General
Property | Value | Condition | Related Standards | Shape |
---|---|---|---|---|
Density | 2.65 g/cm³ Show Material materials with Density of 2.65 g/cm³ | O | BS EN 573-3, BS EN 485-2 | Plate, Sheet |
2.66 g/cm³ Show Material materials with Density of 2.66 g/cm³ | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 | ||
2.66 g/cm³ Show Material materials with Density of 2.66 g/cm³ | O | |||
2.7 g/cm³ Show Material materials with Density of 2.7 g/cm³ | O |
Mechanical
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Compressive modulus | 71.7 MPa Show Material materials with Compressive modulus of 71.7 MPa | O | ||||
Elastic modulus | 71.0 GPa Show Material materials with Elastic modulus of 71.0 GPa | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 | |||
71 GPa Show Material materials with Elastic modulus of 71 GPa | O | |||||
Elongation | -195 °C | 36 % Show Material materials with Elongation of 36 % | O | Elongation in 50 mm | ||
-80 °C | 30 % Show Material materials with Elongation of 30 % | O | Elongation in 50 mm | |||
10.0 % Show Material materials with Elongation of 10.0 % | O | AA Standards, ASTM B209 | A100 | |||
12.0 % Show Material materials with Elongation of 12.0 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345 | A100 | |||
14.0 % Show Material materials with Elongation of 14.0 % | O | AA Standards, ASTM B209 | A100 | |||
14.0 % Show Material materials with Elongation of 14.0 % | O | AA Standards, ASTM B210, ASTM B221, ASTM B241, ASTM B345 | A50 | |||
16.0 % Show Material materials with Elongation of 16.0 % | O | AA Standards, ASTM B209, ASTM B547 | A50 | |||
16.0 % Show Material materials with Elongation of 16.0 % | O | |||||
20.0 % Show Material materials with Elongation of 20.0 % | O | AA Standards | A100 | |||
0 °C | 27 % Show Material materials with Elongation of 27 % | O | Elongation in 50 mm | |||
24 °C | 25 % Show Material materials with Elongation of 25 % | O | Elongation in 50 mm | |||
100 °C | 36 % Show Material materials with Elongation of 36 % | O | Elongation in 50 mm | |||
150 °C | 50 % Show Material materials with Elongation of 50 % | O | Elongation in 50 mm | |||
205 °C | 60 % Show Material materials with Elongation of 60 % | O | Elongation in 50 mm | |||
260 °C | 80 % Show Material materials with Elongation of 80 % | O | Elongation in 50 mm | |||
315 °C | 110 % Show Material materials with Elongation of 110 % | O | Elongation in 50 mm | |||
370 °C | 130 % Show Material materials with Elongation of 130 % | O | Elongation in 50 mm | |||
Fatigue strength | 160 MPa Show Material materials with Fatigue strength of 160 MPa | O | for 5x10⁸ cycles | |||
Hardness, Brinell | 75.0 [-] Show Material materials with Hardness, Brinell of 75.0 [-] | O | BS EN 573-3, BS EN 485-2 | Plate, Sheet | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||||
Shear modulus | 26.4 GPa Show Material materials with Shear modulus of 26.4 GPa | O | ||||
Shear strength | 172.0 MPa Show Material materials with Shear strength of 172.0 MPa | O | ||||
Tensile strength | -195 °C | 407 MPa Show Material materials with Tensile strength of 407 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
-80 °C | 295 MPa Show Material materials with Tensile strength of 295 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
125.0 MPa Show Material materials with Tensile strength of 125.0 MPa | O | BS EN 573-3, BS EN 485-2 | Plate, Sheet | |||
250.0 MPa Show Material materials with Tensile strength of 250.0 MPa | O | AA Standards, ASTM B209 | ||||
255.0 MPa Show Material materials with Tensile strength of 255.0 MPa | O | AA Standards, ASTM B209 | ||||
260.0 MPa Show Material materials with Tensile strength of 260.0 MPa | O | AA Standards, ASTM B209 | ||||
270.0 - 345.0 MPa Show Material materials with Tensile strength of 270.0 - 345.0 MPa | O | AA Standards, ASTM B209, ASTM B547 | ||||
270.0 - 350.0 MPa Show Material materials with Tensile strength of 270.0 - 350.0 MPa | O | AA Standards, ASTM B210, ASTM B221, ASTM B241, ASTM B345 | ||||
275.0 - 350.0 MPa Show Material materials with Tensile strength of 275.0 - 350.0 MPa | O | AA Standards, ASTM B209, ASTM B547 | ||||
