General
Property | Value | Condition | Related Standards |
---|---|---|---|
Density | 2.71 g/cm³ Show Material materials with Density of 2.71 g/cm³ | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
2.71 g/cm³ Show Material materials with Density of 2.71 g/cm³ | H14 | ||
2.8 g/cm³ Show Material materials with Density of 2.8 g/cm³ | H14 |
Mechanical
Property | Temperature | Value | Condition | Related Standards | Comment |
---|---|---|---|---|---|
Bending Fatigue Strength | 50.0 MPa Show Material materials with Bending Fatigue Strength of 50.0 MPa | H14 | AA Standards | ||
Elastic modulus | 69.0 GPa Show Material materials with Elastic modulus of 69.0 GPa | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | ||
69 GPa Show Material materials with Elastic modulus of 69 GPa | H14 | ||||
Elongation | -195 °C | 45 % Show Material materials with Elongation of 45 % | H14 | Elongation in 50 mm | |
-80 °C | 24 % Show Material materials with Elongation of 24 % | H14 | Elongation in 50 mm | ||
1.0 % Show Material materials with Elongation of 1.0 % | H14 | AA Standards, ASTM B209 | A50 | ||
2.0 % Show Material materials with Elongation of 2.0 % | H14 | AA Standards, ASTM B209 | A50 | ||
3.0 % Show Material materials with Elongation of 3.0 % | H14 | AA Standards, ASTM B209, ASTM B313 | A50 | ||
5.0 % Show Material materials with Elongation of 5.0 % | H14 | AA Standards, ASTM B209, ASTM B313, ASTM B547 | A50 | ||
6.0 % Show Material materials with Elongation of 6.0 % | H14 | AA Standards, ASTM B209 | A100 | ||
7.0 % Show Material materials with Elongation of 7.0 % | H14 | AA Standards, ASTM B209, ASTM B547 | A50 | ||
9.0 % Show Material materials with Elongation of 9.0 % | H14 | AA Standards | A50 | ||
9.6 % Show Material materials with Elongation of 9.6 % | H14 | ||||
15.0 % Show Material materials with Elongation of 15.0 % | H14 | ||||
18.0 % Show Material materials with Elongation of 18.0 % | H14 | AA Standards | A100 | ||
0 °C | 20 % Show Material materials with Elongation of 20 % | H14 | Elongation in 50 mm | ||
24 °C | 20 % Show Material materials with Elongation of 20 % | H14 | Elongation in 50 mm | ||
100 °C | 20 % Show Material materials with Elongation of 20 % | H14 | Elongation in 50 mm | ||
150 °C | 23 % Show Material materials with Elongation of 23 % | H14 | Elongation in 50 mm | ||
205 °C | 26 % Show Material materials with Elongation of 26 % | H14 | Elongation in 50 mm | ||
260 °C | 75 % Show Material materials with Elongation of 75 % | H14 | Elongation in 50 mm | ||
315 °C | 80 % Show Material materials with Elongation of 80 % | H14 | Elongation in 50 mm | ||
370 °C | 85 % Show Material materials with Elongation of 85 % | H14 | Elongation in 50 mm | ||
Fatigue strength | 48 MPa Show Material materials with Fatigue strength of 48 MPa | H14 | for 5x10⁸ cycles | ||
Hardness, Brinell | 32.0 [-] Show Material materials with Hardness, Brinell of 32.0 [-] | H14 | AA Standards | ||
32.0 [-] Show Material materials with Hardness, Brinell of 32.0 [-] | H14 | 500 kg load, 10 mm ball | |||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 1000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | H14 | |||
Shear modulus | 25.0 GPa Show Material materials with Shear modulus of 25.0 GPa | H14 | |||
26.0 GPa Show Material materials with Shear modulus of 26.0 GPa | H14 | ||||
Shear strength | 75.0 MPa Show Material materials with Shear strength of 75.0 MPa | H14 | |||
Tensile strength | -195 °C | 207 MPa Show Material materials with Tensile strength of 207 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
-80 °C | 138 MPa Show Material materials with Tensile strength of 138 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
110.0 - 145.0 MPa Show Material materials with Tensile strength of 110.0 - 145.0 MPa | H14 | AA Standards, ASTM B209, ASTM B313, ASTM B316, ASTM B547 | |||
110.0 MPa Show Material materials with Tensile strength of 110.0 MPa | H14 | AA Standards, ASTM B210, ASTM B211, ASTM B483 | |||
124.0 MPa Show Material materials with Tensile strength of 124.0 MPa | H14 | ||||
125.0 MPa Show Material materials with Tensile strength of 125.0 MPa | H14 | AA Standards | |||
130.0 MPa Show Material materials with Tensile strength of 130.0 MPa | H14 | ||||
0 °C | 130 MPa Show Material materials with Tensile strength of 130 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
24 °C | 125 MPa Show Material materials with Tensile strength of 125 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
100 °C | 110 MPa Show Material materials with Tensile strength of 110 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
150 °C | 97 MPa Show Material materials with Tensile strength of 97 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
205 °C | 70 MPa Show Material materials with Tensile strength of 70 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
