·K) Show Material materials with Specific heat capacity of 900.0 J/(kg·K)	H16
Thermal conductivity		200.0 W/(m·K) Show Material materials with Thermal conductivity of 200.0 W/(m·K)	H16
		201 W/(m·K) Show Material materials with Thermal conductivity of 201 W/(m·K)	H16	AA Standards, ASTM B209

Electrical

Property	Value	Condition	Related Standards
Electrical conductivity	30000000.0 S/m Show Material materials with Electrical conductivity of 30000000.0 S/m	H16	AA Standards, ASTM B209
Electrical resistivity	3.33e-08 Ω·m Show Material materials with Electrical resistivity of 3.33e-08 Ω·m	H16	AA Standards, ASTM B209

Chemical properties

Property	Value	Condition	Related Standards
Aluminium	97.0 - 99.5 % Show Material materials with Aluminium of 97.0 - 99.5 %	H16
Chromium	0.1 % Show Material materials with Chromium of 0.1 %	H16	AA Standards, ASTM B209
Copper	0.2 % Show Material materials with Copper of 0.2 %	H16	AA Standards, ASTM B209
Iron	0.70 % Show Material materials with Iron of 0.70 %	H16	AA Standards, ASTM B209
	0.7 % Show Material materials with Iron of 0.7 %	H16
Magnesium	0.5 - 1.1 % Show Material materials with Magnesium of 0.5 - 1.1 %	H16	AA Standards, ASTM B209
Manganese	0.2 % Show Material materials with Manganese of 0.2 %	H16	AA Standards, ASTM B209
Other	0.15 % Show Material materials with Other of 0.15 %	H16
Silicon	0.3 % Show Material materials with Silicon of 0.3 %	H16	AA Standards, ASTM B209
Zinc	0.25 % Show Material materials with Zinc of 0.25 %	H16	AA Standards, ASTM B209

Technological properties

Property
Brazing	general: Lötbar mit speziellen Techniken oder bei bestimmten Anwendungen
Corrosion properties	Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere
General machinability	General: not suitable (O, H12, H32), poor (H14, H34, H16, H18, H36, H38)
Workability	general (condition): good (O, H12, H32), acceptable (H14, H34), poor(H16, H18, H36, H38)