Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.64 g/cm³ Show Material materials with Density of 2.64 g/cm³ | H18 | AA Standards, ASTM B211 |
2.64 g/cm³ Show Material materials with Density of 2.64 g/cm³ | H18 | ||
2.7 g/cm³ Show Material materials with Density of 2.7 g/cm³ | H18 |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Bending Fatigue Strength | 150.0 MPa Show Material materials with Bending Fatigue Strength of 150.0 MPa | H18 | AA Standards | ||
Elastic modulus | 71.0 GPa Show Material materials with Elastic modulus of 71.0 GPa | H18 | AA Standards, ASTM B211 | ||
71 GPa Show Material materials with Elastic modulus of 71 GPa | H18 | ||||
Elongation | 9.0 % Show Material materials with Elongation of 9.0 % | H18 | AA Standards | A100 | |
9.7 % Show Material materials with Elongation of 9.7 % | H18 | ||||
24 °C | 15 % Show Material materials with Elongation of 15 % | H18 | Elongation in 50 mm | ||
149 °C | 30 % Show Material materials with Elongation of 30 % | H18 | Elongation in 50 mm | ||
204 °C | 50 % Show Material materials with Elongation of 50 % | H18 | Elongation in 50 mm | ||
260 °C | 80 % Show Material materials with Elongation of 80 % | H18 | Elongation in 50 mm | ||
316 °C | 100 % Show Material materials with Elongation of 100 % | H18 | Elongation in 50 mm | ||
Fatigue strength | 152 MPa Show Material materials with Fatigue strength of 152 MPa | H18 | for 5x10⁸ cycles | ||
Hardness, Brinell | 105.0 [-] Show Material materials with Hardness, Brinell of 105.0 [-] | H18 | AA Standards | ||
105.0 [-] Show Material materials with Hardness, Brinell of 105.0 [-] | H18 | 500 kg load, 10 mm ball | |||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | |||
Shear modulus | 25.9 GPa Show Material materials with Shear modulus of 25.9 GPa | H18 | |||
Shear strength | 234.0 MPa Show Material materials with Shear strength of 234.0 MPa | H18 | |||
Tensile strength | 400.0 MPa Show Material materials with Tensile strength of 400.0 MPa | H18 | AA Standards, ASTM B211 | ||
435.0 MPa Show Material materials with Tensile strength of 435.0 MPa | H18 | AA Standards | |||
440.0 MPa Show Material materials with Tensile strength of 440.0 MPa | H18 | ||||
24 °C | 414 MPa Show Material materials with Tensile strength of 414 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
149 °C | 262 MPa Show Material materials with Tensile strength of 262 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
204 °C | 179 MPa Show Material materials with Tensile strength of 179 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
260 °C | 110 MPa Show Material materials with Tensile strength of 110 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
316 °C | 76 MPa Show Material materials with Tensile strength of 76 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
Yield strength | 405.0 MPa Show Material materials with Yield strength of 405.0 MPa | H18 | AA Standards | RP02 | |
410.0 MPa Show Material materials with Yield strength of 410.0 MPa | H18 | ||||
24 °C | 345 MPa Show Material materials with Yield strength of 345 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
149 °C | 214 MPa Show Material materials with Yield strength of 214 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
204 °C | 124 MPa Show Material materials with Yield strength of 124 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
260 °C | 69 MPa Show Material materials with Yield strength of 69 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
316 °C | 48 MPa Show Material materials with Yield strength of 48 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 2.4e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.4e-05 1/K | H18 | |||
20 °C | 2.41e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.41e-05 1/K | H18 | AA Standards, ASTM B211 | ||
100 °C | 2.41e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.41e-05 1/K | H18 | AA Standards, ASTM B211 | ||
Max service temperature | 150.0 °C Show Material materials with Max service temperature of 150.0 °C | Typical for Wrought 5000 Series Aluminium | |||
Melting point | 565.0 - 640.0 °C Show Material materials with Melting point of 565.0 - 640.0 °C | H18 | AA Standards, ASTM B211 | ||
570.0 °C Show Material materials with Melting point of 570.0 °C | H18 | ||||
Specific heat capacity | 910.0 J/(kg·K) Show Material materials with Specific heat capacity of 910.0 J/(kg·K) | H18 | |||
Thermal conductivity | 109.0 - 117.0 W/(m·K) Show Material materials with Thermal conductivity of 109.0 - 117.0 W/(m·K) | H18 | AA Standards, ASTM B211 | ||
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 16000000.0 - 17000000.0 S/m Show Material materials with Electrical conductivity of 16000000.0 - 17000000.0 S/m | H18 | AA Standards, ASTM B211 |
Electrical resistivity | 5.88e-08 - 6.25e-08 Ω·m Show Material materials with Electrical resistivity of 5.88e-08 - 6.25e-08 Ω·m | H18 | AA Standards, ASTM B211 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 93.0 - 95.4 % Show Material materials with Aluminium of 93.0 - 95.4 % | H18 | |
Chromium | 0.05 - 0.2 % Show Material materials with Chromium of 0.05 - 0.2 % | H18 | AA Standards, ASTM B211 |
Copper | 0.1 % Show Material materials with Copper of 0.1 % | H18 | AA Standards, ASTM B211 |
Iron | 0.40 % Show Material materials with Iron of 0.40 % | H18 | AA Standards, ASTM B211 |
0.4 % Show Material materials with Iron of 0.4 % | H18 | ||
Magnesium | 4.5 - 5.6 % Show Material materials with Magnesium of 4.5 - 5.6 % | H18 | AA Standards, ASTM B211 |
Manganese | 0.05 - 0.2 % Show Material materials with Manganese of 0.05 - 0.2 % | H18 | AA Standards, ASTM B211 |
Other | 0.15 % Show Material materials with Other of 0.15 % | H18 | |
Silicon | 0.3 % Show Material materials with Silicon of 0.3 % | H18 | AA Standards, ASTM B211 |
Zinc | 0.1 % Show Material materials with Zinc of 0.1 % | H18 | AA Standards, ASTM B211 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: kein Schadensfall im Betrieb, eingeschränkte Schäden bei den Labortests (O, H111, H12, H32, H14, H34), c (H18, H38), d (H192, H392), general: sehr gut, ohne Schutz in industrieller oder Seewasser-Atmosphäre (O, H111, H12, H32, H14, H34, H18, H38), b (H192, H392) | |
| General machinability | General: poor (O, H111, H12, H32), sufficient (H14, H34, H18, H38), good to acceptable (H192, H392) | |
| Workability | general (condition): good (O, H111), acceptable (H12, H32, H14, H34), poor(H18, H38), d (H192, H392) | |