AA Standards Grade 5154 H112

Want to keep this datasheet? Save it now in your required format

Description

Related Standards

Equivalent Materials

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

Density

ρ

2.66 - 2.7 g/cm³ at 23 °C

Dimension

Dimensions

Dicke

Mechanical

Bending Fatigue Strength

SNf

115 MPa at 23 °C

Show 5000 Series materials with Bending Fatigue Strength of 115 MPa at 23 °C

Compressive modulus

Ecomp

70.7 MPa at 23 °C

Show 5000 Series materials with Compressive modulus of 70.7 MPa at 23 °C

Elastic modulus

E

70 GPa at 23 °C

Show 5000 Series materials with Elastic modulus of 70 GPa at 23 °C

Elongation

A

20 - 25 % at 23 °C

Show 5000 Series materials with Elongation of 20 - 25 % at 23 °C

Elongation A100

A100

9 - 13 % at 23 °C

Show 5000 Series materials with Elongation A100 of 9 - 13 % at 23 °C

Elongation A50

A50

8 - 25 % at 23 °C

Show 5000 Series materials with Elongation A50 of 8 - 25 % at 23 °C

Fatigue strength

SNf

117 MPa at 23 °C

Show 5000 Series materials with Fatigue strength of 117 MPa at 23 °C

for 5x10⁸ cycles

Hardness, Brinell

HB

63 [-] at 23 °C

Show 5000 Series materials with Hardness, Brinell of 63 [-] at 23 °C

500 kg load, 10 mm ball

Plane-Strain Fracture Toughnes

KIC

22 - 35 MPa·√m at 23 °C

Show 5000 Series materials with Plane-Strain Fracture Toughnes of 22 - 35 MPa·√m at 23 °C

Typical for Wrought 5000 Series Aluminium

Poisson's ratio

ν

0.33 [-] at 23 °C

Show 5000 Series materials with Poisson's ratio of 0.33 [-] at 23 °C

Typical for Wrought 5000 Series Aluminium

Shear modulus

G

25.9 GPa at 23 °C

Show 5000 Series materials with Shear modulus of 25.9 GPa at 23 °C

Tensile strength

Rm

205 - 240 MPa at 23 °C

Show 5000 Series materials with Tensile strength of 205 - 240 MPa at 23 °C

Yield strength

YS

110 MPa at 23 °C

Show 5000 Series materials with Yield strength of 110 MPa at 23 °C

Yield strength Rp0.2

Rp0.2

75 - 125 MPa at 23 °C

Show 5000 Series materials with Yield strength Rp0.2 of 75 - 125 MPa at 23 °C

Thermal

Coefficient of thermal expansion

α

2.39E-5 1/K at 20 °C

Hide chart

Max service temperature

Tmax

150 °C

Typical for Wrought 5000 Series Aluminium

Melting point

Tm

590 - 645 °C

Specific heat capacity

cp

900 J/(kg·K) at 23 °C

Thermal conductivity

λ

126 - 130 W/(m·K) at 23 °C

Electrical

Electrical conductivity

σel

1.90E+7 S/m at 23 °C

Electrical resistivity

ρel

5.26E-8 Ω·m at 23 °C

Chemical properties

Element

Weight %

Comment

Al

94.4 - 96.8 %

Mg

3.1 - 3.9 %

Cr

0.15 - 0.35 %

Cu

0 - 0.1 %

Fe

0 - 0.4 %

More

Technological properties

Brazing

general: no brazing is known or developed

Corrosion properties

Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere

General machinability

General: poor (O, H32), sufficient (H34, H36, H38)

Workability

general (condition): good (O), acceptable (H32, H34), poor(H36, H38)

This material data has been provided by MakeItFrom.com,ASM Handbook Volume 2 Properties and Selection: Nonferrous Alloys and Special-Purpose Materials,AluKey.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.