General
Property | Value | Condition | Related Standards |
---|---|---|---|
Density | 2.7 g/cm³ Show Material materials with Density of 2.7 g/cm³ | H12 | |
2.705 g/cm³ Show Material materials with Density of 2.705 g/cm³ | H12 | AA Standards, ASTM B209, ASTM B210, ASTM B483 |
Mechanical
Property | Value | Condition | Related Standards | Comment |
---|---|---|---|---|
Bending Fatigue Strength | 30.0 MPa Show Material materials with Bending Fatigue Strength of 30.0 MPa | H12 | AA Standards | |
Elastic modulus | 69.0 GPa Show Material materials with Elastic modulus of 69.0 GPa | H12 | AA Standards, ASTM B209, ASTM B210, ASTM B483 | |
69 GPa Show Material materials with Elastic modulus of 69 GPa | H12 | |||
Elongation | 6.0 % Show Material materials with Elongation of 6.0 % | H12 | AA Standards, ASTM B209 | A50 |
7.0 % Show Material materials with Elongation of 7.0 % | H12 | AA Standards, ASTM B209 | A50 | |
10.0 % Show Material materials with Elongation of 10.0 % | H12 | AA Standards, ASTM B209 | A100 | |
12.0 % Show Material materials with Elongation of 12.0 % | H12 | AA Standards, ASTM B209 | A50 | |
12.0 % Show Material materials with Elongation of 12.0 % | H12 | |||
16.0 % Show Material materials with Elongation of 16.0 % | H12 | AA Standards | A50 | |
16 % Show Material materials with Elongation of 16 % | H12 | |||
Fatigue strength | 28 MPa Show Material materials with Fatigue strength of 28 MPa | H12 | for 5x10⁸ cycles | |
Hardness, Brinell | 23.0 [-] Show Material materials with Hardness, Brinell of 23.0 [-] | H12 | AA Standards | |
28.0 [-] Show Material materials with Hardness, Brinell of 28.0 [-] | H12 | 500 kg load, 10 mm ball | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 1000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 1000 Series Aluminium | ||
Shear modulus | 25.0 GPa Show Material materials with Shear modulus of 25.0 GPa | H12 | ||
Shear strength | 55.0 MPa Show Material materials with Shear strength of 55.0 MPa | H12 | ||
Tensile strength | 70.0 MPa Show Material materials with Tensile strength of 70.0 MPa | H12 | AA Standards, ASTM B210, ASTM B483 | |
75.0 - 110.0 MPa Show Material materials with Tensile strength of 75.0 - 110.0 MPa | H12 | AA Standards, ASTM B209 | ||
85.0 MPa Show Material materials with Tensile strength of 85.0 MPa | H12 | AA Standards | ||
85 MPa Show Material materials with Tensile strength of 85 MPa | H12 | |||
86.0 MPa Show Material materials with Tensile strength of 86.0 MPa | H12 | |||
Yield strength | 30.0 MPa Show Material materials with Yield strength of 30.0 MPa | H12 | AA Standards, ASTM B210, ASTM B483 | RP02 |
60.0 MPa Show Material materials with Yield strength of 60.0 MPa | H12 | AA Standards, ASTM B209 | RP02 | |
62.0 MPa Show Material materials with Yield strength of 62.0 MPa | H12 | |||
75.0 MPa Show Material materials with Yield strength of 75.0 MPa | H12 | AA Standards | RP02 | |
75 MPa Show Material materials with Yield strength of 75 MPa | H12 | RP02 |
Thermal
Property | Temperature | Value | Condition | Related Standards |
---|---|---|---|---|
Coefficient of thermal expansion | 2.4e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.4e-05 1/K | H12 | ||
20 °C | 2.36e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.36e-05 1/K | H12 | AA Standards, ASTM B209, ASTM B210, ASTM B483 | |
100 °C | 2.36e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.36e-05 1/K | H12 | AA Standards, ASTM B209, ASTM B210, ASTM B483 | |
Melting point | 645.0 - 655.0 °C Show Material materials with Melting point of 645.0 - 655.0 °C | H12 | AA Standards, ASTM B209, ASTM B210, ASTM B483 | |
650.0 °C Show Material materials with Melting point of 650.0 °C | H12 | |||
Specific heat capacity | 900.0 J/(kg·K) Show Material materials with Specific heat capacity of 900.0 J/(kg·K) | H12 | ||
Thermal conductivity | 230.0 - 234.0 W/(m·K) Show Material materials with Thermal conductivity of 230.0 - 234.0 W/(m·K) | H12 | AA Standards, ASTM B209, ASTM B210, ASTM B483 | |
230.0 W/(m·K) Show Material materials with Thermal conductivity of 230.0 W/(m·K) | H12 |
Electrical
Property | Value | Condition | Related Standards |
---|---|---|---|
Electrical conductivity | 35000000.0 - 36000000.0 S/m Show Material materials with Electrical conductivity of 35000000.0 - 36000000.0 S/m | H12 | AA Standards, ASTM B209, ASTM B210, ASTM B483 |
Electrical resistivity | 2.78e-08 - 2.86e-08 Ω·m Show Material materials with Electrical resistivity of 2.78e-08 - 2.86e-08 Ω·m | H12 | AA Standards, ASTM B209, ASTM B210, ASTM B483 |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Aluminium | 99.6 % Show Material materials with Aluminium of 99.6 % | H12 | AA Standards, ASTM B209, ASTM B210, ASTM B483 |
99.6 - 100.0 % Show Material materials with Aluminium of 99.6 - 100.0 % | H12 | ||
Copper | 0.05 % Show Material materials with Copper of 0.05 % | H12 | AA Standards, ASTM B209, ASTM B210, ASTM B483 |
Iron | 0.35 % Show Material materials with Iron of 0.35 % | H12 | AA Standards, ASTM B209, ASTM B210, ASTM B483 |
0.35 % Show Material materials with Iron of 0.35 % | H12 | ||
Magnesium | 0.03 % Show Material materials with Magnesium of 0.03 % | H12 | AA Standards, ASTM B209, ASTM B210, ASTM B483 |
Manganese | 0.03 % Show Material materials with Manganese of 0.03 % | H12 | AA Standards, ASTM B209, ASTM B210, ASTM B483 |
Silicon | 0.25 % Show Material materials with Silicon of 0.25 % | H12 | AA Standards, ASTM B209, ASTM B210, ASTM B483 |
Titanium | 0.03 % Show Material materials with Titanium of 0.03 % | H12 | AA Standards, ASTM B209, ASTM B210, ASTM B483 |
Vanadium | 0.05 % Show Material materials with Vanadium of 0.05 % | H12 | AA Standards, ASTM B209, ASTM B210, ASTM B483 |
Zinc | 0.05 % Show Material materials with Zinc of 0.05 % | H12 | AA Standards, ASTM B209, ASTM B210, ASTM B483 |
Technological properties
Property | ||
---|---|---|
Brazing | general: possible with commercial processes and methods | |
Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
General machinability | General: not suitable (O, H12), poor (H14, H16, H18) | |
Workability | general (condition): good (O, H12, H14), acceptable (H16, H18) |