260 °C | 28 MPa Show Material materials with Tensile strength of 28 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
315 °C | 20 MPa Show Material materials with Tensile strength of 20 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
370 °C | 14 MPa Show Material materials with Tensile strength of 14 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
Yield strength | -196 °C | 140 MPa Show Material materials with Yield strength of 140 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
-80 °C | 125 MPa Show Material materials with Yield strength of 125 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
-28 °C | 115 MPa Show Material materials with Yield strength of 115 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
85.0 MPa Show Material materials with Yield strength of 85.0 MPa | H14 | AA Standards, ASTM B483 | RP02 | ||
95.0 MPa Show Material materials with Yield strength of 95.0 MPa | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B547 | RP02 | ||
110.0 MPa Show Material materials with Yield strength of 110.0 MPa | H14 | ||||
115.0 MPa Show Material materials with Yield strength of 115.0 MPa | H14 | AA Standards | RP02 | ||
117.0 MPa Show Material materials with Yield strength of 117.0 MPa | H14 | ||||
24 °C | 115 MPa Show Material materials with Yield strength of 115 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
100 °C | 105 MPa Show Material materials with Yield strength of 105 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
149 °C | 83 MPa Show Material materials with Yield strength of 83 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
204 °C | 52 MPa Show Material materials with Yield strength of 52 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
260 °C | 18 MPa Show Material materials with Yield strength of 18 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
316 °C | 14 MPa Show Material materials with Yield strength of 14 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
371 °C | 11 MPa Show Material materials with Yield strength of 11 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 |
Thermal
Property | Temperature | Value | Condition | Related Standards |
---|---|---|---|---|
Coefficient of thermal expansion | 2.4e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.4e-05 1/K | H14 | ||
2.66e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.66e-05 1/K | H14 | |||
20 °C | 2.36e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.36e-05 1/K | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | |
100 °C | 2.36e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.36e-05 1/K | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | |
Melting point | 640.0 - 655.0 °C Show Material materials with Melting point of 640.0 - 655.0 °C | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | |
640.0 °C Show Material materials with Melting point of 640.0 °C | H14 | |||
Specific heat capacity | 900.0 J/(kg·K) Show Material materials with Specific heat capacity of 900.0 J/(kg·K) | H14 | ||
904.0 J/(kg·K) Show Material materials with Specific heat capacity of 904.0 J/(kg·K) | H14 | |||
Thermal conductivity | 218.0 - 222.0 W/(m·K) Show Material materials with Thermal conductivity of 218.0 - 222.0 W/(m·K) | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | |
220.0 W/(m·K) Show Material materials with Thermal conductivity of 220.0 W/(m·K) | H14 |
Electrical
Property | Value | Condition | Related Standards |
---|---|---|---|
Electrical conductivity | 33000000.0 - 34000000.0 S/m Show Material materials with Electrical conductivity of 33000000.0 - 34000000.0 S/m | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
Electrical resistivity | 2.94e-08 - 3.03e-08 Ω·m Show Material materials with Electrical resistivity of 2.94e-08 - 3.03e-08 Ω·m | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Aluminium | 99.0 % Show Material materials with Aluminium of 99.0 % | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
99.0 - 100.0 % Show Material materials with Aluminium of 99.0 - 100.0 % | H14 | ||
Copper | 0.05 - 0.2 % Show Material materials with Copper of 0.05 - 0.2 % | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
Iron | 1.0 % Show Material materials with Iron of 1.0 % | H14 | |
Manganese | 0.05 % Show Material materials with Manganese of 0.05 % | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
Other | 0.15 % Show Material materials with Other of 0.15 % | H14 | |
Silicon | 1.0 % Show Material materials with Silicon of 1.0 % | H14 | |
Zinc | 0.1 % Show Material materials with Zinc of 0.1 % | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
Technological properties
Property | ||
---|---|---|
Brazing | general: possible with commercial processes and methods | |
Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
General machinability | General: not suitable (O, H12), poor (H14, H16, H18) | |
Workability | general (condition): good (O, H12, H14), acceptable (H16), poor(H18) |