General
Property | Value | Condition |
---|---|---|
Density | 3.1 g/cm³ Show Material materials with Density of 3.1 g/cm³ | T652 |
Mechanical
Property | Value | Condition | Related Standards | Comment |
---|---|---|---|---|
Elastic modulus | 72.0 GPa Show Material materials with Elastic modulus of 72.0 GPa | T652 | ||
Elongation | 1.0 % Show Material materials with Elongation of 1.0 % | T652 | AA Standards, ASTM B247 | A100 |
1.8 % Show Material materials with Elongation of 1.8 % | T652 | |||
2.0 % Show Material materials with Elongation of 2.0 % | T652 | AA Standards, ASTM B247 | A100 | |
3.0 % Show Material materials with Elongation of 3.0 % | T652 | AA Standards, ASTM B247 | A100 | |
3.0 % Show Material materials with Elongation of 3.0 % | T652 | AA Standards, ASTM B247 | A50 | |
5.0 % Show Material materials with Elongation of 5.0 % | T652 | AA Standards, ASTM B247 | A100 | |
6.0 % Show Material materials with Elongation of 6.0 % | T652 | AA Standards, ASTM B247 | A100 | |
6.0 % Show Material materials with Elongation of 6.0 % | T652 | AA Standards, ASTM B247 | A50 | |
7.0 % Show Material materials with Elongation of 7.0 % | T652 | AA Standards, ASTM B247 | A100 | |
8.0 % Show Material materials with Elongation of 8.0 % | T652 | AA Standards, ASTM B247 | A100 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 7000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 7000 Series Aluminium | ||
Shear modulus | 26.4 - 27.1 GPa Show Material materials with Shear modulus of 26.4 - 27.1 GPa | Typical for Wrought 7000 Series Aluminium | ||
Tensile strength | 450.0 MPa Show Material materials with Tensile strength of 450.0 MPa | T652 | AA Standards, ASTM B247 | |
455.0 MPa Show Material materials with Tensile strength of 455.0 MPa | T652 | AA Standards, ASTM B247 | ||
470.0 MPa Show Material materials with Tensile strength of 470.0 MPa | T652 | AA Standards, ASTM B247 | ||
475.0 MPa Show Material materials with Tensile strength of 475.0 MPa | T652 | AA Standards, ASTM B247 | ||
480.0 MPa Show Material materials with Tensile strength of 480.0 MPa | T652 | |||
485.0 MPa Show Material materials with Tensile strength of 485.0 MPa | T652 | AA Standards, ASTM B247 | ||
490.0 MPa Show Material materials with Tensile strength of 490.0 MPa | T652 | AA Standards, ASTM B247 | ||
505.0 MPa Show Material materials with Tensile strength of 505.0 MPa | T652 | AA Standards, ASTM B247 | ||
510.0 MPa Show Material materials with Tensile strength of 510.0 MPa | T652 | AA Standards, ASTM B247 | ||
Yield strength | 370.0 MPa Show Material materials with Yield strength of 370.0 MPa | T652 | AA Standards, ASTM B247 | RP02 |
370.0 MPa Show Material materials with Yield strength of 370.0 MPa | T652 | |||
380.0 MPa Show Material materials with Yield strength of 380.0 MPa | T652 | AA Standards, ASTM B247 | RP02 | |
385.0 MPa Show Material materials with Yield strength of 385.0 MPa | T652 | AA Standards, ASTM B247 | RP02 | |
395.0 MPa Show Material materials with Yield strength of 395.0 MPa | T652 | AA Standards, ASTM B247 | RP02 | |
400.0 MPa Show Material materials with Yield strength of 400.0 MPa | T652 | AA Standards, ASTM B247 | RP02 | |
405.0 MPa Show Material materials with Yield strength of 405.0 MPa | T652 | AA Standards, ASTM B247 | RP02 | |
415.0 MPa Show Material materials with Yield strength of 415.0 MPa | T652 | AA Standards, ASTM B247 | RP02 | |
420.0 MPa Show Material materials with Yield strength of 420.0 MPa | T652 | AA Standards, ASTM B247 | RP02 | |
435.0 MPa Show Material materials with Yield strength of 435.0 MPa | T652 | AA Standards, ASTM B247 | RP02 |
Thermal
Property | Value | Condition |
---|---|---|
Coefficient of thermal expansion | 2.3e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3e-05 1/K | T652 |
Melting point | 480.0 °C Show Material materials with Melting point of 480.0 °C | T652 |
Specific heat capacity | 910.0 J/(kg·K) Show Material materials with Specific heat capacity of 910.0 J/(kg·K) | T652 |
Thermal conductivity | 130.0 W/(m·K) Show Material materials with Thermal conductivity of 130.0 W/(m·K) | T652 |
Electrical
Property | Value | Condition | Comment |
---|---|---|---|
Electrical conductivity | 19000000 S/m Show Material materials with Electrical conductivity of 19000000 S/m | T652 | Typical/derived value |
Electrical resistivity | 5.22e-08 Ω·m Show Material materials with Electrical resistivity of 5.22e-08 Ω·m | T652 | Typical value |
Specific Electrical conductivity | 33.0 % IACS Show Material materials with Specific Electrical conductivity of 33.0 % IACS | T652 | Typical value |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Aluminium | 86.9 - 91.4 % Show Material materials with Aluminium of 86.9 - 91.4 % | T652 | |
Chromium | 0.18 - 0.28 % Show Material materials with Chromium of 0.18 - 0.28 % | T652 | AA Standards, ASTM B247 |
Copper | 1.2 - 2.0 % Show Material materials with Copper of 1.2 - 2.0 % | T652 | AA Standards, ASTM B247 |
Iron | 0.50 % Show Material materials with Iron of 0.50 % | T652 | AA Standards, ASTM B247 |
0.5 % Show Material materials with Iron of 0.5 % | T652 | ||
Magnesium | 2.1 - 2.9 % Show Material materials with Magnesium of 2.1 - 2.9 % | T652 | AA Standards, ASTM B247 |
Manganese | 0.3 % Show Material materials with Manganese of 0.3 % | T652 | AA Standards, ASTM B247 |
Other | 0.15 % Show Material materials with Other of 0.15 % | T652 | |
Silicon | 0.4 % Show Material materials with Silicon of 0.4 % | T652 | AA Standards, ASTM B247 |
Titanium | 0.2 % Show Material materials with Titanium of 0.2 % | T652 | AA Standards, ASTM B247 |
Zinc | 5.1 - 6.1 % Show Material materials with Zinc of 5.1 - 6.1 % | T652 | AA Standards, ASTM B247 |
Zirconium | 0.25 % Show Material materials with Zirconium of 0.25 % | T652 |
Technological properties
Property | ||
---|---|---|
Brazing | general: no brazing is known or developed | |
Corrosion properties | Stress corrosion cracking: Operational damage in areas with tensile stresses transverse to the grain structure, limited damage to laboratory samples, general: good, without protection in industrial or seawater atmosphere | |
General machinability | General: poor (O), good to acceptable | |
Workability | general (condition): not suitable |