Description

Aluminum AA 5052 is a non-heat treatable alloy with excellent finishing qualities. AA 5052 offers better corrosion resistance than most aluminum alloys, especially to salt water and marine atmospheres. This alloy can be readily welded using most common techniques and is in fact offers some of the best welding characteristics of all aluminum alloys.

Related Standards

Equivalent Materials

This material data has been provided by AluKey,MakeItFrom.com,ASM Handbook Volume 2 Properties and Selection: Nonferrous Alloys and Special-Purpose Materials.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionRelated Standards

Density

2.68 g/cm³

Show Material materials with Density of 2.68 g/cm³

O

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547

2.7 g/cm³

Show Material materials with Density of 2.7 g/cm³

O

2.68 g/cm³

Show Material materials with Density of 2.68 g/cm³

O

Mechanical

PropertyTemperatureValueConditionRelated StandardsComment

Bending Fatigue Strength

110.0 MPa

Show Material materials with Bending Fatigue Strength of 110.0 MPa

O

AA Standards

Elastic modulus

70.0 GPa

Show Material materials with Elastic modulus of 70.0 GPa

O

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547

70 GPa

Show Material materials with Elastic modulus of 70 GPa

O

Elongation

25.0 %

Show Material materials with Elongation of 25.0 %

O

AA Standards, ASTM B211

A50

15.0 %

Show Material materials with Elongation of 15.0 %

O

AA Standards, ASTM B209

A50

18.0 %

Show Material materials with Elongation of 18.0 %

O

AA Standards, ASTM B209, ASTM B547

A50

19.0 %

Show Material materials with Elongation of 19.0 %

O

AA Standards, ASTM B209, ASTM B313, ASTM B547

A50

17.0 %

Show Material materials with Elongation of 17.0 %

O

AA Standards, ASTM B209, ASTM B313

A50

13.0 %

Show Material materials with Elongation of 13.0 %

O

AA Standards, ASTM B209

A50

27.0 %

Show Material materials with Elongation of 27.0 %

O

AA Standards

A100

16.0 %

Show Material materials with Elongation of 16.0 %

O

AA Standards, ASTM B209

A100

22.0 %

Show Material materials with Elongation of 22.0 %

O

AA Standards, ASTM B211

A100

23.0 %

Show Material materials with Elongation of 23.0 %

O

370 °C

130 %

Show Material materials with Elongation of 130 %

O

Elongation in 50 mm

315 °C

110 %

Show Material materials with Elongation of 110 %

O

Elongation in 50 mm

260 °C

80 %

Show Material materials with Elongation of 80 %

O

Elongation in 50 mm

205 °C

60 %

Show Material materials with Elongation of 60 %

O

Elongation in 50 mm

150 °C

50 %

Show Material materials with Elongation of 50 %

O

Elongation in 50 mm

100 °C

36 %

Show Material materials with Elongation of 36 %

O

Elongation in 50 mm

24 °C

30 %

Show Material materials with Elongation of 30 %

O

Elongation in 50 mm

0 °C

32 %

Show Material materials with Elongation of 32 %

O

Elongation in 50 mm

-80 °C

35 %

Show Material materials with Elongation of 35 %

O

Elongation in 50 mm

-195 °C

46 %

Show Material materials with Elongation of 46 %

O

Elongation in 50 mm

Fatigue strength

110 MPa

Show Material materials with Fatigue strength of 110 MPa

O

for 5x10⁸ cycles

Hardness, Brinell

47.0 [-]

Show Material materials with Hardness, Brinell of 47.0 [-]

O

AA Standards

47.0 [-]

Show Material materials with Hardness, Brinell of 47.0 [-]

O

500 kg load, 10 mm ball

Plane-Strain Fracture Toughnes

22.0 - 35.0 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m

Typical for Wrought 5000 Series Aluminium

Poisson's ratio

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-]

Typical for Wrought 5000 Series Aluminium

Shear modulus

25.9 GPa

Show Material materials with Shear modulus of 25.9 GPa

O

Shear strength

125.0 MPa

Show Material materials with Shear strength of 125.0 MPa

O

Tensile strength

195.0 MPa

Show Material materials with Tensile strength of 195.0 MPa

O

AA Standards

170.0 - 215.0 MPa

Show Material materials with Tensile strength of 170.0 - 215.0 MPa

O

AA Standards, ASTM B209, ASTM B313, ASTM B547

170.0 - 240.0 MPa

Show Material materials with Tensile strength of 170.0 - 240.0 MPa

O

AA Standards, ASTM B210, ASTM B221, ASTM B241

170.0 - 220.0 MPa

Show Material materials with Tensile strength of 170.0 - 220.0 MPa

O

AA Standards, ASTM B211

220.0 MPa

Show Material materials with Tensile strength of 220.0 MPa

O

AA Standards, ASTM B316

170.0 MPa

Show Material materials with Tensile strength of 170.0 MPa

O

AA Standards, ASTM B483

190.0 MPa

Show Material materials with Tensile strength of 190.0 MPa

O

370 °C

35 MPa

Show Material materials with Tensile strength of 35 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

