Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 23.0 °C | 2.71 - 2.8 g/cm³ Show Material materials with Density of 2.71 - 2.8 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 69 GPa Show Material materials with Elastic modulus of 69 GPa | |
Elongation | 23.0 °C | 21 % Show Material materials with Elongation of 21 % | |
Elongation A100 | 23.0 °C | 12 - 22 % Show Material materials with Elongation A100 of 12 - 22 % | |
Elongation A50 | 23.0 °C | 9 - 25 % Show Material materials with Elongation A50 of 9 - 25 % | |
Plane-Strain Fracture Toughnes | 23.0 °C | 22 - 35 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22 - 35 MPa·√m | Typical for Wrought 1000 Series Aluminium |
Poisson's ratio | 23.0 °C | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 1000 Series Aluminium |
Shear modulus | 23.0 °C | 25.9 GPa Show Material materials with Shear modulus of 25.9 GPa | Typical for Wrought 1000 Series Aluminium |
Tensile strength | 23.0 °C | 75 - 90 MPa Show Material materials with Tensile strength of 75 - 90 MPa | |
Yield strength | 23.0 °C | 36 MPa Show Material materials with Yield strength of 36 MPa | |
Yield strength Rp0.2 | 23.0 °C | 20 - 50 MPa Show Material materials with Yield strength Rp0.2 of 20 - 50 MPa |
Thermal
| Property | Temperature | Value |
|---|---|---|
Coefficient of thermal expansion | 20.0 °C | 2.36E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.36E-5 1/K |
23.0 °C | 2.4E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.4E-5 1/K | |
100.0 °C | 2.36E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.36E-5 1/K | |
Melting point | 640 - 655 °C Show Material materials with Melting point of 640 - 655 °C | |
Specific heat capacity | 23.0 °C | 900 J/(kg·K) Show Material materials with Specific heat capacity of 900 J/(kg·K) |
Thermal conductivity | 23.0 °C | 218 - 222 W/(m·K) Show Material materials with Thermal conductivity of 218 - 222 W/(m·K) |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical conductivity | 23.0 °C | 3.30E+7 - 3.40E+7 S/m Show Material materials with Electrical conductivity of 3.30E+7 - 3.40E+7 S/m |
Electrical resistivity | 23.0 °C | 2.94E-8 - 3.03E-8 Ω·m Show Material materials with Electrical resistivity of 2.94E-8 - 3.03E-8 Ω·m |
Chemical properties
| Property | Value | Comment |
|---|---|---|
Aluminium | 99 - 100 % Show Material materials with Aluminium of 99 - 100 % | |
Copper | 0.05 - 0.2 % Show Material materials with Copper of 0.05 - 0.2 % | |
Iron | 0 - 1 % Show Material materials with Iron of 0 - 1 % | |
Manganese | 0 - 0.05 % Show Material materials with Manganese of 0 - 0.05 % | |
Other | 0 - 0.15 % Show Material materials with Other of 0 - 0.15 % | each 0.05, total 0.15, Si + Fe < 0.95 |
Silicon | 0 - 1 % Show Material materials with Silicon of 0 - 1 % | |
Zinc | 0 - 0.1 % Show Material materials with Zinc of 0 - 0.1 % |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: possible with commercial processes and methods | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: not suitable (O, H12), poor (H14, H16, H18) | |
| Workability | general (condition): good (O, H12, H14), acceptable (H16), poor(H18) | |