AA Standards Grade 5454 H34

Want to keep this datasheet? Save it now in your required format

Related Standards

Equivalent Materials

This material data has been provided by AluKey,MakeItFrom.com,ASM Handbook Volume 2 Properties and Selection: Nonferrous Alloys and Special-Purpose Materials.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueCondition

Density

2.7 g/cm³

Show Material materials with Density of 2.7 g/cm³

H34

2.69 g/cm³

Show Material materials with Density of 2.69 g/cm³

H34

Mechanical

PropertyTemperatureValueConditionRelated StandardsComment

Compressive modulus

71.0 MPa

Show Material materials with Compressive modulus of 71.0 MPa

H34

Elastic modulus

71.0 GPa

Show Material materials with Elastic modulus of 71.0 GPa

H34

70 GPa

Show Material materials with Elastic modulus of 70 GPa

H34

Elongation

10.0 %

Show Material materials with Elongation of 10.0 %

H34

AA Standards, ASTM B209, ASTM B547

A50

4.0 %

Show Material materials with Elongation of 4.0 %

H34

AA Standards, ASTM B209

A50

6.0 %

Show Material materials with Elongation of 6.0 %

H34

AA Standards, ASTM B209, ASTM B547

A50

5.0 %

Show Material materials with Elongation of 5.0 %

H34

AA Standards, ASTM B209

A50

9.0 %

Show Material materials with Elongation of 9.0 %

H34

AA Standards, ASTM B209

A100

4.0 %

Show Material materials with Elongation of 4.0 %

H34

AA Standards, ASTM B234

A100

6.0 %

Show Material materials with Elongation of 6.0 %

H34

AA Standards, ASTM B234

A100

7.3 %

Show Material materials with Elongation of 7.3 %

H34

370 °C

130 %

Show Material materials with Elongation of 130 %

H34

Elongation in 50 mm

315 °C

110 %

Show Material materials with Elongation of 110 %

H34

Elongation in 50 mm

260 °C

80 %

Show Material materials with Elongation of 80 %

H34

Elongation in 50 mm

205 °C

45 %

Show Material materials with Elongation of 45 %

H34

Elongation in 50 mm

150 °C

32 %

Show Material materials with Elongation of 32 %

H34

Elongation in 50 mm

100 °C, 0 °C

18 %

Show Material materials with Elongation of 18 %

H34

Elongation in 50 mm

24 °C

16 %

Show Material materials with Elongation of 16 %

H34

Elongation in 50 mm

-80 °C

21 %

Show Material materials with Elongation of 21 %

H34

Elongation in 50 mm

-195 °C

30 %

Show Material materials with Elongation of 30 %

H34

Elongation in 50 mm

Hardness, Brinell

81.0 [-]

Show Material materials with Hardness, Brinell of 81.0 [-]

H34

AA Standards

81.0 [-]

Show Material materials with Hardness, Brinell of 81.0 [-]

H34

500 kg load, 10 mm ball

Plane-Strain Fracture Toughnes

22.0 - 35.0 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m

Typical for Wrought 5000 Series Aluminium

Poisson's ratio

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-]

Typical for Wrought 5000 Series Aluminium

Shear modulus

26.0 - 26.5 GPa

Show Material materials with Shear modulus of 26.0 - 26.5 GPa

Typical for Wrought 5000 Series Aluminium

Shear strength

179.0 MPa

Show Material materials with Shear strength of 179.0 MPa

H34

Tensile strength

305.0 MPa

Show Material materials with Tensile strength of 305.0 MPa

H34

AA Standards

270.0 - 325.0 MPa

Show Material materials with Tensile strength of 270.0 - 325.0 MPa

H34

AA Standards, ASTM B209, ASTM B547

270.0 MPa

Show Material materials with Tensile strength of 270.0 MPa

H34

AA Standards, ASTM B234

300.0 MPa

Show Material materials with Tensile strength of 300.0 MPa

H34

370 °C

40 MPa

Show Material materials with Tensile strength of 40 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

315 °C

74 MPa

Show Material materials with Tensile strength of 74 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

260 °C

117 MPa

Show Material materials with Tensile strength of 117 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

205 °C

180 MPa

Show Material materials with Tensile strength of 180 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

150 °C

235 MPa

Show Material materials with Tensile strength of 235 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

