AA Standards Grade 5050 H38

View suppliers (7)
Want to keep this datasheet? Save it now in your required format

Related Standards

Equivalent Materials

This material data has been provided by AluKey,MakeItFrom.com,ASM Handbook Volume 2 Properties and Selection: Nonferrous Alloys and Special-Purpose Materials.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionRelated Standards

Density

2.69 g/cm³

Show Material materials with Density of 2.69 g/cm³

H38

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483

2.69 g/cm³

Show Material materials with Density of 2.69 g/cm³

H38

2.7 g/cm³

Show Material materials with Density of 2.7 g/cm³

H38

Mechanical

PropertyTemperatureValueConditionRelated StandardsComment

Bending Fatigue Strength

95.0 MPa

Show Material materials with Bending Fatigue Strength of 95.0 MPa

H38

AA Standards

Elastic modulus

69.0 GPa

Show Material materials with Elastic modulus of 69.0 GPa

H38

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483

69 GPa

Show Material materials with Elastic modulus of 69 GPa

H38

Elongation

1.0 %

Show Material materials with Elongation of 1.0 %

H38

AA Standards, ASTM B209

A50

2.0 %

Show Material materials with Elongation of 2.0 %

H38

AA Standards, ASTM B209

A50

3.0 %

Show Material materials with Elongation of 3.0 %

H38

AA Standards, ASTM B209, ASTM B313

A50

3.1 %

Show Material materials with Elongation of 3.1 %

H38

4.0 %

Show Material materials with Elongation of 4.0 %

H38

AA Standards, ASTM B209, ASTM B313

A50

6.0 %

Show Material materials with Elongation of 6.0 %

H38

AA Standards

A50

6 %

Show Material materials with Elongation of 6 %

H38

Fatigue strength

100 MPa

Show Material materials with Fatigue strength of 100 MPa

H38

for 5x10⁸ cycles

Hardness, Brinell

63.0 [-]

Show Material materials with Hardness, Brinell of 63.0 [-]

H38

AA Standards

63.0 [-]

Show Material materials with Hardness, Brinell of 63.0 [-]

H38

500 kg load, 10 mm ball

Plane-Strain Fracture Toughnes

22.0 - 35.0 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m

Typical for Wrought 5000 Series Aluminium

Poisson's ratio

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-]

