AA Standards Grade 1060 O

Want to keep this datasheet? Save it now in your required format

Description

Related Standards

Equivalent Materials

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

Density

ρ

2.7 - 2.71 g/cm³ at 23 °C

Dimension

Dimensions

Dicke

Mechanical

Bending Fatigue Strength

SNf

20 MPa at 23 °C

Show 1000 Series materials with Bending Fatigue Strength of 20 MPa at 23 °C

Elastic modulus

E

69 GPa at 23 °C

Show 1000 Series materials with Elastic modulus of 69 GPa at 23 °C

Elongation

A

31 - 43 % at 23 °C

Show 1000 Series materials with Elongation of 31 - 43 % at 23 °C

Elongation A100

A100

22 % at 23 °C

Show 1000 Series materials with Elongation A100 of 22 % at 23 °C

Elongation A50

A50

15 - 43 % at 23 °C

Show 1000 Series materials with Elongation A50 of 15 - 43 % at 23 °C

Fatigue strength

SNf

21 MPa at 23 °C

Show 1000 Series materials with Fatigue strength of 21 MPa at 23 °C

for 5x10⁸ cycles

Hardness, Brinell

HB

19 - 23 [-] at 23 °C

Show 1000 Series materials with Hardness, Brinell of 19 - 23 [-] at 23 °C

500 kg load, 10 mm ball

Plane-Strain Fracture Toughnes

KIC

22 - 35 MPa·√m at 23 °C

Show 1000 Series materials with Plane-Strain Fracture Toughnes of 22 - 35 MPa·√m at 23 °C

Typical for Wrought 1000 Series Aluminium

Poisson's ratio

ν

0.33 [-] at 23 °C

Show 1000 Series materials with Poisson's ratio of 0.33 [-] at 23 °C

Typical for Wrought 1000 Series Aluminium

Shear modulus

G

25 GPa at 23 °C

Show 1000 Series materials with Shear modulus of 25 GPa at 23 °C

Shear strength

τ

50 MPa at 23 °C

Show 1000 Series materials with Shear strength of 50 MPa at 23 °C

Tensile strength

Rm

55 - 95 MPa at 23 °C

Show 1000 Series materials with Tensile strength of 55 - 95 MPa at 23 °C

Yield strength

YS

21 MPa at 23 °C

Show 1000 Series materials with Yield strength of 21 MPa at 23 °C

Yield strength Rp0.2

Rp0.2

15 - 30 MPa at 23 °C

Show 1000 Series materials with Yield strength Rp0.2 of 15 - 30 MPa at 23 °C

Thermal

Coefficient of thermal expansion

α

2.36E-5 1/K at 20 °C

Hide chart

Melting point

Tm

645 - 655 °C

Specific heat capacity

cp

900 J/(kg·K) at 23 °C

Thermal conductivity

λ

230 - 234 W/(m·K) at 23 °C

unstated value

Unlock all property charts

Electrical

Electrical conductivity

σel

3.50E+7 - 3.60E+7 S/m at 23 °C

Typical/derived value

Electrical resistivity

ρel

2.78E-8 - 2.86E-8 Ω·m at 23 °C

Specific Electrical conductivity

62 % IACS

Typical value

Chemical properties

Element

Weight %

Comment

Other

-

each 0.03

Al

99.6 - 100 %

Cu

0 - 0.05 %

Fe

0 - 0.35 %

Mg

0 - 0.03 %

More

Technological properties

Brazing

general: possible with commercial processes and methods

Corrosion properties

Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere

General machinability

General: not suitable (O, H12), poor (H14, H16, H18)

Workability

general (condition): good (O, H12, H14), acceptable (H16, H18)

This material data has been provided by MakeItFrom.com,ASM Handbook Volume 2 Properties and Selection: Nonferrous Alloys and Special-Purpose Materials,WroughtAl_Thermal,AluKey.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.