Properties
General
| Property | Value | Condition |
|---|---|---|
Density | 2.7 g/cm³ Show Material materials with Density of 2.7 g/cm³ | H38 |
2.69 g/cm³ Show Material materials with Density of 2.69 g/cm³ | H38 |
Mechanical
| Property | Value | Condition | Comment |
|---|---|---|---|
Compressive modulus | 71.0 MPa Show Material materials with Compressive modulus of 71.0 MPa | H38 | |
Elastic modulus | 71.0 GPa Show Material materials with Elastic modulus of 71.0 GPa | H38 | |
Elongation | 3.5 % Show Material materials with Elongation of 3.5 % | H38 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | |
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | |
Shear modulus | 26.0 - 26.5 GPa Show Material materials with Shear modulus of 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | |
Tensile strength | 360.0 MPa Show Material materials with Tensile strength of 360.0 MPa | H38 | |
Yield strength | 290.0 MPa Show Material materials with Yield strength of 290.0 MPa | H38 |
Thermal
| Property | Value | Condition | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 2.4e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.4e-05 1/K | H38 | |
Max service temperature | 150.0 °C Show Material materials with Max service temperature of 150.0 °C | Typical for Wrought 5000 Series Aluminium | |
Melting point | 600.0 °C Show Material materials with Melting point of 600.0 °C | H38 | |
Specific heat capacity | 900.0 J/(kg·K) Show Material materials with Specific heat capacity of 900.0 J/(kg·K) | H38 | |
Thermal conductivity | 130.0 W/(m·K) Show Material materials with Thermal conductivity of 130.0 W/(m·K) | H38 |
Electrical
| Property | Value | Condition | Comment |
|---|---|---|---|
Electrical conductivity | 19700000 S/m Show Material materials with Electrical conductivity of 19700000 S/m | H38 | Typical/derived value |
Electrical resistivity | 3.3e-08 - 5e-08 Ω·m Show Material materials with Electrical resistivity of 3.3e-08 - 5e-08 Ω·m | Typical for Wrought 5000 Series Aluminium | |
Specific Electrical conductivity | 34.0 % IACS Show Material materials with Specific Electrical conductivity of 34.0 % IACS | H38 | Typical value |
Chemical properties
| Property | Value | Condition |
|---|---|---|
Aluminium | 94.5 - 97.1 % Show Material materials with Aluminium of 94.5 - 97.1 % | H38 |
Chromium | 0.05 - 0.2 % Show Material materials with Chromium of 0.05 - 0.2 % | H38 |
Copper | 0.1 % Show Material materials with Copper of 0.1 % | H38 |
Iron | 0.4 % Show Material materials with Iron of 0.4 % | H38 |
Magnesium | 2.4 - 3.0 % Show Material materials with Magnesium of 2.4 - 3.0 % | H38 |
Manganese | 0.5 - 1.0 % Show Material materials with Manganese of 0.5 - 1.0 % | H38 |
Other | 0.15 % Show Material materials with Other of 0.15 % | H38 |
Silicon | 0.25 % Show Material materials with Silicon of 0.25 % | H38 |
Titanium | 0.2 % Show Material materials with Titanium of 0.2 % | H38 |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | H38 |
Technological properties
| Property | ||
|---|---|---|
| Workability | Good workability. | |