AA Standards Grade 7075 T73511

View suppliers (130)
Want to keep this datasheet? Save it now in your required format

Description

AA 7075 is a high-strength alloy that offers good stress-corrosion cracking resistance. Known as a mainstay in the aerospace industry since it was introduced, Aluminum 7075 brings moderate toughness as well as an excellent strength-to-weight ratio. It is also important to note that at sub-zero temperatures Aluminum 7075 increases in strength.

Related Standards

Equivalent Materials

This material data has been provided by AluKey,MakeItFrom.com,Righton Blackburns.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionRelated StandardsShape

Density

2.81 g/cm³

Show Material materials with Density of 2.81 g/cm³

T73511

BS L160

Bar

3.1 g/cm³

Show Material materials with Density of 3.1 g/cm³

T73511

Mechanical

PropertyValueConditionRelated StandardsShapeComment

Elastic modulus

72.0 GPa

Show Material materials with Elastic modulus of 72.0 GPa

T73511

BS L160

Bar

Elongation

6.0 %

Show Material materials with Elongation of 6.0 %

T73511

AA Standards, ASTM B221

A100

7.0 %

Show Material materials with Elongation of 7.0 %

T73511

AA Standards, ASTM B221

A100

7.0 %

Show Material materials with Elongation of 7.0 %

T73511

AA Standards, ASTM B221

A50

7.0 - 8.0 %

Show Material materials with Elongation of 7.0 - 8.0 %

T73511

BS L160

Bar

8.0 %

Show Material materials with Elongation of 8.0 %

T73511

AA Standards, ASTM B221

A50

8.1 %

Show Material materials with Elongation of 8.1 %

T73511

Plane-Strain Fracture Toughnes

22.0 - 35.0 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m

Typical for Wrought 7000 Series Aluminium

Poisson's ratio

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-]

Typical for Wrought 7000 Series Aluminium

Shear modulus

26.4 - 27.1 GPa

Show Material materials with Shear modulus of 26.4 - 27.1 GPa

Typical for Wrought 7000 Series Aluminium

Tensile strength

425.0 - 485.0 MPa

Show Material materials with Tensile strength of 425.0 - 485.0 MPa

T73511

BS L160

Bar

450.0 MPa

Show Material materials with Tensile strength of 450.0 MPa

T73511

AA Standards, ASTM B221

470.0 MPa

Show Material materials with Tensile strength of 470.0 MPa

T73511

AA Standards, ASTM B221

475.0 MPa

Show Material materials with Tensile strength of 475.0 MPa

T73511

AA Standards, ASTM B221

485.0 MPa

Show Material materials with Tensile strength of 485.0 MPa

T73511

AA Standards, ASTM B221

510.0 MPa

Show Material materials with Tensile strength of 510.0 MPa

T73511

Yield strength

365.0 - 420.0 MPa

Show Material materials with Yield strength of 365.0 - 420.0 MPa

T73511

BS L160

Bar

RP02

380.0 MPa

Show Material materials with Yield strength of 380.0 MPa

T73511

AA Standards, ASTM B221

RP02

395.0 MPa

Show Material materials with Yield strength of 395.0 MPa

T73511

AA Standards, ASTM B221

RP02

400.0 MPa

Show Material materials with Yield strength of 400.0 MPa

T73511

AA Standards, ASTM B221

RP02

405.0 MPa

Show Material materials with Yield strength of 405.0 MPa

T73511

AA Standards, ASTM B221

RP02

420.0 MPa

Show Material materials with Yield strength of 420.0 MPa

T73511

AA Standards, ASTM B221

RP02

430.0 MPa

Show Material materials with Yield strength of 430.0 MPa

T73511

Thermal

PropertyValueConditionRelated StandardsShape

Coefficient of thermal expansion

2.3e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.3e-05 1/K

T73511

2.35e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.35e-05 1/K

T73511

BS L160

Bar

Melting point

480.0 °C

Show Material materials with Melting point of 480.0 °C

T73511

635.0 °C

Show Material materials with Melting point of 635.0 °C

T73511

BS L160

Bar

Specific heat capacity

910.0 J/(kg·K)

Show Material materials with Specific heat capacity of 910.0 J/(kg·K)

T73511

Thermal conductivity

130.0 W/(m·K)

Show Material materials with Thermal conductivity of 130.0 W/(m·K)

T73511

134.0 - 160.0 W/(m·K)

Show Material materials with Thermal conductivity of 134.0 - 160.0 W/(m·K)

T73511

BS L160

Bar

Electrical

PropertyValueConditionRelated StandardsShapeComment

Electrical conductivity

18000000.0 - 34000000.0 S/m

Show Material materials with Electrical conductivity of 18000000.0 - 34000000.0 S/m

Typical for Wrought 7000 Series Aluminium

Electrical resistivity

4.31e-08 Ω·m

Show Material materials with Electrical resistivity of 4.31e-08 Ω·m

T73511

BS L160

Bar

Chemical properties

PropertyValueConditionRelated StandardsShapeComment

Aluminium

86.9 - 91.4 %

Show Material materials with Aluminium of 86.9 - 91.4 %

T73511

Chromium

0.18 - 0.28 %

Show Material materials with Chromium of 0.18 - 0.28 %

T73511

AA Standards, ASTM B221, BS L160

Bar

Copper

1.2 - 2.0 %

Show Material materials with Copper of 1.2 - 2.0 %

T73511

AA Standards, ASTM B221, BS L160

Bar

Iron

0.50 %

Show Material materials with Iron of 0.50 %

T73511

AA Standards, ASTM B221

0.5 %

Show Material materials with Iron of 0.5 %

T73511

BS L160

Bar

Magnesium

2.1 - 2.9 %

Show Material materials with Magnesium of 2.1 - 2.9 %

T73511

AA Standards, ASTM B221, BS L160

Bar

Manganese

0.3 %

Show Material materials with Manganese of 0.3 %

T73511

AA Standards, ASTM B221, BS L160

Bar

Other

0.15 %

Show Material materials with Other of 0.15 %

T73511

BS L160

Bar

Total

Silicon

0.4 %

Show Material materials with Silicon of 0.4 %

T73511

AA Standards, ASTM B221, BS L160

Bar

Titanium

0.2 %

Show Material materials with Titanium of 0.2 %

T73511

AA Standards, ASTM B221, BS L160

Bar

Zinc

5.1 - 6.1 %

Show Material materials with Zinc of 5.1 - 6.1 %

T73511

AA Standards, ASTM B221, BS L160

Bar

Zirconium

0.25 %

Show Material materials with Zirconium of 0.25 %

T73511

BS L160

Bar

Ti + Zr

Technological properties

Property
Application areas

Aerospace

Brazing

general: no brazing is known or developed

Corrosion properties

Stress corrosion cracking: Operational damage in areas with tensile stresses transverse to the grain structure, limited damage to laboratory samples, general: good, without protection in industrial or seawater atmosphere

General machinability

General: poor (O), good to acceptable

Workability

general (condition): not suitable