Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.68 g/cm³ Show Material materials with Density of 2.68 g/cm³ | H38 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 |
2.68 g/cm³ Show Material materials with Density of 2.68 g/cm³ | H38 | ||
2.7 g/cm³ Show Material materials with Density of 2.7 g/cm³ | H38 |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Bending Fatigue Strength | 140.0 MPa Show Material materials with Bending Fatigue Strength of 140.0 MPa | H38 | AA Standards | ||
Elastic modulus | 70.0 GPa Show Material materials with Elastic modulus of 70.0 GPa | H38 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 | ||
70 GPa Show Material materials with Elastic modulus of 70 GPa | H38 | ||||
Elongation | -195 °C | 25 % Show Material materials with Elongation of 25 % | H38 | Elongation in 50 mm | |
-80 °C | 18 % Show Material materials with Elongation of 18 % | H38 | Elongation in 50 mm | ||
2.0 % Show Material materials with Elongation of 2.0 % | H38 | AA Standards, ASTM B209 | A50 | ||
3.0 % Show Material materials with Elongation of 3.0 % | H38 | AA Standards, ASTM B209 | A50 | ||
4.0 % Show Material materials with Elongation of 4.0 % | H38 | AA Standards, ASTM B209, ASTM B313 | A50 | ||
5.9 % Show Material materials with Elongation of 5.9 % | H38 | ||||
7.0 % Show Material materials with Elongation of 7.0 % | H38 | AA Standards | A50 | ||
7.0 % Show Material materials with Elongation of 7.0 % | H38 | AA Standards | A100 | ||
0 °C | 15 % Show Material materials with Elongation of 15 % | H38 | Elongation in 50 mm | ||
24 °C | 14 % Show Material materials with Elongation of 14 % | H38 | Elongation in 50 mm | ||
100 °C | 16 % Show Material materials with Elongation of 16 % | H38 | Elongation in 50 mm | ||
150 °C | 24 % Show Material materials with Elongation of 24 % | H38 | Elongation in 50 mm | ||
205 °C | 45 % Show Material materials with Elongation of 45 % | H38 | Elongation in 50 mm | ||
260 °C | 80 % Show Material materials with Elongation of 80 % | H38 | Elongation in 50 mm | ||
315 °C | 110 % Show Material materials with Elongation of 110 % | H38 | Elongation in 50 mm | ||
370 °C | 130 % Show Material materials with Elongation of 130 % | H38 | Elongation in 50 mm | ||
Fatigue strength | 140 MPa Show Material materials with Fatigue strength of 140 MPa | H38 | for 5x10⁸ cycles | ||
Hardness, Brinell | 77.0 [-] Show Material materials with Hardness, Brinell of 77.0 [-] | H38 | AA Standards | ||
77.0 [-] Show Material materials with Hardness, Brinell of 77.0 [-] | H38 | 500 kg load, 10 mm ball | |||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | |||
Shear modulus | 25.9 GPa Show Material materials with Shear modulus of 25.9 GPa | H38 | |||
Shear strength | 165.0 MPa Show Material materials with Shear strength of 165.0 MPa | H38 | |||
Tensile strength | -195 °C | 415 MPa Show Material materials with Tensile strength of 415 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
-80 °C | 303 MPa Show Material materials with Tensile strength of 303 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
270.0 MPa Show Material materials with Tensile strength of 270.0 MPa | H38 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 | |||
290.0 MPa Show Material materials with Tensile strength of 290.0 MPa | H38 | AA Standards | |||
0 °C | 290 MPa Show Material materials with Tensile strength of 290 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
300.0 MPa Show Material materials with Tensile strength of 300.0 MPa | H38 | ||||
24 °C | 290 MPa Show Material materials with Tensile strength of 290 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
100 °C | 275 MPa Show Material materials with Tensile strength of 275 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
150 °C | 235 MPa Show Material materials with Tensile strength of 235 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
205 °C | 172 MPa Show Material materials with Tensile strength of 172 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
260 °C | 83 MPa Show Material materials with Tensile strength of 83 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
315 °C | 52 MPa Show Material materials with Tensile strength of 52 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
370 °C | 35 MPa Show Material materials with Tensile strength of 35 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
