Property | Value | Condition | Related Standards | Comment |
---|---|---|---|---|
Elastic modulus | 69.0 GPa Show Material materials with Elastic modulus of 69.0 GPa | H18 | AA Standards, ASTM B209 | |
69 GPa Show Material materials with Elastic modulus of 69 GPa | H18 | |||
Elongation | 1.0 % Show Material materials with Elongation of 1.0 % | H18 | AA Standards, ASTM B209 | A50 |
2.0 % Show Material materials with Elongation of 2.0 % | H18 | AA Standards, ASTM B209 | A50 | |
3.0 % Show Material materials with Elongation of 3.0 % | H18 | AA Standards, ASTM B209 | A50 | |
3.0 % Show Material materials with Elongation of 3.0 % | H18 | |||
4.0 % Show Material materials with Elongation of 4.0 % | H18 | AA Standards | A50 | |
4 % Show Material materials with Elongation of 4 % | H18 | |||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||
Shear modulus | 25.9 GPa Show Material materials with Shear modulus of 25.9 GPa | H18 | ||
Shear strength | 110.0 MPa Show Material materials with Shear strength of 110.0 MPa | H18 | ||
Tensile strength | 185.0 MPa Show Material materials with Tensile strength of 185.0 MPa | H18 | AA Standards, ASTM B209 | |
200.0 MPa Show Material materials with Tensile strength of 200.0 MPa | H18 | AA Standards | ||
200 MPa Show Material materials with Tensile strength of 200 MPa | H18 | |||
210.0 MPa Show Material materials with Tensile strength of 210.0 MPa | H18 | |||
Yield strength | 190.0 MPa Show Material materials with Yield strength of 190.0 MPa | H18 | ||
195.0 MPa Show Material materials with Yield strength of 195.0 MPa | H18 | AA Standards | RP02 | |
195 MPa Show Material materials with Yield strength of 195 MPa | H18 | RP02 |
Thermal
Property | Temperature | Value | Condition | Related Standards | Comment |
---|---|---|---|---|---|
Coefficient of thermal expansion | 2.4e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.4e-05 1/K | H18 | |||
20 °C | 2.38e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.38e-05 1/K | H18 | AA Standards, ASTM B209 | ||
100 °C | 2.38e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.38e-05 1/K | H18 | AA Standards, ASTM B209 | ||
Max service temperature | 150.0 °C Show Material materials with Max service temperature of 150.0 °C | Typical for Wrought 5000 Series Aluminium | |||
Melting point | 630.0 - 655.0 °C Show Material materials with Melting point of 630.0 - 655.0 °C | H18 | AA Standards, ASTM B209 | ||
630.0 °C Show Material materials with Melting point of 630.0 °C | H18 | ||||
Specific heat capacity | 900.0 J/(kg·K) Show Material materials with Specific heat capacity of 900.0 J/(kg·K) | H18 | |||
Thermal conductivity | 200.0 W/(m·K) Show Material materials with Thermal conductivity of 200.0 W/(m·K) | H18 | |||
201 W/(m·K) Show Material materials with Thermal conductivity of 201 W/(m·K) | H18 | AA Standards, ASTM B209 |
Electrical
Property | Value | Condition | Related Standards |
---|---|---|---|
Electrical conductivity | 30000000.0 S/m Show Material materials with Electrical conductivity of 30000000.0 S/m | H18 | AA Standards, ASTM B209 |
Electrical resistivity | 3.33e-08 Ω·m Show Material materials with Electrical resistivity of 3.33e-08 Ω·m | H18 | AA Standards, ASTM B209 |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Aluminium | 97.0 - 99.5 % Show Material materials with Aluminium of 97.0 - 99.5 % | H18 | |
Chromium | 0.1 % Show Material materials with Chromium of 0.1 % | H18 | AA Standards, ASTM B209 |
Copper | 0.2 % Show Material materials with Copper of 0.2 % | H18 | AA Standards, ASTM B209 |
Iron | 0.70 % Show Material materials with Iron of 0.70 % | H18 | AA Standards, ASTM B209 |
0.7 % Show Material materials with Iron of 0.7 % | H18 | ||
Magnesium | 0.5 - 1.1 % Show Material materials with Magnesium of 0.5 - 1.1 % | H18 | AA Standards, ASTM B209 |
Manganese | 0.2 % Show Material materials with Manganese of 0.2 % | H18 | AA Standards, ASTM B209 |
Other | 0.15 % Show Material materials with Other of 0.15 % | H18 | |
Silicon | 0.3 % Show Material materials with Silicon of 0.3 % | H18 | AA Standards, ASTM B209 |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | H18 | AA Standards, ASTM B209 |
Technological properties
Property | ||
---|---|---|
Brazing | general: Lötbar mit speziellen Techniken oder bei bestimmten Anwendungen | |
Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
General machinability | General: not suitable (O, H12, H32), poor (H14, H34, H16, H18, H36, H38) | |
Workability | general (condition): good (O, H12, H32), acceptable (H14, H34), poor(H16, H18, H36, H38) |