Properties
General
| Property | Value | Temperature |
|---|---|---|
Density | 2.7 g/cm³ Show Material materials with Density of 2.7 g/cm³ at 23.0 °C | 23.0 °C |
Mechanical
| Property | Value | Temperature | Comment |
|---|---|---|---|
Elastic modulus | 69 GPa Show Material materials with Elastic modulus of 69 GPa at 23.0 °C | 23.0 °C | |
Elongation | 29 % Show Material materials with Elongation of 29 % at 23.0 °C | 23.0 °C | |
Plane-Strain Fracture Toughnes | 22 - 35 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22 - 35 MPa·√m at 23.0 °C | 23.0 °C | Typical for Wrought 1000 Series Aluminium |
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] at 23.0 °C | 23.0 °C | Typical for Wrought 1000 Series Aluminium |
Shear modulus | 25.9 GPa Show Material materials with Shear modulus of 25.9 GPa at 23.0 °C | 23.0 °C | Typical for Wrought 1000 Series Aluminium |
Tensile strength | 82 MPa Show Material materials with Tensile strength of 82 MPa at 23.0 °C | 23.0 °C | |
Yield strength | 35 MPa Show Material materials with Yield strength of 35 MPa at 23.0 °C | 23.0 °C |
Thermal
| Property | Value | Temperature |
|---|---|---|
Coefficient of thermal expansion | 2.4E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.4E-5 1/K at 23.0 °C | 23.0 °C |
Melting point | 650 °C Show Material materials with Melting point of 650 °C | |
Specific heat capacity | 900 J/(kg·K) Show Material materials with Specific heat capacity of 900 J/(kg·K) at 23.0 °C | 23.0 °C |
Thermal conductivity | 230 W/(m·K) Show Material materials with Thermal conductivity of 230 W/(m·K) at 23.0 °C | 23.0 °C |
Electrical
| Property | Value | Temperature | Comment |
|---|---|---|---|
Electrical conductivity | 3.30E+7 - 3.80E+7 S/m Show Material materials with Electrical conductivity of 3.30E+7 - 3.80E+7 S/m at 23.0 °C | 23.0 °C | Typical for Wrought 1000 Series Aluminium |
Electrical resistivity | 2.7E-8 - 3E-8 Ω·m Show Material materials with Electrical resistivity of 2.7E-8 - 3E-8 Ω·m at 23.0 °C | 23.0 °C | Typical for Wrought 1000 Series Aluminium |
Chemical properties
| Property | ||
|---|---|---|
Aluminium | 99.5 - 100 % | |
Copper | 0 - 0.05 % | |
Iron | 0 - 0.4 % | |
Magnesium | 0 - 0.05 % | |
Manganese | 0 - 0.05 % | |
Silicon | 0 - 0.25 % | |
Titanium | 0 - 0.03 % | |
Vanadium | 0 - 0.05 % | |
Zinc | 0 - 0.05 % |
Technological properties
| Property | ||
|---|---|---|
| Brazing | Excellent | |
| Workability | Excellent workability. | |