AA Standards Grade 5050 H34

Want to keep this datasheet? Save it now in your required format

Related Standards

Equivalent Materials

This material data has been provided by AluKey,MakeItFrom.com,ASM Handbook Volume 2 Properties and Selection: Nonferrous Alloys and Special-Purpose Materials.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionRelated Standards

Density

2.69 g/cm³

Show Material materials with Density of 2.69 g/cm³

H34

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547

2.69 g/cm³

Show Material materials with Density of 2.69 g/cm³

H34

2.7 g/cm³

Show Material materials with Density of 2.7 g/cm³

H34

Mechanical

PropertyTemperatureValueConditionRelated StandardsComment

Bending Fatigue Strength

90.0 MPa

Show Material materials with Bending Fatigue Strength of 90.0 MPa

H34

AA Standards

Elastic modulus

69.0 GPa

Show Material materials with Elastic modulus of 69.0 GPa

H34

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547

69 GPa

Show Material materials with Elastic modulus of 69 GPa

H34

Elongation

3.0 %

Show Material materials with Elongation of 3.0 %

H34

AA Standards, ASTM B209

A50

4.0 %

Show Material materials with Elongation of 4.0 %

H34

AA Standards, ASTM B209, ASTM B313

A50

5.0 %

Show Material materials with Elongation of 5.0 %

H34

AA Standards, ASTM B209, ASTM B313, ASTM B547

A50

5.7 %

Show Material materials with Elongation of 5.7 %

H34

8.0 %

Show Material materials with Elongation of 8.0 %

H34

AA Standards

A50

8 %

Show Material materials with Elongation of 8 %

H34

Fatigue strength

90 MPa

Show Material materials with Fatigue strength of 90 MPa

H34

for 5x10⁸ cycles

Hardness, Brinell

53.0 [-]

Show Material materials with Hardness, Brinell of 53.0 [-]

H34

AA Standards

53.0 [-]

Show Material materials with Hardness, Brinell of 53.0 [-]

H34

500 kg load, 10 mm ball

Plane-Strain Fracture Toughnes

22.0 - 35.0 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m

Typical for Wrought 5000 Series Aluminium

Poisson's ratio

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-]

Typical for Wrought 5000 Series Aluminium

Shear modulus

25.9 GPa

Show Material materials with Shear modulus of 25.9 GPa

H34

Shear strength

123.0 MPa

Show Material materials with Shear strength of 123.0 MPa

H34

Tensile strength

-195 °C

303 MPa

Show Material materials with Tensile strength of 303 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

-80 °C

207 MPa

Show Material materials with Tensile strength of 207 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

170.0 - 215.0 MPa

Show Material materials with Tensile strength of 170.0 - 215.0 MPa

H34

AA Standards, ASTM B209, ASTM B313, ASTM B547

170.0 MPa

Show Material materials with Tensile strength of 170.0 MPa

H34

AA Standards, ASTM B210, ASTM B483

190.0 MPa

Show Material materials with Tensile strength of 190.0 MPa

H34

AA Standards

0 °C

193 MPa

Show Material materials with Tensile strength of 193 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

24 °C

193 MPa

Show Material materials with Tensile strength of 193 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

100 °C

193 MPa

Show Material materials with Tensile strength of 193 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

150 °C

172 MPa

Show Material materials with Tensile strength of 172 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

205 °C

97 MPa

Show Material materials with Tensile strength of 97 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

260 °C

62 MPa

Show Material materials with Tensile strength of 62 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

315 °C

40 MPa

Show Material materials with Tensile strength of 40 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

370 °C

27 MPa

Show Material materials with Tensile strength of 27 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

Yield strength

-196 °C

205 MPa

Show Material materials with Yield strength of 205 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

-80 °C

170 MPa

Show Material materials with Yield strength of 170 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

-28 °C

165 MPa

Show Material materials with Yield strength of 165 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

140.0 MPa

Show Material materials with Yield strength of 140.0 MPa

H34

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547

RP02

160.0 MPa

Show Material materials with Yield strength of 160.0 MPa

H34

165.0 MPa

Show Material materials with Yield strength of 165.0 MPa

H34

AA Standards

RP02

24 °C

165 MPa

Show Material materials with Yield strength of 165 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

100 °C

165 MPa

Show Material materials with Yield strength of 165 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

149 °C

150 MPa

Show Material materials with Yield strength of 150 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

204 °C

50 MPa

Show Material materials with Yield strength of 50 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

260 °C

41 MPa

Show Material materials with Yield strength of 41 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

316 °C

29 MPa

Show Material materials with Yield strength of 29 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

371 °C

18 MPa

Show Material materials with Yield strength of 18 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

Unlock all property charts

Thermal

PropertyTemperatureValueConditionRelated StandardsComment

Coefficient of thermal expansion

2.4e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.4e-05 1/K

H34

20 °C

2.38e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.38e-05 1/K

H34

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547

100 °C

2.38e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.38e-05 1/K

H34

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547

Unlock all property charts

Max service temperature

150.0 °C

Show Material materials with Max service temperature of 150.0 °C

Typical for Wrought 5000 Series Aluminium

Melting point

625.0 - 650.0 °C

Show Material materials with Melting point of 625.0 - 650.0 °C

H34

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547

630.0 °C

Show Material materials with Melting point of 630.0 °C

H34

Specific heat capacity

900.0 J/(kg·K)

Show Material materials with Specific heat capacity of 900.0 J/(kg·K)

H34

Thermal conductivity

190.0 W/(m·K)

Show Material materials with Thermal conductivity of 190.0 W/(m·K)

H34

193 W/(m·K)

Show Material materials with Thermal conductivity of 193 W/(m·K)

H34

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547

Electrical

PropertyValueConditionRelated Standards

Electrical conductivity

29000000.0 S/m

Show Material materials with Electrical conductivity of 29000000.0 S/m

H34

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547

Electrical resistivity

3.45e-08 Ω·m

Show Material materials with Electrical resistivity of 3.45e-08 Ω·m

H34

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547

Chemical properties

PropertyValueConditionRelated Standards

Aluminium

96.3 - 98.9 %

Show Material materials with Aluminium of 96.3 - 98.9 %

H34

Chromium

0.1 %

Show Material materials with Chromium of 0.1 %

H34

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547

Copper

0.2 %

Show Material materials with Copper of 0.2 %

H34

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547

Iron

0.70 %

Show Material materials with Iron of 0.70 %

H34

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547

0.7 %

Show Material materials with Iron of 0.7 %

H34

Magnesium

1.1 - 1.8 %

Show Material materials with Magnesium of 1.1 - 1.8 %

H34

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547

Manganese

0.1 %

Show Material materials with Manganese of 0.1 %

H34

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547

Other

0.15 %

Show Material materials with Other of 0.15 %

H34

Silicon

0.4 %

Show Material materials with Silicon of 0.4 %

H34

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547

Zinc

0.25 %

Show Material materials with Zinc of 0.25 %

H34

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547

Technological properties

Property
Brazing

general: Lötbar mit speziellen Techniken oder bei bestimmten Anwendungen

Corrosion properties

Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere

General machinability

General: not suitable (O), poor (H32, H34), sufficient (H36, H38)

Workability

general (condition): good (O, H32), acceptable (H34), poor(H36, H38)