AA Standards Grade 6061 O

Want to keep this datasheet? Save it now in your required format

Description

Related Standards

Equivalent Materials

Ashby charts

See where AA Standards Grade 6061 O falls on the material property chart for Density against Elastic modulus in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

Density

ρ

2.7 g/cm³ at 20 °C

Dimension

Dimensions

Wanddicke

Mechanical

Compressive modulus

Ecomp

69.7 MPa at 20 °C

Show 6000 Series materials with Compressive modulus of 69.7 MPa at 20 °C

Elastic modulus

E

69 GPa at 20 °C

Show 6000 Series materials with Elastic modulus of 69 GPa at 20 °C

Elongation

A

17 - 27.5 % at 20 °C

Show 6000 Series materials with Elongation of 17 - 27.5 % at 20 °C

Elongation A100

A100

13 - 27 % at 20 °C

Show 6000 Series materials with Elongation A100 of 13 - 27 % at 20 °C

Elongation A50

A50

10 - 25 % at 20 °C

Show 6000 Series materials with Elongation A50 of 10 - 25 % at 20 °C

Hardness, Brinell

HB

30 [-] at 20 °C

Show 6000 Series materials with Hardness, Brinell of 30 [-] at 20 °C

500 kg load, 10 mm ball

Plane-Strain Fracture Toughnes

KIC

22 - 35 MPa·√m at 20 °C

Show 6000 Series materials with Plane-Strain Fracture Toughnes of 22 - 35 MPa·√m at 20 °C

Typical for Wrought 6000 Series Aluminium

Poisson's ratio

ν

0.33 [-] at 20 °C

Show 6000 Series materials with Poisson's ratio of 0.33 [-] at 20 °C

Shear modulus

G

26 - 26.5 GPa at 20 °C

Show 6000 Series materials with Shear modulus of 26 - 26.5 GPa at 20 °C

Typical for Wrought 6000 Series Aluminium

Shear strength

τ

83 MPa at 20 °C

Show 6000 Series materials with Shear strength of 83 MPa at 20 °C

Tensile strength

Rm

125 - 228 MPa at 20 °C

Show 6000 Series materials with Tensile strength of 125 - 228 MPa at 20 °C

Yield strength

YS

75 - 103 MPa at 20 °C

Show 6000 Series materials with Yield strength of 75 - 103 MPa at 20 °C

Yield strength Rp0.2

Rp0.2

55 - 110 MPa at 20 °C

Show 6000 Series materials with Yield strength Rp0.2 of 55 - 110 MPa at 20 °C

Thermal

Coefficient of thermal expansion

α

2.36E-5 - 2.4E-5 1/K at 20 °C

Hide chart

Melting point

Tm

580 - 650 °C

Specific heat capacity

cp

896 - 900 J/(kg·K) at 20 °C

Thermal conductivity

λ

155 - 180 W/(m·K) at 20 °C

Electrical

Electrical conductivity

σel

2.30E+7 - 2.49E+8 S/m at 20 °C

Typical value

Electrical resistivity

ρel

3.7E-8 - 3.7E-7 Ω·m at 20 °C

Typical value

Specific Electrical conductivity

47 % IACS

Typical/Derived value

Chemical properties

Element

Weight %

Comment

Al

95.9 - 98.6 %

Mg

0.8 - 1.2 %

Si

0.4 - 0.8 %

Cu

0.15 - 0.4 %

Cr

0.04 - 0.35 %

More

Technological properties

Brazing

general: possible with commercial processes and methods

Corrosion properties

Stress corrosion cracking: no damage during operation and laboratory tests (O, T6, T651, T652, T6510, T6511), no damage during operation, limited damage during laboratory tests (T4, T451, T4510, T4511), general: good, without protection in industrial or seawater atmosphere

General machinability

General: poor (O), sufficient (T4, T451, T4510, T4511, T6, T651, T652, T6510, T6511)

Workability

general (condition): good (O), acceptable (T4, T451, T4510, T4511), poor(T6, T651, T652, T6510, T6511)

This material data has been provided by MakeItFrom.com,ASM Handbook Volume 2 Properties and Selection: Nonferrous Alloys and Special-Purpose Materials,Matmatch,WroughtAl_ElectricalResistivity,AluKey.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.