AA Standards Grade 5454 H112

Want to keep this datasheet? Save it now in your required format

Related Standards

Equivalent Materials

This material data has been provided by AluKey,MakeItFrom.com,ASM Handbook Volume 2 Properties and Selection: Nonferrous Alloys and Special-Purpose Materials.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueCondition

Density

2.69 g/cm³

Show Material materials with Density of 2.69 g/cm³

H112

2.7 g/cm³

Show Material materials with Density of 2.7 g/cm³

H112

Mechanical

PropertyValueConditionRelated StandardsComment

Compressive modulus

71.0 MPa

Show Material materials with Compressive modulus of 71.0 MPa

H112

Elastic modulus

70 GPa

Show Material materials with Elastic modulus of 70 GPa

H112

71.0 GPa

Show Material materials with Elastic modulus of 71.0 GPa

H112

Elongation

8.0 %

Show Material materials with Elongation of 8.0 %

H112

AA Standards, ASTM B209, ASTM B547

A50

9.0 %

Show Material materials with Elongation of 9.0 %

H112

AA Standards, ASTM B209

A100

10.0 %

Show Material materials with Elongation of 10.0 %

H112

AA Standards, ASTM B221, ASTM B241

A100

12.0 %

Show Material materials with Elongation of 12.0 %

H112

AA Standards, ASTM B221, ASTM B241

A50

13.0 %

Show Material materials with Elongation of 13.0 %

H112

AA Standards, ASTM B209

A100

14.0 %

Show Material materials with Elongation of 14.0 %

H112

18.0 %

Show Material materials with Elongation of 18.0 %

H112

AA Standards

A50

18 %

Show Material materials with Elongation of 18 %

H112

Hardness, Brinell

62.0 [-]

Show Material materials with Hardness, Brinell of 62.0 [-]

H112

AA Standards

62.0 [-]

Show Material materials with Hardness, Brinell of 62.0 [-]

H112

500 kg load, 10 mm ball

Plane-Strain Fracture Toughnes

22.0 - 35.0 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m

Typical for Wrought 5000 Series Aluminium

Poisson's ratio

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-]

Typical for Wrought 5000 Series Aluminium

Shear modulus

26.0 - 26.5 GPa

Show Material materials with Shear modulus of 26.0 - 26.5 GPa

Typical for Wrought 5000 Series Aluminium

Shear strength

159.0 MPa

Show Material materials with Shear strength of 159.0 MPa

H112

Tensile strength

215.0 MPa

Show Material materials with Tensile strength of 215.0 MPa

H112

AA Standards, ASTM B209, ASTM B221, ASTM B241

220.0 MPa

Show Material materials with Tensile strength of 220.0 MPa

H112

AA Standards, ASTM B209, ASTM B547

250.0 MPa

Show Material materials with Tensile strength of 250.0 MPa

H112

AA Standards

250 MPa

Show Material materials with Tensile strength of 250 MPa

H112

Yield strength

85.0 MPa

Show Material materials with Yield strength of 85.0 MPa

H112

AA Standards, ASTM B209, ASTM B221, ASTM B241

RP02

110.0 MPa

Show Material materials with Yield strength of 110.0 MPa

H112

125.0 MPa

Show Material materials with Yield strength of 125.0 MPa

H112

AA Standards, ASTM B209, ASTM B547

RP02

125 MPa

Show Material materials with Yield strength of 125 MPa

H112

RP02

Thermal

PropertyValueConditionComment

Coefficient of thermal expansion

2.4e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.4e-05 1/K

H112

Max service temperature

150.0 °C

Show Material materials with Max service temperature of 150.0 °C

Typical for Wrought 5000 Series Aluminium

Melting point

600.0 °C

Show Material materials with Melting point of 600.0 °C

H112

Specific heat capacity

900.0 J/(kg·K)

Show Material materials with Specific heat capacity of 900.0 J/(kg·K)

H112

Thermal conductivity

130.0 W/(m·K)

Show Material materials with Thermal conductivity of 130.0 W/(m·K)

H112

Electrical

PropertyValueComment

Electrical conductivity

18000000.0 - 31000000.0 S/m

Show Material materials with Electrical conductivity of 18000000.0 - 31000000.0 S/m

Typical for Wrought 5000 Series Aluminium

Electrical resistivity

3.3e-08 - 5e-08 Ω·m

Show Material materials with Electrical resistivity of 3.3e-08 - 5e-08 Ω·m

Typical for Wrought 5000 Series Aluminium

Chemical properties

PropertyValueConditionRelated Standards

Aluminium

94.5 - 97.1 %

Show Material materials with Aluminium of 94.5 - 97.1 %

H112

Chromium

0.05 - 0.2 %

Show Material materials with Chromium of 0.05 - 0.2 %

H112

AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547

Copper

0.1 %

Show Material materials with Copper of 0.1 %

H112

AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547

Iron

0.40 %

Show Material materials with Iron of 0.40 %

H112

AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547

0.4 %

Show Material materials with Iron of 0.4 %

H112

Magnesium

2.4 - 3.0 %

Show Material materials with Magnesium of 2.4 - 3.0 %

H112

AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547

Manganese

0.5 - 1.0 %

Show Material materials with Manganese of 0.5 - 1.0 %

H112

AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547

Other

0.15 %

Show Material materials with Other of 0.15 %

H112

Silicon

0.25 %

Show Material materials with Silicon of 0.25 %

H112

AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547

Titanium

0.2 %

Show Material materials with Titanium of 0.2 %

H112

AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547

Zinc

0.25 %

Show Material materials with Zinc of 0.25 %

H112

AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B547

Technological properties

Property
Brazing

general: no brazing is known or developed

Corrosion properties

Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere

General machinability

General: poor (O, H32, H111), sufficient (H34)

Workability

general (condition): good (O), acceptable (H32, H34, H111)