AA Standards Grade 5050 O

Want to keep this datasheet? Save it now in your required format

Related Standards

Equivalent Materials

This material data has been provided by AluKey,MakeItFrom.com,ASM Handbook Volume 2 Properties and Selection: Nonferrous Alloys and Special-Purpose Materials.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionRelated Standards

Density

2.69 g/cm³

Show Material materials with Density of 2.69 g/cm³

O

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547

2.7 g/cm³

Show Material materials with Density of 2.7 g/cm³

O

2.69 g/cm³

Show Material materials with Density of 2.69 g/cm³

O

Mechanical

PropertyTemperatureValueConditionRelated StandardsComment

Bending Fatigue Strength

85.0 MPa

Show Material materials with Bending Fatigue Strength of 85.0 MPa

O

AA Standards

Elastic modulus

69.0 GPa

Show Material materials with Elastic modulus of 69.0 GPa

O

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547

69 GPa

Show Material materials with Elastic modulus of 69 GPa

O

Elongation

24.0 %

Show Material materials with Elongation of 24.0 %

O

AA Standards

A50

19.0 %

Show Material materials with Elongation of 19.0 %

O

AA Standards, ASTM B209, ASTM B313

A50

17.0 %

Show Material materials with Elongation of 17.0 %

O

AA Standards, ASTM B209

A50

15.0 %

Show Material materials with Elongation of 15.0 %

O

AA Standards, ASTM B209

A50

20.0 %

Show Material materials with Elongation of 20.0 %

O

AA Standards, ASTM B209, ASTM B313, ASTM B547

A50

18.0 %

Show Material materials with Elongation of 18.0 %

O

AA Standards, ASTM B209

A100

21.0 %

Show Material materials with Elongation of 21.0 %

O

24 %

Show Material materials with Elongation of 24 %

O

Fatigue strength

83 MPa

Show Material materials with Fatigue strength of 83 MPa

O

for 5x10⁸ cycles

Hardness, Brinell

36.0 [-]

Show Material materials with Hardness, Brinell of 36.0 [-]

O

AA Standards

36.0 [-]

Show Material materials with Hardness, Brinell of 36.0 [-]

O

500 kg load, 10 mm ball

Plane-Strain Fracture Toughnes

22.0 - 35.0 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m

Typical for Wrought 5000 Series Aluminium

Poisson's ratio

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-]

Typical for Wrought 5000 Series Aluminium

Shear modulus

25.9 GPa

Show Material materials with Shear modulus of 25.9 GPa

O

Shear strength

105.0 MPa

Show Material materials with Shear strength of 105.0 MPa

O

Tensile strength

145.0 MPa

Show Material materials with Tensile strength of 145.0 MPa

O

AA Standards

125.0 - 165.0 MPa

Show Material materials with Tensile strength of 125.0 - 165.0 MPa

O

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B547

125.0 MPa

Show Material materials with Tensile strength of 125.0 MPa

O

AA Standards, ASTM B483

140.0 MPa

Show Material materials with Tensile strength of 140.0 MPa

O

370 °C

27 MPa

Show Material materials with Tensile strength of 27 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

315 °C

40 MPa

Show Material materials with Tensile strength of 40 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

260 °C

62 MPa

Show Material materials with Tensile strength of 62 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

205 °C

97 MPa

Show Material materials with Tensile strength of 97 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

150 °C

130 MPa

Show Material materials with Tensile strength of 130 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

100 °C, 24 °C, 0 °C

145 MPa

Show Material materials with Tensile strength of 145 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

-80 °C

152 MPa

Show Material materials with Tensile strength of 152 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

-195 °C

255 MPa

Show Material materials with Tensile strength of 255 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

Yield strength

55.0 MPa

Show Material materials with Yield strength of 55.0 MPa

O

AA Standards

RP02

40.0 MPa

Show Material materials with Yield strength of 40.0 MPa

O

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547

RP02

371 °C

18 MPa

Show Material materials with Yield strength of 18 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

316 °C

29 MPa

Show Material materials with Yield strength of 29 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

260 °C

41 MPa

Show Material materials with Yield strength of 41 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

204 °C

50 MPa

Show Material materials with Yield strength of 50 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

149 °C, 100 °C, 24 °C, -28 °C

55 MPa

Show Material materials with Yield strength of 55 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

-80 °C

60 MPa

Show Material materials with Yield strength of 60 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

-196 °C

70 MPa

Show Material materials with Yield strength of 70 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

50.0 MPa

Show Material materials with Yield strength of 50.0 MPa

O

Unlock all property charts

Thermal

PropertyTemperatureValueConditionRelated StandardsComment

Coefficient of thermal expansion

2.4e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.4e-05 1/K

O

100 °C, 20 °C

2.38e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.38e-05 1/K

O

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547

Max service temperature

150.0 °C

Show Material materials with Max service temperature of 150.0 °C

Typical for Wrought 5000 Series Aluminium

Melting point

625.0 - 650.0 °C

Show Material materials with Melting point of 625.0 - 650.0 °C

O

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547

630.0 °C

Show Material materials with Melting point of 630.0 °C

O

Specific heat capacity

900.0 J/(kg·K)

Show Material materials with Specific heat capacity of 900.0 J/(kg·K)

O

Thermal conductivity

193 W/(m·K)

Show Material materials with Thermal conductivity of 193 W/(m·K)

O

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547

190.0 W/(m·K)

Show Material materials with Thermal conductivity of 190.0 W/(m·K)

O

Electrical

PropertyValueConditionRelated StandardsComment

Electrical conductivity

29000000.0 S/m

Show Material materials with Electrical conductivity of 29000000.0 S/m

O

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547

29000000 S/m

Show Material materials with Electrical conductivity of 29000000 S/m

O

Typical/derived value

Electrical resistivity

3.45e-08 Ω·m

Show Material materials with Electrical resistivity of 3.45e-08 Ω·m

O

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547

Specific Electrical conductivity

50.0 % IACS

Show Material materials with Specific Electrical conductivity of 50.0 % IACS

O

Typical value

Chemical properties

PropertyValueConditionRelated Standards

Aluminium

96.3 - 98.9 %

Show Material materials with Aluminium of 96.3 - 98.9 %

O

Chromium

0.1 %

Show Material materials with Chromium of 0.1 %

O

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547

Copper

0.2 %

Show Material materials with Copper of 0.2 %

O

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547

Iron

0.70 %

Show Material materials with Iron of 0.70 %

O

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547

0.7 %

Show Material materials with Iron of 0.7 %

O

Magnesium

1.1 - 1.8 %

Show Material materials with Magnesium of 1.1 - 1.8 %

O

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547

Manganese

0.1 %

Show Material materials with Manganese of 0.1 %

O

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547

Other

0.15 %

Show Material materials with Other of 0.15 %

O

Silicon

0.4 %

Show Material materials with Silicon of 0.4 %

O

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547

Zinc

0.25 %

Show Material materials with Zinc of 0.25 %

O

AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547

Technological properties

Property
Brazing

general: Lötbar mit speziellen Techniken oder bei bestimmten Anwendungen

Corrosion properties

Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere

General machinability

General: not suitable (O), poor (H32, H34), sufficient (H36, H38)

Workability

general (condition): good (O, H32), acceptable (H34), poor(H36, H38)