AA Standards Grade 5056 H14

Want to keep this datasheet? Save it now in your required format

Related Standards

Equivalent Materials

This material data has been provided by AluKey,MakeItFrom.com.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionRelated Standards

Density

2.64 g/cm³

Show Material materials with Density of 2.64 g/cm³

H14

AA Standards, ASTM B211

2.7 g/cm³

Show Material materials with Density of 2.7 g/cm³

H14

Mechanical

PropertyValueConditionRelated StandardsComment

Elastic modulus

71.0 GPa

Show Material materials with Elastic modulus of 71.0 GPa

H14

AA Standards, ASTM B211

Plane-Strain Fracture Toughnes

22.0 - 35.0 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m

Typical for Wrought 5000 Series Aluminium

Poisson's ratio

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-]

Typical for Wrought 5000 Series Aluminium

Shear modulus

26.0 - 26.5 GPa

Show Material materials with Shear modulus of 26.0 - 26.5 GPa

Typical for Wrought 5000 Series Aluminium

Tensile strength

360.0 MPa

Show Material materials with Tensile strength of 360.0 MPa

H14

AA Standards, ASTM B211

410.0 MPa

Show Material materials with Tensile strength of 410.0 MPa

H14

Thermal

PropertyTemperatureValueConditionRelated StandardsComment

Coefficient of thermal expansion

2.4e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.4e-05 1/K

H14

20 °C

2.41e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.41e-05 1/K

H14

AA Standards, ASTM B211

100 °C

2.41e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.41e-05 1/K

H14

AA Standards, ASTM B211

Max service temperature

150.0 °C

Show Material materials with Max service temperature of 150.0 °C

Typical for Wrought 5000 Series Aluminium

Melting point

565.0 - 640.0 °C

Show Material materials with Melting point of 565.0 - 640.0 °C

H14

AA Standards, ASTM B211

570.0 °C

Show Material materials with Melting point of 570.0 °C

H14

Specific heat capacity

910.0 J/(kg·K)

Show Material materials with Specific heat capacity of 910.0 J/(kg·K)

H14

Thermal conductivity

109.0 - 117.0 W/(m·K)

Show Material materials with Thermal conductivity of 109.0 - 117.0 W/(m·K)

H14

AA Standards, ASTM B211

Electrical

PropertyValueConditionRelated Standards

Electrical conductivity

16000000.0 - 17000000.0 S/m

Show Material materials with Electrical conductivity of 16000000.0 - 17000000.0 S/m

H14

AA Standards, ASTM B211

Electrical resistivity

5.88e-08 - 6.25e-08 Ω·m

Show Material materials with Electrical resistivity of 5.88e-08 - 6.25e-08 Ω·m

H14

AA Standards, ASTM B211

Chemical properties

PropertyValueConditionRelated Standards

Aluminium

93.0 - 95.4 %

Show Material materials with Aluminium of 93.0 - 95.4 %

H14

Chromium

0.05 - 0.2 %

Show Material materials with Chromium of 0.05 - 0.2 %

H14

AA Standards, ASTM B211

Copper

0.1 %

Show Material materials with Copper of 0.1 %

H14

AA Standards, ASTM B211

Iron

0.40 %

Show Material materials with Iron of 0.40 %

H14

AA Standards, ASTM B211

0.4 %

Show Material materials with Iron of 0.4 %

H14

Magnesium

4.5 - 5.6 %

Show Material materials with Magnesium of 4.5 - 5.6 %

H14

AA Standards, ASTM B211

Manganese

0.05 - 0.2 %

Show Material materials with Manganese of 0.05 - 0.2 %

H14

AA Standards, ASTM B211

Other

0.15 %

Show Material materials with Other of 0.15 %

H14

Silicon

0.3 %

Show Material materials with Silicon of 0.3 %

H14

AA Standards, ASTM B211

Zinc

0.1 %

Show Material materials with Zinc of 0.1 %

H14

AA Standards, ASTM B211

Technological properties

Property
Brazing

general: no brazing is known or developed

Corrosion properties

Stress corrosion cracking: kein Schadensfall im Betrieb, eingeschränkte Schäden bei den Labortests (O, H111, H12, H32, H14, H34), c (H18, H38), d (H192, H392), general: sehr gut, ohne Schutz in industrieller oder Seewasser-Atmosphäre (O, H111, H12, H32, H14, H34, H18, H38), b (H192, H392)

General machinability

General: poor (O, H111, H12, H32), sufficient (H14, H34, H18, H38), good to acceptable (H192, H392)

Workability

general (condition): good (O, H111), acceptable (H12, H32, H14, H34), poor(H18, H38), d (H192, H392)