290.0 MPa Show Material materials with Tensile strength of 290.0 MPa | O | AA Standards | ||||
0 °C | 290 MPa Show Material materials with Tensile strength of 290 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
300.0 MPa Show Material materials with Tensile strength of 300.0 MPa | O | |||||
24 °C | 290 MPa Show Material materials with Tensile strength of 290 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
100 °C | 275 MPa Show Material materials with Tensile strength of 275 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
150 °C | 215 MPa Show Material materials with Tensile strength of 215 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
205 °C | 152 MPa Show Material materials with Tensile strength of 152 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
260 °C | 117 MPa Show Material materials with Tensile strength of 117 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
315 °C | 75 MPa Show Material materials with Tensile strength of 75 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
370 °C | 40 MPa Show Material materials with Tensile strength of 40 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
Yield strength | -195 °C | 165 MPa Show Material materials with Yield strength of 165 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
-80 °C | 145 MPa Show Material materials with Yield strength of 145 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
-30 °C | 145 MPa Show Material materials with Yield strength of 145 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
100.0 MPa Show Material materials with Yield strength of 100.0 MPa | O | AA Standards, ASTM B209 | RP02 | |||
105.0 MPa Show Material materials with Yield strength of 105.0 MPa | O | AA Standards, ASTM B209 | RP02 | |||
110.0 MPa Show Material materials with Yield strength of 110.0 MPa | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345 | RP02 | |||
115.0 - 200.0 MPa Show Material materials with Yield strength of 115.0 - 200.0 MPa | O | AA Standards, ASTM B209 | RP02 | |||
115.0 MPa Show Material materials with Yield strength of 115.0 MPa | O | AA Standards, ASTM B547 | RP02 | |||
125.0 - 200.0 MPa Show Material materials with Yield strength of 125.0 - 200.0 MPa | O | AA Standards, ASTM B209 | RP02 | |||
125.0 MPa Show Material materials with Yield strength of 125.0 MPa | O | AA Standards, ASTM B547 | RP02 | |||
140.0 MPa Show Material materials with Yield strength of 140.0 MPa | O | |||||
145.0 MPa Show Material materials with Yield strength of 145.0 MPa | O | AA Standards | RP02 | |||
25 °C | 145 MPa Show Material materials with Yield strength of 145 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
100 °C | 145 MPa Show Material materials with Yield strength of 145 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
150 °C | 130 MPa Show Material materials with Yield strength of 130 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
205 °C | 115 MPa Show Material materials with Yield strength of 115 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
260 °C | 75 MPa Show Material materials with Yield strength of 75 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
315 °C | 50 MPa Show Material materials with Yield strength of 50 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 |
Thermal
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Coefficient of thermal expansion | 2.4e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.4e-05 1/K | O | ||||
20 °C | 2.38e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.38e-05 1/K | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 | |||
100 °C | 2.38e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.38e-05 1/K | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 | |||
Max service temperature | 150.0 °C Show Material materials with Max service temperature of 150.0 °C | Typical for Wrought 5000 Series Aluminium | ||||
Melting point | 570.0 °C Show Material materials with Melting point of 570.0 °C | O | BS EN 573-3, BS EN 485-2 | Plate, Sheet | ||
580.0 - 640.0 °C Show Material materials with Melting point of 580.0 - 640.0 °C | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 | ||||
