AA Standards Grade 5454 H111

Want to keep this datasheet? Save it now in your required format

Related Standards

Equivalent Materials

This material data has been provided by AluKey,MakeItFrom.com,ASM Handbook Volume 2 Properties and Selection: Nonferrous Alloys and Special-Purpose Materials.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueCondition

Density

2.7 g/cm³

Show Material materials with Density of 2.7 g/cm³

H111

2.69 g/cm³

Show Material materials with Density of 2.69 g/cm³

H111

Mechanical

PropertyValueConditionRelated StandardsComment

Compressive modulus

71.0 MPa

Show Material materials with Compressive modulus of 71.0 MPa

H111

Elastic modulus

71.0 GPa

Show Material materials with Elastic modulus of 71.0 GPa

H111

70 GPa

Show Material materials with Elastic modulus of 70 GPa

H111

Elongation

14.0 %

Show Material materials with Elongation of 14.0 %

H111

AA Standards

A50

12.0 %

Show Material materials with Elongation of 12.0 %

H111

AA Standards, ASTM B221, ASTM B241

A50

10.0 %

Show Material materials with Elongation of 10.0 %

H111

AA Standards, ASTM B221, ASTM B241

A100

15.0 %

Show Material materials with Elongation of 15.0 %

H111

14 %

Show Material materials with Elongation of 14 %

H111

Hardness, Brinell

70.0 [-]

Show Material materials with Hardness, Brinell of 70.0 [-]

H111

AA Standards

70.0 [-]

Show Material materials with Hardness, Brinell of 70.0 [-]

H111

500 kg load, 10 mm ball

Plane-Strain Fracture Toughnes

22.0 - 35.0 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m

Typical for Wrought 5000 Series Aluminium

Poisson's ratio

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-]

Typical for Wrought 5000 Series Aluminium

Shear modulus

26.0 - 26.5 GPa

Show Material materials with Shear modulus of 26.0 - 26.5 GPa

Typical for Wrought 5000 Series Aluminium

Shear strength

159.0 MPa

Show Material materials with Shear strength of 159.0 MPa

H111

Tensile strength

260.0 MPa

Show Material materials with Tensile strength of 260.0 MPa

H111

AA Standards

230.0 MPa

Show Material materials with Tensile strength of 230.0 MPa

H111

AA Standards, ASTM B221, ASTM B241

250.0 MPa

Show Material materials with Tensile strength of 250.0 MPa

H111

260 MPa

Show Material materials with Tensile strength of 260 MPa

H111

Yield strength

180.0 MPa

Show Material materials with Yield strength of 180.0 MPa

H111

AA Standards

RP02

130.0 MPa

Show Material materials with Yield strength of 130.0 MPa

H111

AA Standards, ASTM B221, ASTM B241

RP02

180 MPa

Show Material materials with Yield strength of 180 MPa

H111

RP02

140.0 MPa

Show Material materials with Yield strength of 140.0 MPa

H111

Thermal

PropertyValueConditionComment

Coefficient of thermal expansion

2.4e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.4e-05 1/K

H111

Max service temperature

150.0 °C

Show Material materials with Max service temperature of 150.0 °C

Typical for Wrought 5000 Series Aluminium

Melting point

600.0 °C

Show Material materials with Melting point of 600.0 °C

H111

Specific heat capacity

900.0 J/(kg·K)

Show Material materials with Specific heat capacity of 900.0 J/(kg·K)

H111

Thermal conductivity

130.0 W/(m·K)

Show Material materials with Thermal conductivity of 130.0 W/(m·K)

H111

Electrical

PropertyValueComment

Electrical conductivity

18000000.0 - 31000000.0 S/m

Show Material materials with Electrical conductivity of 18000000.0 - 31000000.0 S/m

Typical for Wrought 5000 Series Aluminium

Electrical resistivity

3.3e-08 - 5e-08 Ω·m

Show Material materials with Electrical resistivity of 3.3e-08 - 5e-08 Ω·m

Typical for Wrought 5000 Series Aluminium

Chemical properties

PropertyValueConditionRelated Standards

Aluminium

94.5 - 97.1 %

Show Material materials with Aluminium of 94.5 - 97.1 %

H111

Chromium

0.05 - 0.2 %

Show Material materials with Chromium of 0.05 - 0.2 %

H111

AA Standards, ASTM B221, ASTM B241

Copper

0.1 %

Show Material materials with Copper of 0.1 %

H111

AA Standards, ASTM B221, ASTM B241

Iron

0.40 %

Show Material materials with Iron of 0.40 %

H111

AA Standards, ASTM B221, ASTM B241

0.4 %

Show Material materials with Iron of 0.4 %

H111

Magnesium

2.4 - 3.0 %

Show Material materials with Magnesium of 2.4 - 3.0 %

H111

AA Standards, ASTM B221, ASTM B241

Manganese

0.5 - 1.0 %

Show Material materials with Manganese of 0.5 - 1.0 %

H111

AA Standards, ASTM B221, ASTM B241

Other

0.15 %

Show Material materials with Other of 0.15 %

H111

Silicon

0.25 %

Show Material materials with Silicon of 0.25 %

H111

AA Standards, ASTM B221, ASTM B241

Titanium

0.2 %

Show Material materials with Titanium of 0.2 %

H111

AA Standards, ASTM B221, ASTM B241

Zinc

0.25 %

Show Material materials with Zinc of 0.25 %

H111

AA Standards, ASTM B221, ASTM B241

Technological properties

Property
Brazing

general: no brazing is known or developed

Corrosion properties

Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere

General machinability

General: poor (O, H32, H111), sufficient (H34)

Workability

general (condition): good (O), acceptable (H32, H34, H111)