Yield strength | -196 °C | 303 MPa Show Material materials with Yield strength of 303 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
-80 °C | 262 MPa Show Material materials with Yield strength of 262 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
-28 °C | 255 MPa Show Material materials with Yield strength of 255 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
215.0 MPa Show Material materials with Yield strength of 215.0 MPa | H38 | AA Standards, ASTM B210, ASTM B483 | RP02 | ||
220.0 MPa Show Material materials with Yield strength of 220.0 MPa | H38 | AA Standards, ASTM B209, ASTM B313 | RP02 | ||
250.0 MPa Show Material materials with Yield strength of 250.0 MPa | H38 | ||||
255.0 MPa Show Material materials with Yield strength of 255.0 MPa | H38 | AA Standards | RP02 | ||
24 °C | 255 MPa Show Material materials with Yield strength of 255 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
100 °C | 248 MPa Show Material materials with Yield strength of 248 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
149 °C | 193 MPa Show Material materials with Yield strength of 193 MPa | H38 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 2.4e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.4e-05 1/K | H38 | |||
20 °C | 2.38e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.38e-05 1/K | H38 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 | ||
100 °C | 2.38e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.38e-05 1/K | H38 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 | ||
Max service temperature | 150.0 °C Show Material materials with Max service temperature of 150.0 °C | Typical for Wrought 5000 Series Aluminium | |||
Melting point | 605.0 - 650.0 °C Show Material materials with Melting point of 605.0 - 650.0 °C | H38 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 | ||
610.0 °C Show Material materials with Melting point of 610.0 °C | H38 | ||||
Specific heat capacity | 900.0 J/(kg·K) Show Material materials with Specific heat capacity of 900.0 J/(kg·K) | H38 | |||
Thermal conductivity | 138 W/(m·K) Show Material materials with Thermal conductivity of 138 W/(m·K) | H38 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 | ||
140.0 W/(m·K) Show Material materials with Thermal conductivity of 140.0 W/(m·K) | H38 | ||||
Electrical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Electrical conductivity | 20000000.0 S/m Show Material materials with Electrical conductivity of 20000000.0 S/m | H38 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 | |
20300000 S/m Show Material materials with Electrical conductivity of 20300000 S/m | H38 | Unstated/Typical value | ||
Electrical resistivity | 5e-08 Ω·m Show Material materials with Electrical resistivity of 5e-08 Ω·m | H38 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 | |
Specific Electrical conductivity | 35.0 % IACS Show Material materials with Specific Electrical conductivity of 35.0 % IACS | H38 | Unstated value |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 95.8 - 97.7 % Show Material materials with Aluminium of 95.8 - 97.7 % | H38 | |
Chromium | 0.15 - 0.35 % Show Material materials with Chromium of 0.15 - 0.35 % | H38 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 |
Copper | 0.1 % Show Material materials with Copper of 0.1 % | H38 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 |
Iron | 0.40 % Show Material materials with Iron of 0.40 % | H38 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 |
0.4 % Show Material materials with Iron of 0.4 % | H38 | ||
Magnesium | 2.2 - 2.8 % Show Material materials with Magnesium of 2.2 - 2.8 % | H38 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 |
Manganese | 0.1 % Show Material materials with Manganese of 0.1 % | H38 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 |
Other | 0.15 % Show Material materials with Other of 0.15 % | H38 | |
Silicon | 0.25 % Show Material materials with Silicon of 0.25 % | H38 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 |
Zinc | 0.1 % Show Material materials with Zinc of 0.1 % | H38 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: limited brazing | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (O, H32), sufficient (H34, H36, H38) | |
| Workability | general (condition): good (O), acceptable (H32, H34), poor(H36, H38) | |