580.0 °C Show Material materials with Melting point of 580.0 °C | O | |||||
Specific heat capacity | 900.0 J/(kg·K) Show Material materials with Specific heat capacity of 900.0 J/(kg·K) | O | ||||
Thermal conductivity | 117.0 W/(m·K) Show Material materials with Thermal conductivity of 117.0 W/(m·K) | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 | |||
120.0 W/(m·K) Show Material materials with Thermal conductivity of 120.0 W/(m·K) | O | |||||
121.0 W/(m·K) Show Material materials with Thermal conductivity of 121.0 W/(m·K) | O | BS EN 573-3, BS EN 485-2 | Plate, Sheet |
Electrical
Property | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|
Electrical conductivity | 17000000.0 S/m Show Material materials with Electrical conductivity of 17000000.0 S/m | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 | ||
17000000 S/m Show Material materials with Electrical conductivity of 17000000 S/m | O | Typical value | |||
Electrical resistivity | 5.8e-08 Ω·m Show Material materials with Electrical resistivity of 5.8e-08 Ω·m | O | BS EN 573-3, BS EN 485-2 | Plate, Sheet | |
5.88e-08 Ω·m Show Material materials with Electrical resistivity of 5.88e-08 Ω·m | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 | |||
6e-08 Ω·m Show Material materials with Electrical resistivity of 6e-08 Ω·m | O | Typical value | |||
Specific Electrical conductivity | 29.0 % IACS Show Material materials with Specific Electrical conductivity of 29.0 % IACS | O | Typical/Derived value |
Chemical properties
Property | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|
Aluminium | 92.4 - 95.6 % Show Material materials with Aluminium of 92.4 - 95.6 % | O | |||
Chromium | 0.05 - 0.25 % Show Material materials with Chromium of 0.05 - 0.25 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547, BS EN 573-3, BS EN 485-2 | Plate, Sheet | |
Copper | 0.1 % Show Material materials with Copper of 0.1 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547, BS EN 573-3, BS EN 485-2 | Plate, Sheet | Typical |
Iron | 0.40 % Show Material materials with Iron of 0.40 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 | ||
0.4 % Show Material materials with Iron of 0.4 % | O | BS EN 573-3, BS EN 485-2 | Plate, Sheet | ||
Magnesium | 4.0 - 4.9 % Show Material materials with Magnesium of 4.0 - 4.9 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547, BS EN 573-3, BS EN 485-2 | Plate, Sheet | |
Manganese | 0.4 - 1.0 % Show Material materials with Manganese of 0.4 - 1.0 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547, BS EN 573-3, BS EN 485-2 | Plate, Sheet | |
Other | 0.15 % Show Material materials with Other of 0.15 % | O | BS EN 573-3, BS EN 485-2 | Plate, Sheet | Total |
Silicon | 0.4 % Show Material materials with Silicon of 0.4 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547, BS EN 573-3, BS EN 485-2 | Plate, Sheet | |
Titanium | 0.05 - 0.25 % Show Material materials with Titanium of 0.05 - 0.25 % | O | BS EN 573-3, BS EN 485-2 | Plate, Sheet | |
0.15 % Show Material materials with Titanium of 0.15 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 | |||
Zinc | 0.1 % Show Material materials with Zinc of 0.1 % | O | BS EN 573-3, BS EN 485-2 | Plate, Sheet | |
0.25 % Show Material materials with Zinc of 0.25 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 |
Technological properties
Property | ||
---|---|---|
Application areas | Ship building, Rail cars, Vehicle bodies, Tip truck bodies, Mine skips and cages, Pressure vessels | |
Brazing | general: no brazing is known or developed | |
Corrosion properties | Stress corrosion cracking: kein Schadensfall im Betrieb und bei Labortests (O, H321, H116), kein Schadensfall im Betrieb, eingeschränkte Schäden bei den Labortests (H111), general: very good, without protection in industrial or seawater atmosphere | |
General machinability | General: poor | |
Soldering general | Poor | |
Welding | When welding 5083 to itself or another alloy from the same sub-group, the recommended filler metal is 5183. Other suitable fillers are 5356 and 5556. Gas: Average; Arc: Excellent; Resistance: Excellent | |
Workability | general (condition): acceptable (O), poor(H321, H116, H111) |