General
Property | Value | Condition | Related Standards |
---|---|---|---|
Density | 2.66 g/cm³ Show Material materials with Density of 2.66 g/cm³ | H111 | AA Standards, ASTM B221, ASTM B241, ASTM B345 |
2.7 g/cm³ Show Material materials with Density of 2.7 g/cm³ | H111 |
Mechanical
Property | Value | Condition | Related Standards | Comment |
---|---|---|---|---|
Elastic modulus | 71.0 GPa Show Material materials with Elastic modulus of 71.0 GPa | H111 | AA Standards, ASTM B221, ASTM B241, ASTM B345 | |
Elongation | 10.0 % Show Material materials with Elongation of 10.0 % | H111 | AA Standards, ASTM B221, ASTM B241, ASTM B345 | A100 |
12.0 % Show Material materials with Elongation of 12.0 % | H111 | AA Standards, ASTM B221, ASTM B241, ASTM B345 | A50 | |
16.0 % Show Material materials with Elongation of 16.0 % | H111 | |||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||
Shear modulus | 26.0 - 26.5 GPa Show Material materials with Shear modulus of 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | ||
Tensile strength | 250.0 MPa Show Material materials with Tensile strength of 250.0 MPa | H111 | AA Standards, ASTM B221, ASTM B241, ASTM B345 | |
270.0 MPa Show Material materials with Tensile strength of 270.0 MPa | H111 | |||
Yield strength | 130.0 MPa Show Material materials with Yield strength of 130.0 MPa | H111 | ||
145.0 MPa Show Material materials with Yield strength of 145.0 MPa | H111 | AA Standards, ASTM B221, ASTM B241, ASTM B345 | RP02 |
Thermal
Property | Temperature | Value | Condition | Related Standards | Comment |
---|---|---|---|---|---|
Coefficient of thermal expansion | 2.4e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.4e-05 1/K | H111 | |||
20 °C | 2.38e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.38e-05 1/K | H111 | AA Standards, ASTM B221, ASTM B241, ASTM B345 | ||
100 °C | 2.38e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.38e-05 1/K | H111 | AA Standards, ASTM B221, ASTM B241, ASTM B345 | ||
Max service temperature | 150.0 °C Show Material materials with Max service temperature of 150.0 °C | Typical for Wrought 5000 Series Aluminium | |||
Melting point | 585.0 - 640.0 °C Show Material materials with Melting point of 585.0 - 640.0 °C | H111 | AA Standards, ASTM B221, ASTM B241, ASTM B345 | ||
590.0 °C Show Material materials with Melting point of 590.0 °C | H111 | ||||
Specific heat capacity | 900.0 J/(kg·K) Show Material materials with Specific heat capacity of 900.0 J/(kg·K) | H111 | |||
Thermal conductivity | 126 W/(m·K) Show Material materials with Thermal conductivity of 126 W/(m·K) | H111 | AA Standards, ASTM B221, ASTM B241, ASTM B345 | ||
130.0 W/(m·K) Show Material materials with Thermal conductivity of 130.0 W/(m·K) | H111 |
Electrical
Property | Value | Condition | Related Standards |
---|---|---|---|
Electrical conductivity | 18000000.0 S/m Show Material materials with Electrical conductivity of 18000000.0 S/m | H111 | AA Standards, ASTM B221, ASTM B241, ASTM B345 |
Electrical resistivity | 5.56e-08 Ω·m Show Material materials with Electrical resistivity of 5.56e-08 Ω·m | H111 | AA Standards, ASTM B221, ASTM B241, ASTM B345 |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Aluminium | 93.0 - 96.3 % Show Material materials with Aluminium of 93.0 - 96.3 % | H111 | |
Chromium | 0.05 - 0.25 % Show Material materials with Chromium of 0.05 - 0.25 % | H111 | AA Standards, ASTM B221, ASTM B241, ASTM B345 |
Copper | 0.1 % Show Material materials with Copper of 0.1 % | H111 | AA Standards, ASTM B221, ASTM B241, ASTM B345 |
Iron | 0.50 % Show Material materials with Iron of 0.50 % | H111 | AA Standards, ASTM B221, ASTM B241, ASTM B345 |
0.5 % Show Material materials with Iron of 0.5 % | H111 | ||
Magnesium | 3.5 - 4.5 % Show Material materials with Magnesium of 3.5 - 4.5 % | H111 | AA Standards, ASTM B221, ASTM B241, ASTM B345 |
Manganese | 0.2 - 0.7 % Show Material materials with Manganese of 0.2 - 0.7 % | H111 | AA Standards, ASTM B221, ASTM B241, ASTM B345 |
Other | 0.15 % Show Material materials with Other of 0.15 % | H111 | |
Silicon | 0.4 % Show Material materials with Silicon of 0.4 % | H111 | AA Standards, ASTM B221, ASTM B241, ASTM B345 |
Titanium | 0.15 % Show Material materials with Titanium of 0.15 % | H111 | AA Standards, ASTM B221, ASTM B241, ASTM B345 |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | H111 | AA Standards, ASTM B221, ASTM B241, ASTM B345 |
Technological properties
Property | ||
---|---|---|
Brazing | general: no brazing is known or developed | |
Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests (O, H32, H116, H111), no damage during operation, limited damage during laboratory tests (H34, H36, H38), general: very good, without protection in industrial or seawater atmosphere | |
General machinability | General: poor (O, H32, H116, H111), sufficient (H34, H36, H38) | |
Workability | general (condition): good (O), acceptable (H32, H116, H111), poor(H36, H38) |