AA Standards Grade 5454 H32

Want to keep this datasheet? Save it now in your required format

Related Standards

Equivalent Materials

This material data has been provided by AluKey,MakeItFrom.com,ASM Handbook Volume 2 Properties and Selection: Nonferrous Alloys and Special-Purpose Materials.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueCondition

Density

2.7 g/cm³

Show Material materials with Density of 2.7 g/cm³

H32

2.69 g/cm³

Show Material materials with Density of 2.69 g/cm³

H32

Mechanical

PropertyTemperatureValueConditionRelated StandardsComment

Compressive modulus

71.0 MPa

Show Material materials with Compressive modulus of 71.0 MPa

H32

Elastic modulus

71.0 GPa

Show Material materials with Elastic modulus of 71.0 GPa

H32

70 GPa

Show Material materials with Elastic modulus of 70 GPa

H32

Elongation

10.0 %

Show Material materials with Elongation of 10.0 %

H32

AA Standards

A50

8.0 %

Show Material materials with Elongation of 8.0 %

H32

AA Standards, ASTM B209, ASTM B547

A50

6.0 %

Show Material materials with Elongation of 6.0 %

H32

AA Standards, ASTM B209

A50

12.0 %

Show Material materials with Elongation of 12.0 %

H32

AA Standards, ASTM B209, ASTM B547

A50

5.0 %

Show Material materials with Elongation of 5.0 %

H32

AA Standards, ASTM B209

A50

10.0 %

Show Material materials with Elongation of 10.0 %

H32

AA Standards, ASTM B209

A100

5.0 %

Show Material materials with Elongation of 5.0 %

H32

AA Standards, ASTM B234

A100

8.0 %

Show Material materials with Elongation of 8.0 %

H32

AA Standards, ASTM B234

A100

7.9 %

Show Material materials with Elongation of 7.9 %

H32

370 °C

130 %

Show Material materials with Elongation of 130 %

H32

Elongation in 50 mm

315 °C

110 %

Show Material materials with Elongation of 110 %

H32

Elongation in 50 mm

260 °C

80 %

Show Material materials with Elongation of 80 %

H32

Elongation in 50 mm

205 °C

45 %

Show Material materials with Elongation of 45 %

H32

Elongation in 50 mm

150 °C

37 %

Show Material materials with Elongation of 37 %

H32

Elongation in 50 mm

100 °C, 0 °C

20 %

Show Material materials with Elongation of 20 %

H32

Elongation in 50 mm

24 °C

18 %

Show Material materials with Elongation of 18 %

H32

Elongation in 50 mm

-80 °C

23 %

Show Material materials with Elongation of 23 %

H32

Elongation in 50 mm

-195 °C

32 %

Show Material materials with Elongation of 32 %

H32

Elongation in 50 mm

Hardness, Brinell

73.0 [-]

Show Material materials with Hardness, Brinell of 73.0 [-]

H32

AA Standards

73.0 [-]

Show Material materials with Hardness, Brinell of 73.0 [-]

H32

500 kg load, 10 mm ball

Plane-Strain Fracture Toughnes

22.0 - 35.0 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m

Typical for Wrought 5000 Series Aluminium

Poisson's ratio

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-]

