AA Standards Grade 7005 T53

Want to keep this datasheet? Save it now in your required format

Related Standards

Equivalent Materials

This material data has been provided by AluKey,MakeItFrom.com,ASM Handbook Volume 2 Properties and Selection: Nonferrous Alloys and Special-Purpose Materials,WroughtAl_ElectricalResistivity.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionRelated Standards

Density

2.78 g/cm³

Show Material materials with Density of 2.78 g/cm³

T53

AA Standards, ASTM B221

2.78 g/cm³

Show Material materials with Density of 2.78 g/cm³

T53

2.9 g/cm³

Show Material materials with Density of 2.9 g/cm³

T53

Mechanical

PropertyTemperatureValueConditionRelated StandardsComment

Compressive modulus

72.4 MPa

Show Material materials with Compressive modulus of 72.4 MPa

T53

Elastic modulus

71.0 GPa

Show Material materials with Elastic modulus of 71.0 GPa

T53

Elongation

-269 °C

16 %

Show Material materials with Elongation of 16 %

T53

Elongation in 50 mm

-196 °C

16 %

Show Material materials with Elongation of 16 %

T53

Elongation in 50 mm

-80 °C

13 %

Show Material materials with Elongation of 13 %

T53

Elongation in 50 mm

-28 °C

14 %

Show Material materials with Elongation of 14 %

T53

Elongation in 50 mm

9.0 %

Show Material materials with Elongation of 9.0 %

T53

AA Standards, ASTM B221

A100

10.0 %

Show Material materials with Elongation of 10.0 %

T53

AA Standards, ASTM B221

A50

10.0 %

Show Material materials with Elongation of 10.0 %

T53

24 °C

15 %

Show Material materials with Elongation of 15 %

T53

Elongation in 50 mm

100 °C

20 %

Show Material materials with Elongation of 20 %

T53

Elongation in 50 mm

149 °C

35 %

Show Material materials with Elongation of 35 %

T53

Elongation in 50 mm

204 °C

60 %

Show Material materials with Elongation of 60 %

T53

Elongation in 50 mm

Fatigue strength

231 MPa

Show Material materials with Fatigue strength of 231 MPa

T53

fo 5x10⁸ cycles

Plane-Strain Fracture Toughnes

22.0 - 35.0 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m

Typical for Wrought 7000 Series Aluminium

Poisson's ratio

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-]

Typical for Wrought 7000 Series Aluminium

Shear modulus

26.9 GPa

Show Material materials with Shear modulus of 26.9 GPa

T53

Shear strength

221.0 MPa

Show Material materials with Shear strength of 221.0 MPa

T53

Tensile strength

-269 °C

641 MPa

Show Material materials with Tensile strength of 641 MPa

T53

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

-196 °C

538 MPa

Show Material materials with Tensile strength of 538 MPa

T53

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

-80 °C

441 MPa

Show Material materials with Tensile strength of 441 MPa

T53

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

-28 °C

421 MPa

Show Material materials with Tensile strength of 421 MPa

T53

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

345.0 MPa

Show Material materials with Tensile strength of 345.0 MPa

T53

AA Standards, ASTM B221

400.0 MPa

Show Material materials with Tensile strength of 400.0 MPa

T53

24 °C

392 MPa

Show Material materials with Tensile strength of 392 MPa

T53

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

100 °C

303 MPa

Show Material materials with Tensile strength of 303 MPa

T53

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

149 °C

165 MPa

Show Material materials with Tensile strength of 165 MPa

T53

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

204 °C

97 MPa

Show Material materials with Tensile strength of 97 MPa

T53

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

Unlock all property charts

Yield strength

-269 °C

483 MPa

Show Material materials with Yield strength of 483 MPa

T53

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

-196 °C

421 MPa

Show Material materials with Yield strength of 421 MPa

T53

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

-80 °C

379 MPa

Show Material materials with Yield strength of 379 MPa

T53

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

-28 °C

359 MPa

Show Material materials with Yield strength of 359 MPa

T53

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

305.0 MPa

Show Material materials with Yield strength of 305.0 MPa

T53

AA Standards, ASTM B221

RP02

350.0 MPa

Show Material materials with Yield strength of 350.0 MPa

T53

24 °C

345 MPa

Show Material materials with Yield strength of 345 MPa

T53

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

100 °C

283 MPa

Show Material materials with Yield strength of 283 MPa

T53

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

149 °C

145 MPa

Show Material materials with Yield strength of 145 MPa

T53

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

204 °C

83 MPa

Show Material materials with Yield strength of 83 MPa

T53

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

Unlock all property charts

Thermal

PropertyValueConditionComment

Coefficient of thermal expansion

2.3e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.3e-05 1/K

T53

Melting point

610.0 °C

Show Material materials with Melting point of 610.0 °C

T53

Specific heat capacity

880.0 J/(kg·K)

Show Material materials with Specific heat capacity of 880.0 J/(kg·K)

T53

Thermal conductivity

121.0 - 170.0 W/(m·K)

Show Material materials with Thermal conductivity of 121.0 - 170.0 W/(m·K)

Typical for Wrought 7000 Series Aluminium

Electrical

PropertyValueConditionComment

Electrical conductivity

22000000 S/m

Show Material materials with Electrical conductivity of 22000000 S/m

T53

Typical/derived value

Electrical resistivity

4.54e-08 Ω·m

Show Material materials with Electrical resistivity of 4.54e-08 Ω·m

T53

Typical value

Specific Electrical conductivity

38.0 % IACS

Show Material materials with Specific Electrical conductivity of 38.0 % IACS

T53

Typical value

Chemical properties

PropertyValueConditionRelated Standards

Aluminium

91.0 - 94.7 %

Show Material materials with Aluminium of 91.0 - 94.7 %

T53

Chromium

0.06 - 0.2 %

Show Material materials with Chromium of 0.06 - 0.2 %

T53

AA Standards, ASTM B221

Copper

0.1 %

Show Material materials with Copper of 0.1 %

T53

AA Standards, ASTM B221

Iron

0.40 %

Show Material materials with Iron of 0.40 %

T53

AA Standards, ASTM B221

0.4 %

Show Material materials with Iron of 0.4 %

T53

Magnesium

1.0 - 1.8 %

Show Material materials with Magnesium of 1.0 - 1.8 %

T53

AA Standards, ASTM B221

Manganese

0.2 - 0.7 %

Show Material materials with Manganese of 0.2 - 0.7 %

T53

AA Standards, ASTM B221

Other

0.15 %

Show Material materials with Other of 0.15 %

T53

Silicon

0.35 %

Show Material materials with Silicon of 0.35 %

T53

AA Standards, ASTM B221

Titanium

0.01 - 0.06 %

Show Material materials with Titanium of 0.01 - 0.06 %

T53

AA Standards, ASTM B221

Zinc

4.0 - 5.0 %

Show Material materials with Zinc of 4.0 - 5.0 %

T53

AA Standards, ASTM B221

Zirconium

0.08 - 0.2 %

Show Material materials with Zirconium of 0.08 - 0.2 %

T53

AA Standards, ASTM B221

Technological properties

Property
Brazing

general: Lötbar mit speziellen Techniken oder bei bestimmten Anwendungen