315 °C

52 MPa

Show Material materials with Tensile strength of 52 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

260 °C

83 MPa

Show Material materials with Tensile strength of 83 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

205 °C

117 MPa

Show Material materials with Tensile strength of 117 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

150 °C

160 MPa

Show Material materials with Tensile strength of 160 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

100 °C, 24 °C, 0 °C

193 MPa

Show Material materials with Tensile strength of 193 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

-80 °C

200 MPa

Show Material materials with Tensile strength of 200 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

-195 °C

303 MPa

Show Material materials with Tensile strength of 303 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

Unlock all property charts

Yield strength

90.0 MPa

Show Material materials with Yield strength of 90.0 MPa

O

AA Standards

RP02

65.0 MPa

Show Material materials with Yield strength of 65.0 MPa

O

AA Standards, ASTM B209, ASTM B211, ASTM B313, ASTM B547

RP02

70.0 MPa

Show Material materials with Yield strength of 70.0 MPa

O

AA Standards, ASTM B210, ASTM B221, ASTM B241, ASTM B483

RP02

371 °C

21 MPa

Show Material materials with Yield strength of 21 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

316 °C

38 MPa

Show Material materials with Yield strength of 38 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

260 °C

52 MPa

Show Material materials with Yield strength of 52 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

204 °C

76 MPa

Show Material materials with Yield strength of 76 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

149 °C, 100 °C, 24 °C, -28 °C, -80 °C

90 MPa

Show Material materials with Yield strength of 90 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

-196 °C

110 MPa

Show Material materials with Yield strength of 110 MPa

O

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

80.0 MPa

Show Material materials with Yield strength of 80.0 MPa

O

Unlock all property charts

Thermal

PropertyTemperatureValueConditionRelated StandardsComment

Coefficient of thermal expansion

2.4e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.4e-05 1/K

O

100 °C, 20 °C

2.38e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.38e-05 1/K

O

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547

Max service temperature

150.0 °C

Show Material materials with Max service temperature of 150.0 °C

Typical for Wrought 5000 Series Aluminium

Melting point

605.0 - 650.0 °C

Show Material materials with Melting point of 605.0 - 650.0 °C

O

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547

610.0 °C

Show Material materials with Melting point of 610.0 °C

O

Specific heat capacity

900.0 J/(kg·K)

Show Material materials with Specific heat capacity of 900.0 J/(kg·K)

O

Thermal conductivity

138 W/(m·K)

Show Material materials with Thermal conductivity of 138 W/(m·K)

O

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547

140.0 W/(m·K)

Show Material materials with Thermal conductivity of 140.0 W/(m·K)

O

Electrical

PropertyValueConditionRelated StandardsComment

Electrical conductivity

20000000.0 S/m

Show Material materials with Electrical conductivity of 20000000.0 S/m

O

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547

20300000 S/m

Show Material materials with Electrical conductivity of 20300000 S/m

O

Unstated/Typical value, Typical/derived value

Electrical resistivity

5e-08 Ω·m

Show Material materials with Electrical resistivity of 5e-08 Ω·m

O

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547

Specific Electrical conductivity

35.0 % IACS

Show Material materials with Specific Electrical conductivity of 35.0 % IACS

O

Unstated value, Typical value

Chemical properties

PropertyValueConditionRelated Standards

Aluminium

95.8 - 97.7 %

Show Material materials with Aluminium of 95.8 - 97.7 %

O

Chromium

0.15 - 0.35 %

Show Material materials with Chromium of 0.15 - 0.35 %

O

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547

Copper

0.1 %

Show Material materials with Copper of 0.1 %

O

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547

Iron

0.40 %

Show Material materials with Iron of 0.40 %

O

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547

0.4 %

Show Material materials with Iron of 0.4 %

O

Magnesium

2.2 - 2.8 %

Show Material materials with Magnesium of 2.2 - 2.8 %

O

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547

Manganese

0.1 %

Show Material materials with Manganese of 0.1 %

O

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547

Other

0.15 %

Show Material materials with Other of 0.15 %

O

Silicon

0.25 %

Show Material materials with Silicon of 0.25 %

O

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547

Zinc

0.1 %

Show Material materials with Zinc of 0.1 %

O

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547

Technological properties

Property
Brazing

general: limited brazing

Corrosion properties

Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere

General machinability

General: poor (O, H32), sufficient (H34, H36, H38)

Workability

general (condition): good (O), acceptable (H32, H34), poor(H36, H38)