Typical for Wrought 5000 Series Aluminium

Shear modulus

25.9 GPa

Show Material materials with Shear modulus of 25.9 GPa

H38

Shear strength

135.0 MPa

Show Material materials with Shear strength of 135.0 MPa

H38

Tensile strength

-195 °C

317 MPa

Show Material materials with Tensile strength of 317 MPa

H38

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

-80 °C

235 MPa

Show Material materials with Tensile strength of 235 MPa

H38

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

200.0 MPa

Show Material materials with Tensile strength of 200.0 MPa

H38

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483

220.0 MPa

Show Material materials with Tensile strength of 220.0 MPa

H38

AA Standards

0 °C

220 MPa

Show Material materials with Tensile strength of 220 MPa

H38

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

230.0 MPa

Show Material materials with Tensile strength of 230.0 MPa

H38

24 °C

220 MPa

Show Material materials with Tensile strength of 220 MPa

H38

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

100 °C

215 MPa

Show Material materials with Tensile strength of 215 MPa

H38

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

150 °C

185 MPa

Show Material materials with Tensile strength of 185 MPa

H38

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

205 °C

97 MPa

Show Material materials with Tensile strength of 97 MPa

H38

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

260 °C

62 MPa

Show Material materials with Tensile strength of 62 MPa

H38

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

315 °C

40 MPa

Show Material materials with Tensile strength of 40 MPa

H38

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

370 °C

27 MPa

Show Material materials with Tensile strength of 27 MPa

H38

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

Yield strength

-196 °C

250 MPa

Show Material materials with Yield strength of 250 MPa

H38

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

-80 °C

205 MPa

Show Material materials with Yield strength of 205 MPa

H38

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

-28 °C

200 MPa

Show Material materials with Yield strength of 200 MPa

H38

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

165.0 MPa

Show Material materials with Yield strength of 165.0 MPa

H38

AA Standards, ASTM B210, ASTM B483

RP02

200.0 MPa

Show Material materials with Yield strength of 200.0 MPa

H38

AA Standards

RP02

200.0 MPa

Show Material materials with Yield strength of 200.0 MPa

H38

24 °C

200 MPa

Show Material materials with Yield strength of 200 MPa

H38

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

100 °C

200 MPa

Show Material materials with Yield strength of 200 MPa

H38

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

149 °C

170 MPa

Show Material materials with Yield strength of 170 MPa

H38

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

204 °C

50 MPa

Show Material materials with Yield strength of 50 MPa

H38

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

260 °C

41 MPa

Show Material materials with Yield strength of 41 MPa

H38

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

316 °C

29 MPa

Show Material materials with Yield strength of 29 MPa

H38

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

371 °C

18 MPa

Show Material materials with Yield strength of 18 MPa

H38

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

Thermal

PropertyTemperatureValueConditionRelated StandardsComment

Coefficient of thermal expansion

2.4e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.4e-05 1/K

H38

20 °C

2.38e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.38e-05 1/K

H38

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483

100 °C

2.38e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.38e-05 1/K

H38

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483

Max service temperature

150.0 °C

Show Material materials with Max service temperature of 150.0 °C

Typical for Wrought 5000 Series Aluminium

Melting point

625.0 - 650.0 °C

Show Material materials with Melting point of 625.0 - 650.0 °C

H38

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483

630.0 °C

Show Material materials with Melting point of 630.0 °C

H38

Specific heat capacity

900.0 J/(kg·K)

Show Material materials with Specific heat capacity of 900.0 J/(kg·K)

H38

Thermal conductivity

190.0 W/(m·K)

Show Material materials with Thermal conductivity of 190.0 W/(m·K)

H38

193 W/(m·K)

Show Material materials with Thermal conductivity of 193 W/(m·K)

H38

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483

Electrical

PropertyValueConditionRelated StandardsComment

Electrical conductivity

29000000.0 S/m

Show Material materials with Electrical conductivity of 29000000.0 S/m

H38

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483

29000000 S/m

Show Material materials with Electrical conductivity of 29000000 S/m

H38

Typical/derived value

Electrical resistivity

3.45e-08 Ω·m

Show Material materials with Electrical resistivity of 3.45e-08 Ω·m

H38

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483

Specific Electrical conductivity

50.0 % IACS

Show Material materials with Specific Electrical conductivity of 50.0 % IACS

H38

Typical value

Chemical properties

PropertyValueConditionRelated Standards

Aluminium

96.3 - 98.9 %

Show Material materials with Aluminium of 96.3 - 98.9 %

H38

Chromium

0.1 %

Show Material materials with Chromium of 0.1 %

H38

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483

Copper

0.2 %

Show Material materials with Copper of 0.2 %

H38

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483

Iron

0.70 %

Show Material materials with Iron of 0.70 %

H38

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483

0.7 %

Show Material materials with Iron of 0.7 %

H38

Magnesium

1.1 - 1.8 %

Show Material materials with Magnesium of 1.1 - 1.8 %

H38

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483

Manganese

0.1 %

Show Material materials with Manganese of 0.1 %

H38

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483

Other

0.15 %

Show Material materials with Other of 0.15 %

H38

Silicon

0.4 %

Show Material materials with Silicon of 0.4 %

H38

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483

Zinc

0.25 %

Show Material materials with Zinc of 0.25 %

H38

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483

Technological properties

Property
Brazing

general: Lötbar mit speziellen Techniken oder bei bestimmten Anwendungen

Corrosion properties

Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere

General machinability

General: not suitable (O), poor (H32, H34), sufficient (H36, H38)

Workability

general (condition): good (O, H32), acceptable (H34), poor(H36, H38)