AA Standards Grade 5050 H32

Want to keep this datasheet? Save it now in your required format

Description

Related Standards

Equivalent Materials

Ashby charts

See where AA Standards Grade 5050 H32 falls on the material property chart for Density against Elastic modulus in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

Density

ρ

2.69 - 2.7 g/cm³ at 20 °C

Dimension

Dimensions

Dicke

Mechanical

Elastic modulus

E

69 GPa at 20 °C

Show 5000 Series materials with Elastic modulus of 69 GPa at 20 °C

Elongation

A

6.8 - 9 % at 20 °C

Show 5000 Series materials with Elongation of 6.8 - 9 % at 20 °C

Elongation A50

A50

4 - 9 % at 20 °C

Show 5000 Series materials with Elongation A50 of 4 - 9 % at 20 °C

Fatigue strength

SNf

90 MPa at 20 °C

Show 5000 Series materials with Fatigue strength of 90 MPa at 20 °C

for 5x10⁸ cycles

Hardness, Brinell

HB

46 [-] at 20 °C

Show 5000 Series materials with Hardness, Brinell of 46 [-] at 20 °C

500 kg load, 10 mm ball

Plane-Strain Fracture Toughnes

KIC

22 - 35 MPa·√m at 20 °C

Show 5000 Series materials with Plane-Strain Fracture Toughnes of 22 - 35 MPa·√m at 20 °C

Typical for Wrought 5000 Series Aluminium

Poisson's ratio

ν

0.33 [-] at 20 °C

Show 5000 Series materials with Poisson's ratio of 0.33 [-] at 20 °C

Typical for Wrought 5000 Series Aluminium

Shear modulus

G

25.9 GPa at 20 °C

Show 5000 Series materials with Shear modulus of 25.9 GPa at 20 °C

Shear strength

τ

115 MPa at 20 °C

Show 5000 Series materials with Shear strength of 115 MPa at 20 °C

Tensile strength

Rm

150 - 195 MPa at 20 °C

Show 5000 Series materials with Tensile strength of 150 - 195 MPa at 20 °C

Yield strength

YS

130 MPa at 20 °C

Show 5000 Series materials with Yield strength of 130 MPa at 20 °C

Yield strength Rp0.2

Rp0.2

110 - 145 MPa at 20 °C

Show 5000 Series materials with Yield strength Rp0.2 of 110 - 145 MPa at 20 °C

Thermal

Coefficient of thermal expansion

α

2.38E-5 - 2.4E-5 1/K at 20 °C

Hide chart

Max service temperature

Tmax

150 °C

Typical for Wrought 5000 Series Aluminium

Melting point

Tm

625 - 650 °C

Specific heat capacity

cp

900 J/(kg·K) at 20 °C

Thermal conductivity

λ

190 - 193 W/(m·K) at 20 °C

Electrical

Electrical conductivity

σel

2.90E+7 - 2.90E+8 S/m at 20 °C

Electrical resistivity

ρel

3.45E-8 Ω·m at 20 °C

Chemical properties

Element

Weight %

Comment

Al

96.3 - 98.9 %

Mg

1.1 - 1.8 %

Cr

0 - 0.1 %

Cu

0 - 0.2 %

Fe

0 - 0.7 %

More

Technological properties

Brazing

general: Lötbar mit speziellen Techniken oder bei bestimmten Anwendungen

Corrosion properties

Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere

General machinability

General: not suitable (O), poor (H32, H34), sufficient (H36, H38)

Workability

general (condition): good (O, H32), acceptable (H34), poor(H36, H38)

This material data has been provided by MakeItFrom.com,ASM Handbook Volume 2 Properties and Selection: Nonferrous Alloys and Special-Purpose Materials,AluKey.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.