Typical for Wrought 5000 Series Aluminium

Shear modulus

26.0 - 26.5 GPa

Show Material materials with Shear modulus of 26.0 - 26.5 GPa

Typical for Wrought 5000 Series Aluminium

Shear strength

165.0 MPa

Show Material materials with Shear strength of 165.0 MPa

H32

Tensile strength

275.0 MPa

Show Material materials with Tensile strength of 275.0 MPa

H32

AA Standards

250.0 - 305.0 MPa

Show Material materials with Tensile strength of 250.0 - 305.0 MPa

H32

AA Standards, ASTM B209, ASTM B547

250.0 MPa

Show Material materials with Tensile strength of 250.0 MPa

H32

AA Standards, ASTM B234

270.0 MPa

Show Material materials with Tensile strength of 270.0 MPa

H32

370 °C

40 MPa

Show Material materials with Tensile strength of 40 MPa

H32

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

315 °C

75 MPa

Show Material materials with Tensile strength of 75 MPa

H32

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

260 °C

117 MPa

Show Material materials with Tensile strength of 117 MPa

H32

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

205 °C

172 MPa

Show Material materials with Tensile strength of 172 MPa

H32

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

150 °C

220 MPa

Show Material materials with Tensile strength of 220 MPa

H32

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

100 °C

270 MPa

Show Material materials with Tensile strength of 270 MPa

H32

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

24 °C

275 MPa

Show Material materials with Tensile strength of 275 MPa

H32

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

0 °C

283 MPa

Show Material materials with Tensile strength of 283 MPa

H32

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

-80 °C

290 MPa

Show Material materials with Tensile strength of 290 MPa

H32

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

-195 °C

407 MPa

Show Material materials with Tensile strength of 407 MPa

H32

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

Unlock all property charts

Yield strength

205.0 MPa

Show Material materials with Yield strength of 205.0 MPa

H32

AA Standards

RP02

180.0 MPa

Show Material materials with Yield strength of 180.0 MPa

H32

AA Standards, ASTM B209, ASTM B234, ASTM B547

RP02

371 °C

29 MPa

Show Material materials with Yield strength of 29 MPa

H32

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

316 °C

50 MPa

Show Material materials with Yield strength of 50 MPa

H32

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

260 °C

75 MPa

Show Material materials with Yield strength of 75 MPa

H32

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

204 °C

130 MPa

Show Material materials with Yield strength of 130 MPa

H32

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

149 °C

180 MPa

Show Material materials with Yield strength of 180 MPa

H32

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

100 °C

200 MPa

Show Material materials with Yield strength of 200 MPa

H32

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

24 °C, -28 °C

205 MPa

Show Material materials with Yield strength of 205 MPa

H32

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

-80 °C

215 MPa

Show Material materials with Yield strength of 215 MPa

H32

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

-196 °C

250 MPa

Show Material materials with Yield strength of 250 MPa

H32

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

210.0 MPa

Show Material materials with Yield strength of 210.0 MPa

H32

Unlock all property charts

Thermal

PropertyValueConditionComment

Coefficient of thermal expansion

2.4e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.4e-05 1/K

H32

Max service temperature

150.0 °C

Show Material materials with Max service temperature of 150.0 °C

Typical for Wrought 5000 Series Aluminium

Melting point

600.0 °C

Show Material materials with Melting point of 600.0 °C

H32

Specific heat capacity

900.0 J/(kg·K)

Show Material materials with Specific heat capacity of 900.0 J/(kg·K)

H32

Thermal conductivity

130.0 W/(m·K)

Show Material materials with Thermal conductivity of 130.0 W/(m·K)

H32

Electrical

PropertyValueComment

Electrical conductivity

18000000.0 - 31000000.0 S/m

Show Material materials with Electrical conductivity of 18000000.0 - 31000000.0 S/m

Typical for Wrought 5000 Series Aluminium

Electrical resistivity

3.3e-08 - 5e-08 Ω·m

Show Material materials with Electrical resistivity of 3.3e-08 - 5e-08 Ω·m

Typical for Wrought 5000 Series Aluminium

Chemical properties

PropertyValueConditionRelated Standards

Aluminium

94.5 - 97.1 %

Show Material materials with Aluminium of 94.5 - 97.1 %

H32

Chromium

0.05 - 0.2 %

Show Material materials with Chromium of 0.05 - 0.2 %

H32

AA Standards, ASTM B209, ASTM B234, ASTM B547

Copper

0.1 %

Show Material materials with Copper of 0.1 %

H32

AA Standards, ASTM B209, ASTM B234, ASTM B547

Iron

0.40 %

Show Material materials with Iron of 0.40 %

H32

AA Standards, ASTM B209, ASTM B234, ASTM B547

0.4 %

Show Material materials with Iron of 0.4 %

H32

Magnesium

2.4 - 3.0 %

Show Material materials with Magnesium of 2.4 - 3.0 %

H32

AA Standards, ASTM B209, ASTM B234, ASTM B547

Manganese

0.5 - 1.0 %

Show Material materials with Manganese of 0.5 - 1.0 %

H32

AA Standards, ASTM B209, ASTM B234, ASTM B547

Other

0.15 %

Show Material materials with Other of 0.15 %

H32

Silicon

0.25 %

Show Material materials with Silicon of 0.25 %

H32

AA Standards, ASTM B209, ASTM B234, ASTM B547

Titanium

0.2 %

Show Material materials with Titanium of 0.2 %

H32

AA Standards, ASTM B209, ASTM B234, ASTM B547

Zinc

0.25 %

Show Material materials with Zinc of 0.25 %

H32

AA Standards, ASTM B209, ASTM B234, ASTM B547

Technological properties

Property
Brazing

general: no brazing is known or developed

Corrosion properties

Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere

General machinability

General: poor (O, H32, H111), sufficient (H34)

Workability

general (condition): good (O), acceptable (H32, H34, H111)