100 °C

295 MPa

Show Material materials with Tensile strength of 295 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

24 °C, 0 °C

303 MPa

Show Material materials with Tensile strength of 303 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

-80 °C

317 MPa

Show Material materials with Tensile strength of 317 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

-195 °C

435 MPa

Show Material materials with Tensile strength of 435 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

Unlock all property charts

Yield strength

240.0 MPa

Show Material materials with Yield strength of 240.0 MPa

H34

AA Standards

RP02

200.0 MPa

Show Material materials with Yield strength of 200.0 MPa

H34

AA Standards, ASTM B209, ASTM B234, ASTM B547

RP02

371 °C

29 MPa

Show Material materials with Yield strength of 29 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

316 °C

50 MPa

Show Material materials with Yield strength of 50 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

260 °C

75 MPa

Show Material materials with Yield strength of 75 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

204 °C

130 MPa

Show Material materials with Yield strength of 130 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

149 °C

195 MPa

Show Material materials with Yield strength of 195 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

100 °C

235 MPa

Show Material materials with Yield strength of 235 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

24 °C, -28 °C

240 MPa

Show Material materials with Yield strength of 240 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

-80 °C

250 MPa

Show Material materials with Yield strength of 250 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

-196 °C

285 MPa

Show Material materials with Yield strength of 285 MPa

H34

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

240.0 MPa

Show Material materials with Yield strength of 240.0 MPa

H34

Unlock all property charts

Thermal

PropertyValueConditionComment

Coefficient of thermal expansion

2.4e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.4e-05 1/K

H34

Max service temperature

150.0 °C

Show Material materials with Max service temperature of 150.0 °C

Typical for Wrought 5000 Series Aluminium

Melting point

600.0 °C

Show Material materials with Melting point of 600.0 °C

H34

Specific heat capacity

900.0 J/(kg·K)

Show Material materials with Specific heat capacity of 900.0 J/(kg·K)

H34

Thermal conductivity

130.0 W/(m·K)

Show Material materials with Thermal conductivity of 130.0 W/(m·K)

H34

Electrical

PropertyValueComment

Electrical conductivity

18000000.0 - 31000000.0 S/m

Show Material materials with Electrical conductivity of 18000000.0 - 31000000.0 S/m

Typical for Wrought 5000 Series Aluminium

Electrical resistivity

3.3e-08 - 5e-08 Ω·m

Show Material materials with Electrical resistivity of 3.3e-08 - 5e-08 Ω·m

Typical for Wrought 5000 Series Aluminium

Chemical properties

PropertyValueConditionRelated Standards

Aluminium

94.5 - 97.1 %

Show Material materials with Aluminium of 94.5 - 97.1 %

H34

Chromium

0.05 - 0.2 %

Show Material materials with Chromium of 0.05 - 0.2 %

H34

AA Standards, ASTM B209, ASTM B234, ASTM B547

Copper

0.1 %

Show Material materials with Copper of 0.1 %

H34

AA Standards, ASTM B209, ASTM B234, ASTM B547

Iron

0.40 %

Show Material materials with Iron of 0.40 %

H34

AA Standards, ASTM B209, ASTM B234, ASTM B547

0.4 %

Show Material materials with Iron of 0.4 %

H34

Magnesium

2.4 - 3.0 %

Show Material materials with Magnesium of 2.4 - 3.0 %

H34

AA Standards, ASTM B209, ASTM B234, ASTM B547

Manganese

0.5 - 1.0 %

Show Material materials with Manganese of 0.5 - 1.0 %

H34

AA Standards, ASTM B209, ASTM B234, ASTM B547

Other

0.15 %

Show Material materials with Other of 0.15 %

H34

Silicon

0.25 %

Show Material materials with Silicon of 0.25 %

H34

AA Standards, ASTM B209, ASTM B234, ASTM B547

Titanium

0.2 %

Show Material materials with Titanium of 0.2 %

H34

AA Standards, ASTM B209, ASTM B234, ASTM B547

Zinc

0.25 %

Show Material materials with Zinc of 0.25 %

H34

AA Standards, ASTM B209, ASTM B234, ASTM B547

Technological properties

Property
Brazing

general: no brazing is known or developed

Corrosion properties

Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere

General machinability

General: poor (O, H32, H111), sufficient (H34)

Workability

general (condition): good (O), acceptable (H32, H34, H111)